In situ analysis of the strain evolution during welding using low transformation temperature filler materials
- Compared to conventional welding consumables using low transformation temperature (LTT) filler materials is an innovative method to mitigate tensile residual stresses due to delayed martensite transformation of the weld. For the effective usage of LTT filler materials, a deeper understanding of the complex processes that lead to the final residual stress state during multipass welding is necessary. Transformation kinetics and the strain evolution of multi-pass welds during welding were investigated in situ at the beamline HEMS@PETRAIII, Germany. Compared to conventional welds, the total strain was reduced and compression strain was achieved when using LTT filler materials. For an optimal use of the LTT effect in the root of multi-pass welds, the alloying concept must be adapted taking care of dilution.
Autor*innen: | Jonny Dixneit, F. Vollert, Arne KrommORCiD, J. Gibmeier, Andreas Hannemann, Tobias Fischer, Thomas KannengießerORCiD |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Science and Technology of Welding and Joining |
Jahr der Erstveröffentlichung: | 2018 |
Organisationseinheit der BAM: | 9 Komponentensicherheit |
9 Komponentensicherheit / 9.4 Integrität von Schweißverbindungen | |
Verlag: | Taylor & Francis |
Jahrgang/Band: | 24 |
Ausgabe/Heft: | 3 |
Erste Seite: | 243 |
Letzte Seite: | 255 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | ADXRD; Low transformation temperature filler materials; Multi-pass welding; Phase transformation; Synchrotron diffraction |
Themenfelder/Aktivitätsfelder der BAM: | Material |
Material / Degradation von Werkstoffen | |
DOI: | 10.1080/13621718.2018.1525150 |
ISSN: | 1362-1718 |
ISSN: | 1743-2936 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 26.09.2018 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 08.02.2019 |