Adequate repair concepts for high-strength steel weld joints considering design influences
- The sustainable and resource-efficient production of wind energy plants requires the use of modern high-strength fine-grain structural steels. This applies to both foundation and erection structures. During the assembly of steel structures, unacceptable defects can occasionally be found in the weld area. In most cases, the economical solution would be local thermal gouging of the affected areas and re-welding. Due to the high shrinkage restraint of the joint groove in the overall structure, the superposition of design and welding-induced residual stress can lead to crack formation and ultimately to component failure, particularly in interaction with the degradation of the microstructure and mechanical properties high-strength steels during the repair process. In this context, component-related investigations (FOSTA-P1311/IGF-Nr. 20162 N) focusing on welding residual stress evolution during local thermal gouging and rewelding of S500MLO and S960QL are carried out using in-situ digitalThe sustainable and resource-efficient production of wind energy plants requires the use of modern high-strength fine-grain structural steels. This applies to both foundation and erection structures. During the assembly of steel structures, unacceptable defects can occasionally be found in the weld area. In most cases, the economical solution would be local thermal gouging of the affected areas and re-welding. Due to the high shrinkage restraint of the joint groove in the overall structure, the superposition of design and welding-induced residual stress can lead to crack formation and ultimately to component failure, particularly in interaction with the degradation of the microstructure and mechanical properties high-strength steels during the repair process. In this context, component-related investigations (FOSTA-P1311/IGF-Nr. 20162 N) focusing on welding residual stress evolution during local thermal gouging and rewelding of S500MLO and S960QL are carried out using in-situ digital image correlation (DIC) and ex-situ X-ray diffraction methods (XRD). Therefore, self-restrained specimens were systematically gouged and rewelded with defined welding heat control (heat input, working temperature) and parameters. By means of structural mechanics calculations, geometries of self-restrained specimens were identified, that represent defined rigidity conditions of repair welds of real components. It could be shown that with increasing restraint intensity significantly higher residual stresses occur in the weld metal and heat affected zone. Furthermore, it revealed that the transverse stresses along the weld seam decrease at the weld seam ends leading to different stress state during gouging and welding. XRD analysis of the local residual stresses after cooling to RT longitudinal and transverse to the weld direction showed a good comparability with global DIC analyses.…
Autor*innen: | Amadeus Becker |
---|---|
Koautor*innen: | Dirk SchröpferORCiD, Arne KrommORCiD, Thomas KannengießerORCiD |
Dokumenttyp: | Vortrag |
Veröffentlichungsform: | Präsentation |
Sprache: | Englisch |
Jahr der Erstveröffentlichung: | 2021 |
Organisationseinheit der BAM: | 9 Komponentensicherheit |
9 Komponentensicherheit / 9.2 Versuchsanlagen und Prüftechnik | |
9 Komponentensicherheit / 9.4 Integrität von Schweißverbindungen | |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Angewandte Physik | |
Freie Schlagwörter: | Digital image correlation; High-strength steels; Repair welding; X-ray diffraction |
Themenfelder/Aktivitätsfelder der BAM: | Energie |
Material | |
Material / Degradation von Werkstoffen | |
Veranstaltung: | Bachelor-, Master-, Doktoranden-Kolloquium der Otto-von-Guericke Universität Magdeburg |
Veranstaltungsort: | Magdeburg, Germany |
Beginndatum der Veranstaltung: | 20.10.2021 |
Enddatum der Veranstaltung: | 20.10.2021 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 28.10.2021 |
Referierte Publikation: | Nein |
Eingeladener Vortrag: | Nein |