Oxidative ageing of elastomers: Experiment and modelling
- During an extensive test programme at the Bundesanstalt für Materialforschung und prüfung, material property changes of EPDM O-rings were investigated at different ageing times and two ageing temperatures of 125∘C and 150∘C. To exclude possible diffusion-limited oxidation (DLO) effects that can distort the data, IRHD microhardness measurements were taken over the cross section of compressed O-rings. Continuous stress relaxation measurements were taken on samples free of DLO effects. The additional effect of physical processes to irreversible chemical ones during a long-term thermal exposure is quantified by the analysis of compression set measurements under various test conditions. By combining the different experimental methods, characteristic times relative to the degradation processes were determined. On the basis of experimental data, a microphysically motivated model that takes into account reversible and irreversible processes was developed. The parameter identification strategyDuring an extensive test programme at the Bundesanstalt für Materialforschung und prüfung, material property changes of EPDM O-rings were investigated at different ageing times and two ageing temperatures of 125∘C and 150∘C. To exclude possible diffusion-limited oxidation (DLO) effects that can distort the data, IRHD microhardness measurements were taken over the cross section of compressed O-rings. Continuous stress relaxation measurements were taken on samples free of DLO effects. The additional effect of physical processes to irreversible chemical ones during a long-term thermal exposure is quantified by the analysis of compression set measurements under various test conditions. By combining the different experimental methods, characteristic times relative to the degradation processes were determined. On the basis of experimental data, a microphysically motivated model that takes into account reversible and irreversible processes was developed. The parameter identification strategy of the material model is based on our experimental investigations on homogeneously aged elastomer O-rings. The simulated results are in good agreement with the experiments.…
Autor*innen: | Maha Zaghdoudi, Anja Kömmling, Matthias JaunichORCiD, Dietmar Wolff |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Continuum mechanics and thermodynamics |
Jahr der Erstveröffentlichung: | 2022 |
Organisationseinheit der BAM: | 3 Gefahrgutumschließungen; Energiespeicher |
3 Gefahrgutumschließungen; Energiespeicher / 3.4 Sicherheit von Lagerbehältern | |
Veröffentlichende Institution: | Bundesanstalt für Materialforschung und -prüfung (BAM) |
Verlag: | Springer |
Verlagsort: | Berlin |
Erste Seite: | 1 |
Letzte Seite: | 9 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Angewandte Physik | |
Freie Schlagwörter: | Compression set; Compression stress relaxation; IRHD microhardness; Modelling |
Themenfelder/Aktivitätsfelder der BAM: | Energie |
Energie / Kerntechnische Entsorgung | |
Material | |
Material / Degradation von Werkstoffen | |
DOI: | 10.1007/s00161-022-01093-9 |
URN: | urn:nbn:de:kobv:b43-545910 |
ISSN: | 1432-0959 |
Verfügbarkeit des Dokuments: | Datei für die Öffentlichkeit verfügbar ("Open Access") |
Lizenz (Deutsch): | Creative Commons - CC BY - Namensnennung 4.0 International |
Datum der Freischaltung: | 04.04.2022 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 25.04.2022 |
Schriftenreihen ohne Nummerierung: | Wissenschaftliche Artikel der BAM |