Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (148)
- Beitrag zu einem Tagungsband (92)
- Vortrag (54)
- Beitrag zu einem Sammelband (25)
- Forschungsbericht (15)
- Sonstiges (4)
- Buchkapitel (3)
- Corrigendum (2)
- Posterpräsentation (2)
- Dissertation (1)
Schlagworte
- Welding (39)
- Residual stresses (31)
- Eigenspannungen (26)
- Hydrogen (22)
- Residual stress (19)
- Restraint (17)
- Wasserstoff (17)
- Hochfester Stahl (16)
- MAG-Schweißen (16)
- Schweißen (15)
Organisationseinheit der BAM
- 9 Komponentensicherheit (112)
- 9.4 Integrität von Schweißverbindungen (106)
- 9.2 Versuchsanlagen und Prüftechnik (50)
- 9.0 Abteilungsleitung und andere (28)
- 8 Zerstörungsfreie Prüfung (6)
- 8.5 Röntgenbildgebung (4)
- 8.4 Akustische und elektromagnetische Verfahren (2)
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.3 Instrumentelle Analytik (1)
- 5 Werkstofftechnik (1)
Paper des Monats
- ja (6)
Eingeladener Vortrag
- nein (54)
Up to the present, the thermomechanical loads during welding and subsequent cooling under design-specific shrinkage restraint resulting from the interaction between the materials and the structure have often not been taken into consideration approperiately for weldability assessment of components. As compared to previous investigations using small specimens this report presents component weld tests under varying intensities of restraint. Online records of the reaction forces and moments demonstrate in which way the intensity of restraint affects the reaction stresses and moments and their meaning for the evaluation of the load level in welded components.
Düring the past decades, weldability studies have predominantly been concentrated on the material and the welding process. In order to achieve a closer insight into the structural effects, component weldability tests have been performed by online monitoring of the reaction forces and moments. As a particular item, the effects of different strengths of the base and filier material on the reaction force and stress build up transverse to the welding direction have been studied at a specific structural restraint. As a most relevant result for practical welding it is demonstrated that the final reaction force and also the reaction stress level in the multilayer butt welds decreases with overmatch of the weld metal.
Hydrogen generally causes lattice distortions and phase transformations when introduced into a metallic crystal lattice. For the investigations reported in this contribution, hydrogen thermal desorption analysis has been carried out to observe the influence of hydrogen desorption on the lattice of super martensitic stainless steel during continuous heating. The lattice expansion parameter and the phase transformations have been monitored during the thermal desorption process, and the influence of hydrogen on such characteristics has been evaluated. It was found that hydrogen has a significant influence on both the lattice parameter and on the thermal expansion. However, hydrogen has no influence on phase transformation during thermal desorption. The hydrogen's desorption behavior in this process was also observed and it turned out that hydrogen desorbs in two stages, i.e., firstly diffusible hydrogen and trapped hydrogen afterward.
A 20 mm thick heat resistant 13CrMoV9-10 steel was welded using a multi-pass submerged arc tandem setup on a 3-D testing facility designed to prevent shrinkage both during the welding and the subsequent cooling to room temperature. The effects of variations in pre-heating and interpass temperatures on the local stresses were monitored by in situ measurement of reaction forces and bending moments during welding and the subsequent dehydrogenation heat treatment. The austenite to bainite transformation and its effects on the overall loads were monitored through the use of a high sampling rate. Increasing the pre-heating and interpass temperatures led to a rise in reaction forces and bending moments. The bending moments originated from the eccentric force transmission over the backing, with a concomitant risk of fracture, especially in the critical root zone. Although the pre-heating and interpass temperatures had a strong effect on the reaction forces, their effect on the bending moments upon cooling to room temperature was negligible.