Effects of Preheating and Interpass Temperature on Stresses in S 1100 QL Multi-Pass Butt-Welds
(2008)
Modern arc processes, such as the modified spray arc (Mod. SA), have been developed for gas metal arc welding of high-strength structural steels with which even narrow weld seams can be welded. High-strength joints are subjected to increasingly stringent requirements in terms of welding processing and the resulting component performance. In the present work, this challenge is to be met by clarifying the influences on hydrogen-assisted cracking (HAC) in a high-strength structural steel S960QL. Adapted samples analogous to the self-restraint TEKKEN test are used and analyzed with respect to crack formation, microstructure, diffusible hydrogen concentration and residual stresses. The variation of the seam opening angle of the test seams is between 30° and 60°. To prevent HAC, the effectiveness of a dehydrogenation heat treatment (DHT) from the welding heat is investigated.
As a result, the weld metals produced at reduced weld opening angle show slightly higher hydrogen concentrations on average. In addition, increased micro- as well as macro-crack formation can be observed on these weld metal samples. On all samples without DHT, cracks in the root notch occur due to HAC, which can be prevented by DHT immediately after welding.
For higher operational temperatures and pressures required in petrochemical plants, the modified 13CrMoV9-10 steel was developed providing high resistance against creep and compressed hydrogen. Extreme care during the welding procedure is necessary for this steel, attributed to low toughness, high strength in as-welded state, and increased susceptibility to stress relief cracking (SRC) during post-weld heat treatment (PWHT). Previous research of SRC in creep-resistant steels discussed mainly thermal and metallurgical factors. Few previous findings addressed the influences of welding procedure on crack formation during PWHT considering real-life manufacturing conditions. These investigations focus on effects of welding heat control on stresses during welding and subsequent PWHT operations close to realistic restraint and heat dissipation conditions using a special 3D testing facility, which was presented in parts I and II of this contribution. Part III addresses investigations on residual stress evolution affecting crack formation and discusses the transferability of results from large-scale testing to laboratory-scale. Experiments with test set-ups at different scales under diverse rigidity conditions and an assessment of the residual stresses of the weld-specimens using X-ray (surface near) and neutron diffraction analysis (bulk) were performed. This study aims to provide a way of investigating the SRC behaviour considering component-specific residual stresses via small-scale testing concepts instead of expensive weld mock-ups.
High-strength steels with yield strengths ≥ 690 MPa are becoming increasingly significant for modern steel constructions. Both quenched and tempered (QT) high-strength steels and steels produced by the thermo-mechanically controlled process (TMCP) are currently available. TMCP-steels are usually provided with a typical mill scale. Apart from the manufacturing process these steels differ also in their chemical composition. The influence of these differences are investigated here with focus on the residual stresses formed during TIG welding. Bead on plate welds have shown characteristic residual stress distributions depending on the type of steel as well as on the heat input and preheat temperature. The following work demonstrates that the fluid flow, induced by the elements present in the mill scale, leads to a deeper penetration of the material. This can also lead to increased residual stresses in the surface of the weld and the HAZ. Furthermore, higher heat input and preheat temperature can induce higher tensile residual stresses − which are evident in the present study.
High-strength steels are increasingly applied in modern steel constructions to meet today’s lightweight requirements. Welding of these steels demands a profound knowledge of the interactions between the welding process, cooling conditions, heat input, and the resulting metallurgical occurrences in the weld and its vicinity. Additionally, welding stresses may be detrimental for the safety and performance of high-strength steel component welds during fabrication and service, especially due to the high yield ratio. For a development of strategies to adjust welding heat control, all these effects should be considered, to reach a complete exploitation of the high-strength steel potential. In recent researches at BAM, multilayer GMAW experiments were performed with high-strength steels, in which cooling conditions and resulting microstructure were analyzed for varied heat control parameters. The application of a unique 3d-operating testing facility and X-ray diffraction measurements allowed the analysis of local stresses in the weld while welding and cooling under component relevant shrinkage restraints. As a result, correlations between material behavior, welding, and cooling condition and the arising multi-axial stresses and forces were found. Based on this study, statements for the development of adapted heat control concepts were derived, which are presented by means of specific analysis examples.
Energy dispersive synchrotron diffraction for in-situ analyses of hydrogen behavior in steels
(2013)
The extent of hydrogen embrittlement phenomenon is dependent on the interaction of hydrogen with the material i.e. diffusion behavior, lattice distortions, phase transformations and residual stresses developments. For the better understanding of the hydrogen interaction with the metal, possibilities of performing in-situ observations of the mentioned factors has to be accomplished. The EDDI (Energy Dispersive Diffraction) beamline at the BESSY II facility in Berlin provides this possibility and was used in order to investigate the aspects of this phenomenon in in-situ scale.
The energy dispersive method entails a synchrotron X-ray white beam with a wide energy range (20–120 keV) which allows a fixed position of the sample and the detector, and combined with the high photons flux it allows a very short measurement time for obtaining a full scale X-Ray Diffraction patterns.
In this contribution, the successful usage of high energy X-rays, applied for the first time for hydrogen behavior observations, provided the ability for evaluating in-situ the hydrogen diffusion behavior and the hydrogen interaction with stresses fields in the material.
Steel samples were charged with hydrogen and examined by Synchrotron radiation.
Two different methods were used in this research; the first is diffusible hydrogen concentration evaluation extracted from the lattice distortions, i.e. changes of the lattice parameter. The second is calculation of the residual stresses present in the sample and the interaction of hydrogen with them, using the known sin2ψ method.
Crack and fatigue resistance are relevant evaluation criteria for welded joints and are decreased by tensile residual
stresses resulting from the welding and cooling process, while compressive residual stresses can have a positive
influence on the characteristics mentioned. In order to generate compressive residual stresses, a set of post weld
treatment procedures is available, like shot peening, hammering, etc. These procedures have the disadvantage that
they are time and cost extensive and have to be applied after welding. As another point, such technologies can only
produce compressive stresses at the top surface, i.e. can only contribute to the reduction of the risk of cracks initiated
at the surface, like fatigue cracks. A chance to generate compressive stresses over the complete weld joint during the
welding procedure is offered by the so-called Low Transformation Temperature (LTT -) filler wires. Compared to
conventional wires, these materials show lower phase transformation temperatures, which can work against coolingrelated
tensile stresses, resulting from respective shrinkage restraint. In consequence, distinct compressive residual
stresses can be observed within the weld and adjacent areas. The strength of these fillers makes them potentially
applicable to high-strength steel welding. Welds produced with different LTT filler wires have shown different levels
and distributions of the resulting residual stresses depending on the specific transformation temperature. The
transformation temperatures are determined by temperature measurement. Classical X-ray diffraction as well as
diffraction methods using high energy synchrotron radiation have been used for residual stress analysis. By means of
high energy synchrotron diffraction in reflection mode residual stress depth gradients can be determined nondestructively.
The phase selective nature of the diffraction measurements enables the simultaneous determination of
the phase specific residual stresses of all contributing crystalline phases within one experiment. The application of
white beam diffraction implies recording of a multitude of diffraction lines within the energy range of the provided
energy spectrum of the white beam. By this means phase specific residual stress depth distributions up to distances of
150 ìm below the surface can be analysed for steel using the energy dispersive set-up of the HMI-beamline EDDI at
the Bessy site, Berlin, providing an energy range between 20-150 keV. As a side effect quantitative phase analysis can
be carried out using white energy dispersive diffraction e.g. the determination of the content of retained austenite in the
weld.