In-situ analysis of solid state phase transformation in TRIP-aided steels by synchrotron diffraction
(2011)
Energy dispersive synchrotron diffraction (EDXRD) analysis and 3 dimensional digital image correlations were conducted to investigate the stress and strain effected transformation behavior during tensile loading of low alloyed TRansformation Induced Plasticity (TRIP) steel. This technique allowed for phase specific stress measurement during certain tensile load steps in the elastic and also plastic regime. Additionally the simultaneous determination of the load dependent phase content was realized. The results show that the martensite transformation starts only after exceeding the overall yield point and is finished before reaching the uniform elongation, whereas a large portion of the austenite remains unchanged in the structure. Furthermore, the martensite transformation related to the stress in the γ-phase and α-phase was analyzed and quantified.
Energy-dispersive x-ray diffraction offers the possibility for measurement and evaluation of diffraction spectra containing information of various diffraction lines of all contributing crystalline phases of a material. Combined strain imaging and diffraction analysis was conducted during the tensile test of a low alloyed transformation-induced plasticity (TRIP) steel in order to investigate the transformation induced plasticity, strain hardening, and load partitioning effects. Optical strain imaging allowed for determination of localized true strains from three-dimensional deformations measured in situ. High-energy synchrotron radiation has permitted diffraction analysis in transmission mode to gather information from the material interior. Phase-specific stress evolution during loading could be observed applying the sin2ψ technique during certain load steps. The strains of the individual lattice planes were determined in different locations under varying angles between loading and perpendicular direction. Using energy-dispersive methods it was also possible to determine the transformation behaviour during elastic and plastic regime taking into account a large number of diffraction lines. The results show that the approach practised here enables one to pull together macroscopic and phase-specific microscopic material behaviour in order to improve existing models for prediction of complex load situations.
Zugeigenspannungen, wie sie beim Schweißprozess durch inhomogene Temperaturverteilungen und Schrumpfungen hervorgerufen werden, können die Lebensdauer geschweißter Verbindungen signifikant herabsetzen. Eine neue und außerordentlich attraktive Methode, um Druckeigenspannungen bereits während des Schweißens gezielt einzustellen, gelingt mit sogenannten LTT (Low Transformation Temperature)-Legierungen. LTT-Legierungen weisen eine martensitische Phasenumwandlung bei relativ niedrigen Temperaturen auf, wobei die damit verbundene Volumenexpansion zu einer Reduktion der Schrumpfeigenspannungen bzw. Erzeugung von Druckeigenspannungen führt. Zum direkten Nachweis der Phasenumwandlungen und der damit verbundenen resultierenden Schweißeigenspannungen wurden erstmals In-situ-Schweißexperimente unter Nutzung hoch energetischer, polychromatischer Synchrotronstrahlung (Weißstrahl) realisiert, um die Umwandlungskinetik während eines realen Schweißprozesses und die daraus resultierenden Schweißeigenspannungen zu analysieren. Es wird gezeigt, dass mit LTT-Legierungen signifikante Druckeigenspannungen in der Schweißnaht erreicht werden.
TRIP-steels offer a good combination between strength and ductility. Therefore TRIP-steels are widely used in the automobile industries. The aim of this work is to study the stability of involved phases during heating and to identify the kinetics of the occuring phase transformations. For that purpose, in-situ diffraction measurements, using high energy synchrotron radiation were conducted. The analysis revealed the decomposition of the metastable austenitic phase into carbide and ferrite along the heating process and the regeneration of the austenite by further heating of the sample.
The development of high-strength structural steels with yield strengths up to 1000 MPa results in the requirement of suitable filler materials for welding. Recently designed low transformation temperature (LTT) alloys offer appropriate strength. The martensitic phase transformation during welding induces compressive residual stress in the weld zone. Therefore, the mechanical properties of welded joints can be improved. The present paper illustrates numerical simulation of the residual stresses in LTT-welds taking into account the effect of varying Ms/Mf-temperatures, and therefore different retained austenite contents, on the residual stresses. Residual stress distributions measured by synchrotron diffraction are taken as evaluation basis. A numerical model for the simulation of transformation affected welds is established and can be used for identification of appropriate Ms-temperatures considering the content of retained austenite.
Direct measurement and quantification of phase transformation in a low-alloyed transformation induced plasticity steels depending on the tensile load as well as determination of the real true stress and true strain values were carried out in-situ using high energy synchrotron radiation. Digital image correlation technique was used to quantify more precisely the true strain values. The aim of the work was to obtain a better understanding of the phase transformation of commercial low-alloyed transformation induced plasticity steel depending on the true strain and true stress values.
In the last decade, high-strength fine grained steels and welding consumables have gained a strong raise of application ranging from mobile cranes to bridge constructions. However, the cracking susceptibility of these steels increases significantly in correspondence with the achieved improvements in yield strength and the loss in plastic deformation reserves.
In order to determine this behavior a series of different standardized cold cracking tests has been developed. One remaining major problem of these tests is the uncertainty about the quantitative intensity of the restraint conditions as well as the corresponding welding residual stresses.
Consequently, the comparison of different tests and welding conditions as well as the transferability of the results onto real parts is difficult at best. The main topic of this paper is the analysis of the restraint conditions and their link with the welding induced residual stresses. The importance of the given standardized selfrestrained tests and first results about the transferability of
results onto real parts are discussed. The influence of the test specimen geometry on the restraint conditions of the test is investigated for a selected test with numerical Simulation using commercial FEA software. Additionally, the residual stresses caused by the welding process are measured and linked with the restraint conditions which are defined mainly by the geometry parameters.
Finally the transferability of the selected cold cracking test results is validated experimentally. The test results of a multilayer weld on high-strength fine grained steel of real size weldments are investigated. For these experiments a 16 MN large scale testing facility is used which is capable of applying the high reaction forces and clamping conditions found at large scale demonstrator parts.
The results show the importance of the quantitative knowledge of the restraint conditions and the welding residual stresses on the cold cracking resistance.
Hot crack assessment during production and processing of metallic materials is an essential prerequisite for the safety of welded structures. The hot cracking investigations presented here were carried out as part of a study aimed at the development of Cr/Ni low transformation temperature filler materials. Low transformation temperature alloys open up the possibility for welding high strength steels. The externally loaded Modified Varestraint Transvarestraint hot cracking test was employed in the experiments described. The hot cracking resistance was evaluated with the help of light microscopy applied at the specimen surface. The proportionality between hot cracking susceptibility and Cr/Ni alloy content was explained by the altered solidification kinetics and by the enlarged solidification interval. The internal crack paths and the three-dimensional structure of the crack net in the material volume were examined using X-ray computer tomography. The total crack lengths for different material depths and circumjacent rectangular volumes, respectively, were be determined. An increasing hot cracking susceptibility with increasing Cr/Ni alloy content was also be established for the specimen volume.