Robust Determination of Fatigue Crack Propagation Thresholds from Crack Growth Data

  • To assess the ability of cracks to grow, a robust determination of the threshold against fatigue crack propagation ∆Kth is of paramount importance. The standards ASTM E647 and ISO 12108 introduce operational definitions of ∆Kth based on the crack propagation rate da/dN. For evaluating ∆Kth, both suggest fitting a linear function to a defined subset of the logarithmic ∆K – da/dN test data, where ∆Kth follows by evaluating the linear function at da/dN = 10-7 mm/cycle and da/dN = 10-8 mm/cycle, respectively. In general, this kind of fit suffers from a bad representation of the actual curvature of the crack propagation curve. Therefore, we propose a robust method for evaluating ∆Kth using a non-linear function that reduces the artificial conservativeness induced by the evaluation method as well as the susceptibility to scatter in test data and the influence of test data density. The method is calibrated against a large set of S690QL crack growth data obtained from a total of 48 specimens,To assess the ability of cracks to grow, a robust determination of the threshold against fatigue crack propagation ∆Kth is of paramount importance. The standards ASTM E647 and ISO 12108 introduce operational definitions of ∆Kth based on the crack propagation rate da/dN. For evaluating ∆Kth, both suggest fitting a linear function to a defined subset of the logarithmic ∆K – da/dN test data, where ∆Kth follows by evaluating the linear function at da/dN = 10-7 mm/cycle and da/dN = 10-8 mm/cycle, respectively. In general, this kind of fit suffers from a bad representation of the actual curvature of the crack propagation curve. Therefore, we propose a robust method for evaluating ∆Kth using a non-linear function that reduces the artificial conservativeness induced by the evaluation method as well as the susceptibility to scatter in test data and the influence of test data density. The method is calibrated against a large set of S690QL crack growth data obtained from a total of 48 specimens, and validated against a set of S355NL and S960QL data (3 specimens each), obtained as a part the IBESS (integral fracture mechanics determination of the fatigue strength of welds) project.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • 220630_ECF23_Schonherr_Josef.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:J. A. Schönherr
Koautor*innen:Larissa Duarte, Mauro Madia, Uwe Zerbst, M. B. Geilen, M. Klein, M. Oechsner
Dokumenttyp:Vortrag
Veröffentlichungsform:Präsentation
Sprache:Englisch
Jahr der Erstveröffentlichung:2022
Organisationseinheit der BAM:9 Komponentensicherheit
9 Komponentensicherheit / 9.4 Integrität von Schweißverbindungen
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:ASTM E647; Data evaluation methods; Experimental determination; Fatigue crack propagation threshold; ISO 12108
Themenfelder/Aktivitätsfelder der BAM:Material
Material / Degradation von Werkstoffen
Veranstaltung:ECF23 (European Conference on Fracture 2022)
Veranstaltungsort:Madeira, Portugal
Beginndatum der Veranstaltung:27.06.2022
Enddatum der Veranstaltung:01.07.2022
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:13.07.2022
Referierte Publikation:Nein
Eingeladener Vortrag:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.