Influence of mean stress and overaging on fatigue life of aluminum alloy EN AW-2618A
- Fatigue tests were performed on the forged aluminum alloy EN AW-2618A in the T61 state. Different stress ratios (R = -1, R = 0.1) were selected to study the influence of mean stress on fatigue life. Two overaged states (10 h/230 ◦C, 1000 h/230 ◦C) were also tested to investigate the influence of overaging on fatigue life. Transmission electron microscopy (TEM) was used to characterize the precipitates (S-phase), which are mainly responsible for the strength of the alloy. A fractographic analysis was also performed to determine the failure mode. Overaging reduces the fatigue life compared to the T61 state. The longer the aging time, the lower the fatigue resistance. The reason is the decrease in (yield) strength, which correlates with the radius of the S-phase: the precipitate radius increases by a factor of approximately two for the overaged states compared to the initial state. The analysis of the fracture surfaces showed crack initiation occurs predominantly on the outer surface andFatigue tests were performed on the forged aluminum alloy EN AW-2618A in the T61 state. Different stress ratios (R = -1, R = 0.1) were selected to study the influence of mean stress on fatigue life. Two overaged states (10 h/230 ◦C, 1000 h/230 ◦C) were also tested to investigate the influence of overaging on fatigue life. Transmission electron microscopy (TEM) was used to characterize the precipitates (S-phase), which are mainly responsible for the strength of the alloy. A fractographic analysis was also performed to determine the failure mode. Overaging reduces the fatigue life compared to the T61 state. The longer the aging time, the lower the fatigue resistance. The reason is the decrease in (yield) strength, which correlates with the radius of the S-phase: the precipitate radius increases by a factor of approximately two for the overaged states compared to the initial state. The analysis of the fracture surfaces showed crack initiation occurs predominantly on the outer surface and is associated with the primary phases.…
Autor*innen: | Ying Han, Julius Kruse, Julian Rosalie, J. Radners, P. von Hartrott, Birgit SkrotzkiORCiD |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Materials Science & Engineering A |
Jahr der Erstveröffentlichung: | 2023 |
Organisationseinheit der BAM: | 5 Werkstofftechnik |
5 Werkstofftechnik / 5.1 Mikrostruktur Design und Degradation | |
5 Werkstofftechnik / 5.2 Metallische Hochtemperaturwerkstoffe | |
9 Komponentensicherheit | |
9 Komponentensicherheit / 9.4 Integrität von Schweißverbindungen | |
Veröffentlichende Institution: | Bundesanstalt für Materialforschung und -prüfung (BAM) |
Verlag: | Elsevier B.V. |
Jahrgang/Band: | 886 |
Aufsatznummer: | 145660 |
Erste Seite: | 1 |
Letzte Seite: | 10 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Aging; Aluminum alloys; Electron microscopy; Fatigue; Microstructure; S-Phase |
Themenfelder/Aktivitätsfelder der BAM: | Material |
DOI: | 10.1016/j.msea.2023.145660 |
URN: | urn:nbn:de:kobv:b43-583708 |
ISSN: | 0921-5093 |
Verfügbarkeit des Dokuments: | Datei für die Öffentlichkeit verfügbar ("Open Access") |
Lizenz (Deutsch): | Creative Commons - CC BY - Namensnennung 4.0 International |
Datum der Freischaltung: | 21.09.2023 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 12.02.2024 |
Schriftenreihen ohne Nummerierung: | Wissenschaftliche Artikel der BAM |