Observation of the weld pool shape in partial penetration welding and its influence on solidification crack formation for high-power laser beam welding
- Solidification cracking is still a particular problem in laser beam welding, especially in the welding of thick-walled plates. In this study, the influence of weld pool geometry on solidification cracking in partial penetration welding of thick plates is a subject of discussion. For this purpose, a special experimental setup of steel and quartz glass in butt configuration and lateral with high speed camera was used to capture the weld pool shape. Additionally, laser beam welding experiments were carried out to compare the crack positions and the cross section with the high-speed camera observations. The results showed a bulge in the weld pool root separated from the upper region by a nick area. This leads to the fact that three different longitudinal lengths with different solidification areas are taking place. This temporal sequence of solidification strongly promotes the solidification cracks in the weld root.
Autor*innen: | Nasim BakirORCiD |
---|---|
Weitere Person: | Ömer Üstündag, Andrey GumenyukORCiD, Michael RethmeierORCiD |
Dokumenttyp: | Vortrag |
Veröffentlichungsform: | Präsentation |
Sprache: | Englisch |
Jahr der Erstveröffentlichung: | 2021 |
Organisationseinheit der BAM: | 9 Komponentensicherheit |
9 Komponentensicherheit / 9.3 Schweißtechnische Fertigungsverfahren | |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Laser beam welding; Partial penetration; Solidification cracking |
Themenfelder/Aktivitätsfelder der BAM: | Material |
Veranstaltung: | Lasers in Manufacturing Conference 2021 |
Veranstaltungsort: | Online meeting |
Beginndatum der Veranstaltung: | 21.06.2021 |
Enddatum der Veranstaltung: | 24.06.2021 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 21.10.2021 |
Referierte Publikation: | Nein |
Eingeladener Vortrag: | Nein |