Comparison between GTA and laser beam welding of 9%Ni steel for critical cryogenic applications
- IncomparisonwithGTAweldedjoints,highertensilestrengthcomparabletothatofthebasemetalwasobtained for laser beam welded joints due to fine martensitic microstructure. Impact fracture toughness values with much lower mismatching were obtained for laser beam welded joints due to similarity in the microstructures of its weld metal and HAZ. In this case, the lower impact fracture toughness obtained (1.37J/mm2) was much higher than that of the GTA welded joints (0.78J/mm2), which was very close to the specified minimum value (≥0.75J/mm2). In contrast to other research works, the overall tensile and impact properties are influenced not only by the fusion zone microstructure but also by the size of its hardened area as well as the degree of its mechanical mismatching, as a function of the welding process. A better combination of tensile strength and impact toughness of the concerned steel welded joints is assured by autogenous laser beam welding process.
Autor*innen: | A.M. El-Batahgy, Andrey GumenyukORCiD, S. Gook, Michael RethmeierORCiD |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Journal of Materials Processing Tech. |
Jahr der Erstveröffentlichung: | 2018 |
Organisationseinheit der BAM: | 9 Komponentensicherheit |
9 Komponentensicherheit / 9.3 Schweißtechnische Fertigungsverfahren | |
Verlag: | Elsevier |
Ausgabe/Heft: | 261 |
Erste Seite: | 193 |
Letzte Seite: | 201 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | 9%Ni steel; Fusion zone size; GTAW; Impact absorbed energy; Laser beam welding; Microstructure Tensile strength |
Themenfelder/Aktivitätsfelder der BAM: | Material |
DOI: | 10.1016/j.jmatprotec.2018.05.023 |
ISSN: | 0924-0136 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 23.08.2018 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 23.08.2018 |