XCT discloses the Impact of Machining on Mechanical Properties of Diesel Particulate Filter Materials
- Microstructural changes in porous cordierite for diesel particulate filter applications caused by machining were characterized using microtensile testing and X-ray computed tomography (XCT). Young’s modulus was determined on ~215-380 m thick machined samples by digital image correlation. Results show a decrease of Young’s modulus due to machining of the thin samples. Explanation of this phenomenon was provided by XCT: the presence of debris due to machining and the variation of porosity due to removal of the outer layers were quantified and correlated with the introduction of further microcracking.
Autor*innen: | Giovanni BrunoORCiD, Christian Gollwitzer |
---|---|
Koautor*innen: | A. Lange, Yener Onel, R. C. Cooper, T.R. Watkins, A. Shyam |
Dokumenttyp: | Vortrag |
Veröffentlichungsform: | Präsentation |
Sprache: | Englisch |
Jahr der Erstveröffentlichung: | 2018 |
Organisationseinheit der BAM: | 8 Zerstörungsfreie Prüfung |
8 Zerstörungsfreie Prüfung / 8.5 Röntgenbildgebung | |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Diesel Particulate Filter Materials; Mechanical Properties |
Themenfelder/Aktivitätsfelder der BAM: | Material |
Material / Degradation von Werkstoffen | |
Veranstaltung: | ICT Conference 2018 |
Veranstaltungsort: | Wels, Austria |
Beginndatum der Veranstaltung: | 06.02.2018 |
Enddatum der Veranstaltung: | 09.02.2018 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 26.04.2018 |
Referierte Publikation: | Nein |
Eingeladener Vortrag: | Nein |