Characterization of multiphase metal matrix composites by means of CT and neutron diffraction
- The present study examines the relationship between the microstructure of multiphase metal matrix composites and their damage mechanisms. The matrix AlSi12CuMgNi was combined with 15% vol. Al₂O₃ (short fibers), and with 7% vol. Al₂O₃ + 15% vol. SiC (short fibers and whiskers, respectively). The experimental approach encompasses 3D microstructure characterization by means of computed tomography of samples (a) as-cast, (b) after heat treatment, and (c) after compression tests at room temperature. The volume fraction of different phases, their distribution, their orientation, and the presence of defects and damage are studied. The influence of the addition of SiC particles on mechanical properties of composite was investigated. Phase-specific load partition analysis for samples with fiber plane parallel to load was performed by using neutron diffraction (ND) during in-situ compression. ND results show damage in the Si phase, while Al₂O₃ short fibers carry load without damage untilThe present study examines the relationship between the microstructure of multiphase metal matrix composites and their damage mechanisms. The matrix AlSi12CuMgNi was combined with 15% vol. Al₂O₃ (short fibers), and with 7% vol. Al₂O₃ + 15% vol. SiC (short fibers and whiskers, respectively). The experimental approach encompasses 3D microstructure characterization by means of computed tomography of samples (a) as-cast, (b) after heat treatment, and (c) after compression tests at room temperature. The volume fraction of different phases, their distribution, their orientation, and the presence of defects and damage are studied. The influence of the addition of SiC particles on mechanical properties of composite was investigated. Phase-specific load partition analysis for samples with fiber plane parallel to load was performed by using neutron diffraction (ND) during in-situ compression. ND results show damage in the Si phase, while Al₂O₃ short fibers carry load without damage until failure. The computed tomography observations confirm the load partition analysis.…
Autor*innen: | Sandra Cabeza |
---|---|
Koautor*innen: | Giovanni BrunoORCiD, Tatiana MishurovaORCiD |
Dokumenttyp: | Beitrag zu einem Tagungsband |
Veröffentlichungsform: | Graue Literatur |
Sprache: | Englisch |
Jahr der Erstveröffentlichung: | 2016 |
Veröffentlichende Institution: | Bundesanstalt für Materialforschung und -prüfung (BAM) |
Herausgeber (Institution): | 19th World Conference on Non-Destructive Testing 2016 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | aluminum; composite; neutron diffraction; residual stress; synchrotron CT; thermal treatment |
Veranstaltung: | WCNDT |
Veranstaltungsort: | München, Germany |
Beginndatum der Veranstaltung: | 13.06.2016 |
Enddatum der Veranstaltung: | 17.06.2016 |
URN: | urn:nbn:de:kobv:b43-365499 |
Verfügbarkeit des Dokuments: | Datei für die Öffentlichkeit verfügbar ("Open Access") |
Lizenz (Deutsch): | Creative Commons - Namensnennung-Keine Bearbeitung |
Datum der Freischaltung: | 30.06.2016 |
Referierte Publikation: | Nein |
Schriftenreihen ohne Nummerierung: | Wissenschaftliche Artikel der BAM |