Thermoelectric properties of doubly substituted La0.95Sr0.05Co1-xCrxO3 (0 ≤ x ≤ 0.5) ceramics

  • Dense La0.95Sr0.05Co1-xCrxO3 (0 ≤ x ≤ 0.5) ceramics were synthesized by solid-state reaction and conventional sintering. Room-temperature crystal structure and microstructure were investigated and the thermoelectric properties were measured in the temperature range 323 K – 1020 K. All compositions are single phase with rhombohedral structure, and the lattice parameter of La0.95Sr0.05Co1-xCrxO3 increases with increasing Cr content. La0.95Sr0.05Co1-xCrxO3 is a p-type small polaron conductor. The charge carrier concentration is determined by both substitution of La3+ with Sr2+ and thermally-activated charge disproportionation of Co3+ and / or Cr3+. Above 550 K, the substitution of Co with Cr increases the Seebeck coefficient and reduces the electrical conductivity. Below 550 K, the trend of Seebeck coefficient with Cr content is not clear due to the thermally activated charge disproportionation. At low temperature, the electrical conductivity shows a minimum with Cr content of x = 0.4,Dense La0.95Sr0.05Co1-xCrxO3 (0 ≤ x ≤ 0.5) ceramics were synthesized by solid-state reaction and conventional sintering. Room-temperature crystal structure and microstructure were investigated and the thermoelectric properties were measured in the temperature range 323 K – 1020 K. All compositions are single phase with rhombohedral structure, and the lattice parameter of La0.95Sr0.05Co1-xCrxO3 increases with increasing Cr content. La0.95Sr0.05Co1-xCrxO3 is a p-type small polaron conductor. The charge carrier concentration is determined by both substitution of La3+ with Sr2+ and thermally-activated charge disproportionation of Co3+ and / or Cr3+. Above 550 K, the substitution of Co with Cr increases the Seebeck coefficient and reduces the electrical conductivity. Below 550 K, the trend of Seebeck coefficient with Cr content is not clear due to the thermally activated charge disproportionation. At low temperature, the electrical conductivity shows a minimum with Cr content of x = 0.4, as a result of trapped polarons in the Cr sites. By substituting Co with Cr, the power factor below 800 K is reduced and that above 800 K is improved. The thermal conductivity is effectively reduced by doping Cr. The highest ZT value of 0.053 at 373 K is achieved for x = 0, but it decreases rapidly with increasing temperature. Substitution of Co with Cr can effectively improve the ZT values at high temperatures. In the temperature range 700 K – 1000 K, ZT increases with increasing Cr content, the highest being 0.04 at 1000 K for the composition with x = 0.5, more than 4 times the value of the La0.95Sr0.05CoO3 compound.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • ICT2018-CongChen.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Cong Chen
Koautor*innen:F. Giovannelli, T. Chartier, F. Delorme
Dokumenttyp:Vortrag
Veröffentlichungsform:Präsentation
Sprache:Englisch
Jahr der Erstveröffentlichung:2018
Organisationseinheit der BAM:8 Zerstörungsfreie Prüfung
8 Zerstörungsfreie Prüfung / 8.5 Röntgenbildgebung
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:Double substitution; P-type; Perovskite; Thermoelectrics
Themenfelder/Aktivitätsfelder der BAM:Material
Veranstaltung:International / European Conference on Thermoelectrics
Veranstaltungsort:Caen, France
Beginndatum der Veranstaltung:02.07.2018
Enddatum der Veranstaltung:05.07.2018
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:09.07.2018
Referierte Publikation:Nein
Eingeladener Vortrag:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.