Structure, acid resistance and high-temperature behavior of silica-based one-part AAMs

  • One-part geopolymers (OPGs) are a sort of alkali-activated materials (AAMs) which production avoids the use of highly-alkaline activator-solutions and contributes to a better acceptance of alternative mineral binders in terms of safety-related and economic aspects. In the present contribution OPGs were synthesized by blending silica sources (two industrial silicas and two biogenic silicas) with sodium aluminate and only water must be added to initiate the hardening, i.e. mixing is performed in the same way as for conventional Portland cements. The OPGs were characterized by XRD, and SEM and the degrees of reaction of the silicas were determined by a chemical dissolution method. The industrial silicas led to the formation of geopolymer-zeolite composites, that contained, besides geopolymeric gel, crystalline tectosilicates (e.g. zeolite A and hydrosodalite) and depending on the starting composition also unreacted silica. The biogenic silicas provided a higher reactivity and avoided theOne-part geopolymers (OPGs) are a sort of alkali-activated materials (AAMs) which production avoids the use of highly-alkaline activator-solutions and contributes to a better acceptance of alternative mineral binders in terms of safety-related and economic aspects. In the present contribution OPGs were synthesized by blending silica sources (two industrial silicas and two biogenic silicas) with sodium aluminate and only water must be added to initiate the hardening, i.e. mixing is performed in the same way as for conventional Portland cements. The OPGs were characterized by XRD, and SEM and the degrees of reaction of the silicas were determined by a chemical dissolution method. The industrial silicas led to the formation of geopolymer-zeolite composites, that contained, besides geopolymeric gel, crystalline tectosilicates (e.g. zeolite A and hydrosodalite) and depending on the starting composition also unreacted silica. The biogenic silicas provided a higher reactivity and avoided the formation of crystallite by-products. The differences in the microstructures caused differences in the mechanical strength of the specimens. The treatment of the OPG composites at moderate elevated temperatures revealed promising behavior on thermal dehydration in terms of shrinkage and residual strength up to 700 °C. Above 700 °C sintering and partial melting occurred, and new phase formation commenced. After exposure to 1000 °C the specimens appeared virtually amorphous or formed stuffed silica structures of nepheline- or carnegieite-type type. The investigations of the OPG based mortars on their resistance against sulfuric acid in accordance with DIN 19573 (Appendix A) revealed very high residual strengths up to 78 % after treatment with H2SO4 (pH 1) for 70d. A mechanism of dissolution of the primary aluminosilicate reaction products of the pastes and the precipitation of a silica gel that protects the remaining aluminosilicates and decelerates further corrosion was found to be the main reason for the good performance under acidic conditions. The addition of CaO-containing feedstocks enhanced hardening, but at a certain content the resistance against sulfuric acid decreased, due to the formation of gypsum on exposure to sulfate. In addition, the mortars exhibited excellent shrinkage behavior as well as good bond to concrete substrates with pull-off strength up to > 3 MPa. The workability of the fresh mortars provided very good manual applicability; automatic applications such as sprayed and spun mortars will require further optimization regarding rheological properties. In summary, the studied OPG are promising materials for the construction and the repair of concrete structures, such as sewers, that are affected by biogenic sulfuric acid corrosion.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • 2018_ECI II - One-part geopolymers_gekuerzt.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Gregor GluthORCiD
Koautor*innen:Patrick Sturm, Sebastian Greiser, Christian Jäger, H.J.H. Brouwers, Hans-Carsten Kühne
Dokumenttyp:Vortrag
Veröffentlichungsform:Präsentation
Sprache:Englisch
Jahr der Erstveröffentlichung:2018
Organisationseinheit der BAM:6 Materialchemie
6 Materialchemie / 6.3 Strukturanalytik
7 Bauwerkssicherheit
7 Bauwerkssicherheit / 7.4 Baustofftechnologie
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurbau
Freie Schlagwörter:Acid resistance; Alkali-activated materials; Geopolymers; Solid state NMR
Themenfelder/Aktivitätsfelder der BAM:Infrastruktur
Veranstaltung:Alkali Activated Materials and Geopolymers
Veranstaltungsort:Tomar, Portugal
Beginndatum der Veranstaltung:27.05.2018
Enddatum der Veranstaltung:01.06.2018
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:04.06.2018
Referierte Publikation:Nein
Eingeladener Vortrag:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.