The ISO 3690 standard “Determination of hydrogen content in arc weld metal” requires a thermal activation of the diffusible hydrogen in a piece of weld metal for the subsequent ex situ concentration measurement by carrier gas hot extraction CGHE or thermal desorption spectroscopy (TCD). Laser-induced breakdown spectroscopy (LIBS) offers a time and spatially resolved, almost non-destructive, in situ measurement of hydrogen at surfaces without sample preparation. We measured hydrogen in steels, which were charged either electrochemically or by high-pressure hydrogen gas, and compared the results. Further, the feasibility of quantitative hydrogen line scan measurements with LIBS was demonstrated by measuring hydrogen at water jet cut surfaces. The hydrogen concentrations measured with the help of LIBS were compared with CGHE measurements. It was observed that hydrogen can be reliably measured with LIBS for concentrations larger than 2 wt.-ppm. The maximum hydrogen concentration achieved using electrochemical charging was 85.1 ppm. The results show that LIBS is a promising technique for time- and spatially resolved measurements of hydrogen in steels.
Measurement of hydrogen concentration in steel using Laser-induced Breakdown spectroscopy (LIBS)
(2023)
Currently, the ISO 3690 standard requires a thermal activation of the diffusible hydrogen in weld metal for the subsequent ex situ concentration measurement by TDS. Laser-induced breakdown spectroscopy (LIBS) would offer a time and spatially resolved, almost non-destructive, measurement of hydrogen at surfaces. We could already show that this analysis technique allows for highly accurate in situ measurements of chemical compositions of e.g. Mn, Cr and Ni during welding e.g. in the melt pool, the weld metal or the heat affected zone. For quantitative LIBS measurements of hydrogen in steel, certified reference materials with different hydrogen concentrations were used for calibration.
There is a significant problem in welding steels: A critical combination of diffusible hydrogen, hardness microstructure and weld residual stresses can cause cold cracks to form in the weld microstructure. We investigated hydrogen in steels, which was loaded either electrochemically or with high-pressure hydrogen gas. Subsequently, various experiments were conducted to verify the feasibility of hydrogen measurements with LIBS. For example, depth profiles of hydrogen distribution could be obtained. Furthermore, samples were water jet cut and a line scan was made over the cross section to obtain a spatially resolved representation of the hydrogen. Total hydrogen concentrations were determined using carrier gas hot extraction. Our results show that LIBS is a promising technique for time and spatially resolved measurement of hydrogen in steels.