Wasserstoff
Filtern
Dokumenttyp
- Vortrag (192)
- Zeitschriftenartikel (60)
- Beitrag zu einem Tagungsband (23)
- Posterpräsentation (21)
- Forschungsbericht (4)
- Sonstiges (3)
- Dissertation (1)
Schlagworte
- Hydrogen (74)
- Wasserstoff (45)
- H2Safety@BAM (32)
- Safety (24)
- LH2 (20)
- Welding (19)
- Standards (12)
- Diffusion (11)
- Hydrogen assisted cracking (11)
- Schweißen (11)
Organisationseinheit der BAM
- 9 Komponentensicherheit (89)
- 3 Gefahrgutumschließungen; Energiespeicher (84)
- 9.0 Abteilungsleitung und andere (69)
- 3.5 Sicherheit von Gasspeichern (64)
- 2 Prozess- und Anlagensicherheit (55)
- 2.1 Sicherheit von Energieträgern (53)
- 8 Zerstörungsfreie Prüfung (51)
- 9.4 Integrität von Schweißverbindungen (42)
- 1 Analytische Chemie; Referenzmaterialien (32)
- 1.4 Prozessanalytik (31)
Paper des Monats
- ja (3)
In this lecture, the safety assessment of hydrogen gas storage systems is presented using the example of composite pressure vessels. The main element is a probabilistic approval approach based on five steps. Firstly, the testing and evaluation of properties at the beginning of life are shown. Secondly, methods for artificial aging and the effect on the residual strength are presented. Thirdly, testing against dedicated accidents is introduced. Fourthly, effects on the surveillance of production quality are discussed. Finally, degradation and the end of life are estimated. Background information and examples are given for each step. The assessment presented is a method applicable for many safety-related systems.
In this presentation safety aspects of hydrogen transportation are discussed. At first, the regulatory background and level of safety are presented. In the second part, the modelling of consequence due to sudden rupture of pressure receptacles is explained. Finally, the results are used to define a limit for consequence to enable an acceptable and safe transport of hydrogen.
The publication is an extended abstract on the modelling of the manufacturing process related residual stresses in type 4 pressure vessels for hydrogen storage. A 2D analytical model based on the classical laminate theory and a 3D finite element model are introduced. The calculated residual stress state after the filament winding process as well as the stress state in service are presented and discussed.
Climate and air quality are of fundamental interest worldwide.
Gas metrology provides profound solutions to measurement tasks on climate and air quality, e.g., when greenhouse gases or pollutants are to be quantified.
Metrological capabilities are demonstrated through participation in the framework of the CIPM Mutual Recognition Arrangement (CIPM MRA).
In Germany, this is covered by three institutes: Bundesanstalt für Materialforschung und -prüfung (BAM), Physikalisch-Technische Bundesanstalt (PTB), and Umweltbundesamt (UBA).
Together, the three laboratories realize the unit mole by means of the national gas standards and offer services to their customers that are backed-up by internationally accepted calibration and measurement capabilities (CMCs).
Die Umstellung der Wirtschaft auf wasserstoffbasierte Energieversorgung soll in Deutschland vor allem auf Basis der Umstellung des bestehenden Erdgasnetzes erfolgen. Dabei sollen ca. 90 % dieser Fernleitungsnetze auf dem bestehenden Erdgasnetz basieren. Die Beimischung von Wasserstoff zum Erdgas als auch der reine Wasserstofftransport werfen jedoch die Frage auf, ob und wie kompatibel die eingesetzten Materialien sind. Die Reparatur- und Erweiterungsfähigkeit von Erdgas-Bestandspipelines ist zu klären, wenn diese auf Wasserstoff umgestellt werden. Denn gerade Gashochdruckleitungen müssen regelmäßig gewartet und erweitert werden, um einen ordnungsgemäßen Betrieb sicherzustellen. Insbesondere das Schweißen unter Betriebsdruck bzw. an in Betrieb befindlichen Gasleitungen ist eine der wichtigsten Instandhaltungstechnologien, unabhängig von der Zusammensetzung des geförderten Mediums. Es ist daher dringend notwendig, eine geeignete Teststrategie zu erarbeiten, welche die nötigen Vorrausetzungen für sicheres Schweißen an in Betrieb befindlichen Druckwasserstoffleitungen schafft und entsprechende Kriterien für die Praxis liefert. Im Projekt H2-SuD - Einfluss des Schweißens auf die Wasserstoffaufnahme und Degradation im Betrieb befindlicher H2-Ferngasleitungen - soll geklärt werden, ob und wie stark mit einer Eigenschaftsdegradation geschweißter Rohrstähle in Gasnetzen in Folge einer Wasserstoffaufnahme zu rechnen ist. Die Präsentation gibt dazu einen kurzen Überblick über den aktuellen Status des Projektes. Die Förderung erfolgt im Rahmen der DVGW-Innovationsprogammes Wasserstoff (Nr. G 202131).
This presentation describes the usability of the hollow tensile specimen technique for in-situ material testing in a hydrogen atmosphere.
In addition, the presentation provides an outlook on the methodology for investigating the suitability of pipeline steels and their weld seams for hydrogen operation.
EPDM, HNBR and FKM materials were exposed at 150 ◦C to air under atmospheric pressure and to hydrogen at 50 bar for different ageing times. All measurements after hydrogen exposure were conducted on samples in degassed condition to assess irreversible effects resulting from that exposure and to compare them to those after ageing in air. Density, hardness, tensile properties, compression set, and hydrogen permeability of all samples were analysed. In both ageing environments, HNBR exhibited the most significant changes of material properties.
However, for both EPDM and HNBR, considerably less severe ageing effects were observed under hydrogen in comparison to ageing in air. On the other hand, FKM showed about the same low level of deterioration in both ageing environments but exhibited poor resistance against damage due to rapid gas decompression in hydrogen environment that can lead to seal failure. The obtained results may serve as a guidance toward a better understanding for design and utilisation of elastomeric materials in future hydrogen infrastructure components.
Joining and welding technologies are of high importance for the manufacturing of components and parts used in sustainable energy generation, conversion, and transport. In that connection, offshore and on-shore installed wind turbines are of high interest for the generation of electrical energy as well as photo-voltaic systems (solar cells). The electricity can be either directly transported or conversed via power-to-gas e.g., to hydrogen. In that scope, electrolyzer up to MW-range are of interest as well as the conver-sion back to electricity via fuel cells. In addition, hydrogen is a key element of the decarburization of in-dustries as well as the mobility sector encompassing sea, air and land transportation driven by hydrogen or its derivates. Well-known examples cover the direct reduction of iron ore to replace the conventional blast furnace process up to gas turbines or fuel cells for home-end use. All mentioned technologies re-quire reliable components, which are to a high extend dependent on joining and especially welding pro-cessing of materials. Especially, the (petro-) chemical industry has many years of experience with both materials used in hydrogen applications. The challenge is e.g., the transition to mass production of sys-tem components of electrolyzers/fuel cells and for distribution grids. At this point, the scalability of cur-rently applied joining processes often limits the economic efficiency, whereas especially laser welding or additive manufacturing will be of high interest. In that connection, it is very important to provide answers by joint research of universities, institutes, and industrial companies. Very often, solutions are already available and “just” have to be investigated and adapted for the new application, like repair welding of NG pipelines. For that reason, we want to set up a series of comprehensive papers with the aforementioned title. The idea is to get an in-depth but manageable overview of the importance of joining technologies in sustaina-ble energy generation, conversion, and transport encompassing current processes, limitations, and fur-ther perspectives. In that connection, the additive manufacturing is gaining more and more attention. If applicable, current challenges in the adaption or creation of new standards/regulations shall be addressed.
As energy carrier of the future, green hydrogen can make a decisive contribution to a sustainable energy supply. Particularly important is the decarbonization of heavy industry. Therefore, a reliable supply of hydrogen must be guaranteed. A hydrogen pipeline grid can achieve this purpose. In Europe concrete plans for a hydrogen pipeline grid already exist, as the so called “European Hydrogen backbone”. As building a completely new pipeline grid is economically not justifiable, a dual-way strategy of repurposing natural gas (NG) pipelines and newly built pipelines is intended. Long distance pipeline grids require regular maintenance and repairs. For natural gas (NG) pipelines in-service welding is state of the art. Concepts such as hot-tapping (drilling into pressurized pipelines) and “stoppling” (sealing off pipeline sections after installing bypasses or pressure relieves) allow the repair of damaged pipeline sections or the installation of new branches without shutting the pipeline down, which in most cases isn’t possible from an economic standpoint. The EIGA 121/14 guideline already pointed out in 2014 that “a hydrogen hot-tap shall not be considered a routine procedure”. This shows that the determination of the transferability of these repair concepts to hydrogen pipelines is of utmost importance. Due to the degrading effects of hydrogen on mechanical proper-ties, commonly referred to as “hydrogen embrittlement” it is necessary to understand and investigate the occurring effects. In the special case of repair welding on in-service hydrogen pipelines an increased hydro-gen uptake due to a large heat input and microstructural changes in the material needs to be considered. Therefore, material degradation must be investigated to determine whether modifications of repair procedures are necessary to ensure a reliable and safe hydrogen transportation via pipelines. For this reason, this paper gives an overview on existing weld repair concepts and its risks and limitations in terms of hydrogen absorption and possible embrittlement effects when transferred to hydrogen pipelines. The complexity lies in a large variety of materials (low alloyed steels), pipeline diameters and corresponding welded joints. The material compatibility of materials in used (repurposed NG-pipelines) and new condition must be investigated. Particularly for repurposed/used pipelines the effect of a pre-matured/corroded inner surface and sometimes insufficient documentation of the material “history” needs to be considered. An overview on ongoing and completed R&D-projects with respect to repair concepts for hydrogen pipelines and hydrogen effects on pipeline materials is given. The focus hereby lies on possible methods of material testing and modeling. Its current difficulties, limits and possible solution will be discussed.
Contemporary steels creep-resistant steels like the 13CrMoV9-10 are used as thick plates e.g., for applications in hydrocrackers. The large plate thickness requires high efficiency welding processes like submerged arc welding (SAW) and a mandatory post weld heat treatment (PWHT). The PWHT-parameters stem from a combination of empirical knowledge and traditional experiments on free shrinking (FS) welds. In that connection, the formation of so-called stress-relief cracking (SRC) must be anticipated. The SRC susceptibility of a welded component is a complex combination and interaction of com-ponent specific, thermal, and metallurgical factors. Many of which have to date not been conclusively researched. For example, it is well known that SRCs develop during PWHT due to formation and growth of carbides on prior austenite grain boundaries, resulting in a significant hardness increase (secondary hardening) and toughness decrease. This leads to a high SRC susceptibility of the coarse grain heat-affected zone (CGHAZ) of the last weld bead during PWHT. This is intensified in case of high residual stresses from the component-specific, structurally induced stiffness. In combination with multi-layer welding this leads to a multiaxial stress distribution. Nonetheless, the combined effect of PWHT and high-residual stresses on the SRC formation is merely unknown. For that reason, this study presents the effect of different heating rates in conjunction with a certain component stiffness. For that reason, SAW joints of 13CrMoV9-10 steel were investigated under FS and defined external restraint condition.
A systematic, nature-inspired chemical engineering approach is employed to solve the issue of flooding in electrochemical devices. The mechanism of passive water transport utilized by lizards living in arid environments is leveraged to design flow-fields with a microchannel structure on their surface, through which capillary pressure rapidly removes the water generated in the electrochemical device. This water management strategy is implemented in proton exchange membrane fuel cells (PEMFCs) with a lunginspired flow-field, which ensures uniform distribution of reactants across the catalyst layer. Jointly, this nature-inspired approach results in flood-free, stable operation at 100% RH and a B60% increase in current (B1.9 A cm-2) and peak power density (B650 mW cm−2) compared to current PEMFCs with a flood-prone, serpentine flow-field (B0.8 A cm-2 and 280 mW cm-2, respectively). This significant advance allows for PEMFC operation at fully humidified conditions.
Distributed fiber optic sensors for structural health monitoring of composite pressure vessels
(2024)
In diesem Beitrag geben wir einen umfassenden Überblick über unsere Forschung auf dem Gebiet der verteilten faseroptischen Sensorik für die strukturelle Zustandsüberwachung von Wasserstoffdruckbehältern aus Verbundwerkstoffen. Insbesondere zeigen wir, wie die Integration von faseroptischen Sensoren in Druckbehälter aus Verbundwerkstoffen die Sicherheit erhöht und gleichzeitig die Wartungskosten senkt. Die geringe Größe von Lichtwellenleitern ermöglicht ihre Integration in Verbundwerkstoffstrukturen während des Herstellungsprozesses, wodurch eine kontinuierliche Überwachung sowie eine präzise Erkennung und Lokalisierung von Strukturschäden während des Betriebs der Druckbehälter ermöglicht wird. Wir erörtern auch das Potenzial modernster Signalverarbeitungsmethoden und des maschinellen Lernens für die Weiterentwicklung der vorausschauenden Instandhaltung. Die von uns vorgestellten Anwendungen von faseroptischen Sensoren zeigen, dass sie einen wichtigen Beitrag zur Energiewende hin zu erneuerbaren Energien leisten können.
Der Wasserstofftransport auf der Straße ist wichtig und wird wie der noch geringe Transport auf der Schiene weiter stark zunehmen. Die bisherige Effizienzsteigerungen sind über Werkstoff- und Designänderungen vom Vollstahl über umfangsumwickelte Stahl- bis zu Compositespeichern mit Kunststofflinern erfolgt.
Hinzu kam die auf Basis der BAM-GGR 022 an Vorbedingungen geknüpfte Prüffristverlängerung von 5 auf 10 Jahre. Die wiederkehrende Prüfung von großen Transporteinheiten bedeutet jedes Mal einen Stillstand von gut 8 Wochen. Entsprechend steht mit Blick auf die weitere Effizienzsteigerung die Reduktion des Prüfaufwands im Fokus.
Eine Effizienzsteigerung kann nach aktueller Rechtslage geschehen, indem die hydraulische Prüfung auf eine Gasdruckprüfung umgestellt wird. Dies könnte zukünftig mit geeigneten Arbeitsschutzmaßnahmen pneumatisch durchgeführt werden – auch ohne Rechtsänderung.
Ein deutlich größerer Schritt in Richtung Verbesserung des Aufwands- zu Nutzenverhältnis ließe sich erreichen, indem die zerstörungsfreie Prüfung nicht mehr nur als Arbeitsschutz-motiviertes, begleitendes, sondern als zentrales Prüfverfahren ausgebaut wird. Gerade wenn – wie für die Schallemissionsanalyse erwartet – eine relativ gute Abschätzung des Berstdruckes möglich ist, könnte auf die 100%-Prüfung verzichtet werden und bis zu einem kritischen Alter nur auf Stichprobenprüfung basieren, was allerdings erhebliche Rechtsänderung erfordert und auch neue Werkezuge der Informationsverwaltung.
Als Vorlage für einen praktischen Ansatz zur Rechtsänderungen inkl. Informationsverwaltung wird auf die SV 674 in Verbindung mit 6.2.3.5.3ff ADR/RID verwiesen. Dies kombiniert mit einer digitalen Lebenslaufakte, die auf der digitalen Qualitätssicherung (QI-digital) beruht, wäre ein mächtiges Werkzeug für eine Verbesserung des Aufwands- zu Nutzenverhältnis und so auch eine Lösung des mit der stark steigenden Anzahl der Transporteinheiten absehbaren Kapazitätsproblems in der wiederkehrenden Prüfung.
Hydrogen has great potential on the path towards decarbonization of the energy and transport sectors and can mitigate the urgent issue of global warming. It can be sustainably produced through water electrolysis with potentially zero emissions, and efficiently used (e.g., in fuel cell systems). Despite its environmental advantages, hydrogen-metal interactions could result in the degradation of the mechanical properties of several structural materials. In order to determine the magnitude of the material degradation in relation to hydrogen exposure, extensive material testing is required. The standardized procedure for in-situ testing for the quantification of the impact of compressed gaseous hydrogen (CGH2) relies on the utilization of an autoclave around the tested specimen. Such test set-up is complex, expensive, time-consuming and requires special equipment, trained personnel, and strict safety procedures. A relatively recent method to circumvent these issues and provide affordable results consists of using hollow specimens, thus applying the hydrogen pressure inside rather than outside the specimen. It allows to reduce the volume of hydrogen by several orders of magnitude and to perform the tests more efficiently and in a safer manner. This study focuses on evaluating the tensile properties of X65 vintage pipeline steel tested in a high-pressure hydrogen environment using hollow specimens. Tests are performed in 6 MPa H2 and Ar at the nominal strain rate of 10−6 s−1 to evaluate the reduced area at fracture and the elongation loss. The effect of surface finishing on crack initiation and propagation is investigated by comparing two different manufacturing techniques. In this way, this study provides insights into the applicability of a novel, reliable, and safe testing method which can be used to assess the hydrogen-assisted ductility loss in metallic materials.
Bio-electrochemical CO2 conversion into organic products using precious-metal free electrocatalysts
(2024)
For the realization of a sustainable economy, it is of great importance to make use of CO2 for the production of multi-carbon organic chemicals used as feedstock in the chemical industry as well as carbon-neutral fuels (Varela et al. 2019). A promising approach is the electrochemical CO2 reduction followed by microbial conversion of the reduced products.
The hydrogen economy is one of the main solutions for achieving climate neutrality in Europe. Metallic materials, predominantly steels, are the most common structural materials in the various components along the hydrogen supply chain. Ensuring their sustainable and safe use in hydrogen technologies is a key factor in the ramp-up of the hydrogen economy. This requires extensive materials qualification, however, most of the accepted, and standardised test methods for determining the influence of gaseous hydrogen on metallic materials describe complex and costly procedures that are only available to a very limited extent worldwide (e.g., autoclave technique).
The hollow specimen technique is presented as an alternative method that can overcome the limitations of current techniques and complement them. To standardise the technique, a process has been initiated by ISO in 2021. Knowledge gaps for tests with the technique in hydrogen have been identified by DIN. The H2HohlZug project, which falls under the umbrella of TransHyDE, aims to address the identified knowledge gaps and provide a foundation for a comprehensive standardisation of the hollow specimen technique.