Chemische Charakterisierung und Spurenanalytik
Filtern
Dokumenttyp
- Zeitschriftenartikel (3)
- Vortrag (1)
Sprache
- Englisch (4)
Schlagworte
- Calibration (2)
- GD-OES (2)
- Fast flow GD (1)
- GD-MS (1)
- GDMS (1)
- Glow Discharge (1)
- Hot-pressing (1)
- Hydrogen (1)
- Li-ion battery (1)
- Matrix independent calibration (1)
- Non metals (1)
- Sputtering (1)
- Titanium hydride (1)
- Two-phase system (1)
- battery aging mechanism (1)
- current collector corrosion (1)
- depth profiles (1)
Organisationseinheit der BAM
- 1 Analytische Chemie; Referenzmaterialien (4)
- 1.6 Anorganische Referenzmaterialien (4)
- 1.1 Anorganische Spurenanalytik (1)
- 3 Gefahrgutumschließungen; Energiespeicher (1)
- 3.1 Sicherheit von Gefahrgutverpackungen und Batterien (1)
- 5 Werkstofftechnik (1)
- 5.1 Mikrostruktur Design und Degradation (1)
- S Qualitätsinfrastruktur (1)
- S.1 Qualität im Prüfwesen (1)
Eingeladener Vortrag
- nein (1)
In this work, we employed glow discharge optical emission spectrometry (GD-OES) depth profiling as a fast and semi-quantitative method to investigate the aluminum (Al) current collector degradation in commercial lithium cobalt oxide (LCO) pouch cells with no Al2O3 pretreatment. After battery aging, a heterogeneous deposit was found on the surface of the cathode. Gray hotspot areas within an extensive pale white region were formed. Consistent with energy dispersive X-ray (EDX) analysis of micro-cross sections milled via targeted focused ion beam (FIB), an Al-containing layer of approximately 3 µm can be observed using GD-OES. We attribute one main cause of this layer is the degradation of the Al current collector. The nonuniform growth of this layer was investigated by performing GD-OES depth profiling at different in-plane positions. We found that the gray area has a higher mass concentration of Al, probably in metallic form, whereas the white area was probably covered more homogeneously with Al2O3, resulting from the inhomogeneous distribution of the pitting positions on the current collector. Compared to FIB-EDX, GD-OES enables a faster and more convenient depth profile analysis, which allows the more productive characterization of lithium-ion batteries (LIBs), and consequently benefits the development of preferable battery materials.
Mixed copper and titanium hydride powder was hot-pressed and characterized by Carrier Gas Hot Extraction, XRay Diffraction, Thermal Gravimetric Analysis coupled with Mass Spectrometry, and Scanning Electron Microscopy.
The hot-pressed and five conventional samples were applied for calibration of hydrogen in Glow Discharge Optical Emission and Mass Spectrometry. Up to the introduction of 15 ng/s hydrogen the Emission yield model is useful in Glow Discharge Optical Emission Spectrometry. A correlation between saturation and even reversal of the emission yield of the spectral lines H121, H486 and H656 and low sputtering rates was found. Hydrogen effects exist for the spectral lines of Cu(II) 219 and Ti(I) 399. In Glow Discharge Mass Spectrometry, a linear dependency of the 1H ion current on the sputtered mass per time exists over the total range of hydrogen content investigated. Hydrogen effects also exist for the sensitivity of 48Ti and 63Cu. The sputtering rate of two-phase materials depends linearly on the sputtered mass per time of one phase, which allows the sputtering rate of two-phase materials with known composition to be predicted.
The performance of glow discharge mass spectrometry (GD-MS) is investigated for the accurate quantification of metallic impurities and oxygen in solid samples using the fast flow source GD-MS instrument ELEMENT GD.
Different quantification approaches based on relative and absolute sensitivity factors are evaluated for the determination of metallic impurities using three sample matrixes (Al, Cu and Zn). The effect of the discharge conditions (voltage, current, discharge gas pressure/flow) on the sensitivity is investigated and the parameters are optimized to favour matrix independent calibrations. Improved standard relative sensitivity factors (StdRSFs) are calculated under optimal conditions based on multi-matrix calibrations. The sputtering rate corrected calibration is also presented as a multi-matrix calibration approach.
The capabilities of GD-MS for oxygen determination are also investigated using a set of new conductive samples containing oxygen with mass fractions in the percent range in three different matrices (Al, Mg and Cu) produced by a sintering process. Poor limits of detection (in the order of g/kg) were obtained as consequence of the reduced sensitivity of oxygen in GD-MS and high oxygen background signal intensity as well as its variations. The absolute sensitivity procedure is shown as a matrix-independent approach, which provides quantitative values consistent with those obtained by carrier gas hot extraction (CGHE).
Analytical glow discharges with optical (GD-OES) and mass spectrometric (GD-MS) detection are able to obtain depth resolved information about the light elements hydrogen, carbon, nitrogen and oxygen in solid samples, where most of the other analytical techniques fail. However, the interpretation or even quantification of the measured signals is still very challenging. Problems arise due to physical effects (plasma processes such as the ‘Hydrogen effect’, the Doppler effect, self absorption or diffusion of hydrogen in the sample during sputtering) chemical effects(e.g. formation of compounds with argon or the matrix, poisoning of the sample or gettering) as well as instrumental difficulties (e.g. of the sensitivity, calibration and vacuum quality)..
The GD techniques are direct solid sampling methods and require reference materials for calibration. Unfortunately the list of available certified reference materials (CRM) suited for calibration of light elements in different matrix is relatively short Therefore, sintered materials doped with the analytes H2, O2 and N2 were produced at IFW Dresden and applied as calibration standards for hydrogen, oxygen and nitrogen. Due to the high analyte concentration added, it is very likely that the real concentration agree well with the added amount of light elements in the corresponding phases. The validation of the determination of the light element concentration in the sintered samples was possible in some cases only due to the lack of suitable techniques. This fact proves the need for the development of a reliable quantification of light elements by GDS.
A systematic dependence of the sputtering rate on the composition was found and can be explained by basic principles.
Using mixtures of TiH2 and ZrH2 with Cu the ratio of hydrogen and Cu lines has a good correlation with the corresponding concentration ratio. The hydrogen emission yield however decreases over 0.3 m% hydrogen and finally the hydrogen intensity may even decrease. This behaviour can be explained by a very similar quenching of the hydrogen and copper intensity caused by the hydrogen effect. First experiments with GD-MS show no saturation of the hydrogen ion current and thus confirm the quenching of the emission yield in GD-OES.
Sintered material for the oxygen calibration (Al2O3, CuO, Cu2O and MgO mixed with Cu, Al and Mg) confirmed the blue line shift effect at O I 130.22 nm, first time reported by Köster 2009 [1]. The effect is more pronounced at Mg than in Al and Cu, which due to line interference leads to a matrix dependent EY. This effect is negligible at O I 777.19 nm and the EY is matrix independent. Using GD-MS first promising results for the calibration of oxygen with these sintered samples could be obtained, when the sputtering rate was included in the evaluation.
More recently also sintered material for nitrogen calibration (AlN mixed with Al and Si3N4 mixed with Cu) was produced and points to a matrix independent emission yield of nitrogen