- nein (46)
Porous materials play an important role in several fields of technology, especially for energy applications like photovoltaics, electrolysis or batteries. The activity of porous films is affected by properties like porosity, film thickness, chemical composition of the material as well as the crystallinity of the framework. The complex morphology of such porous films constitutes a challenge even for modern analytical techniques and requires new approaches employing the combination/complementation of data of different analytical methods. In this contribution we characterize thin mesoporous iridium-titanium mixed oxide film properties by Electron Probe Microanalysis (EPMA) with energy dispersive X-ray spectroscopy (EDS) at an SEM.
Porous materials play an important role in several fields of technology, especially for energy applications like photovoltaics, electrolysis or batteries. The activity of porous films is affected by properties like porosity, film thickness, chemical composition of the material as well as the crystallinity of the framework. The complex morphology of such porous films constitutes a challenge even for modern analytical techniques and requires new approaches employing the combination/complementation of data of different analytical methods. In this contribution we characterize thin mesoporous iridium-titanium mixed oxide film properties by Electron Probe Microanalysis (EPMA) with energy dispersive X-ray spectroscopy (EDS) at an SEM.
Porous materials play an important role in several fields of technology, especially for energy applications like photovoltaics, electrolysis or batteries. The activity of porous films is affected by properties like porosity, film thickness, chemical composition of the material as well as the crystallinity of the framework. The complex morphology of such porous films constitutes a challenge for modern analytical techniques and requires approaches employing the combination/complementation of data of different analytical methods. In this contribution we characterize thin mesoporous iridium-titanium mixed oxide film properties by spectroscopic ellipsometry (SE).
Mesoporous iridium oxide - titanium oxide (IrOx-TiOx) films were prepared via dip-coating of a solution containing a triblock-copolymer as structure-directing agent, an iridium precursor as well as a titanium precursor in ethanol. Deposited films with different amounts of iridium (0 wt%Ir to 100 wt%Ir) were synthesized and calcined in air. The thin films were analyzed with SE using the Bruggeman effective medium approximation (BEMA) for modelling. The results were compared with electron probe microanalysis (EPMA) as part of a combined SEM/EDS/STRATAGem Analysis.
Outline
- maging ellipsometry: oncept and setup
- Basic theory: ellipsometry on tilted/curved surfaces
- Geometric considerations
- Tilt-induced cross-polarization
- Application: coating analysis on microlensarray
- Mueller-Matrix Imaging
- Conversion to Delta-Psi Image
- Layer-thickness of ITO coating
Ellipsometry has become a powerful measurement tool in semiconductor industry since the sixties of the last century.
Early standardization activities focused exclusively on SiO2/Si (ASTM F 576-01, SEMI 3624). The first generic standard dealing with ellipsometry is DIN 50989-1:2018 Ellipsometry – Part 1: Principles. Standardization is a prerequisite for accreditation according to DIN EN ISO/IEC 17025 and the evaluation of uncertainty budgets.
In the last years, the implementation of imaging ellipsometry in the variety of optical characterization techniques has shown tremendous potential to analyze the topology of surfaces in the lateral dimension. In the later studies, this contrast-rich surface images were affiliated with changes of the refraction indices, Absorption bands or layer thicknesses. However, it was realized that additional factors like curvature or scattering can have a great Impact on the ellipsometric readout of the analyzed system. In this study, we focus on the systematic evaluation of structural anomalies and inhomogenities of several Basic systems. This includes spherical particles as a model for microscopic curved surfaces in a range of 0.25 to 25 μm in diameter. In the macroscopic regime several conventional convex lenses were analyzed. Additional affords were made to generate microscopic concave model systems by applying nanoindentation with a spherical indentation unit. With this method calottes with a depth of 0.04 to 2 μm and radius of 2.5 μm were made. The macroscopic counterpart is delivered by conventional concave lens systems. For all systems, a variety of different bulk materials was investigated. This includes metal oxides, metals and polymers as well as combinations of each by applying coatings on the bulk materials with different layer thicknesses.
To analyze these structural anomalies and inhomogenities properly, Mueller-Matrix imaging ellipsometry is the method of choice to address cross- and depolarization effects that occur due to the curved surfaces.
Supplementary methods were used for an independent characterization of the topological properties of all structural anomalies and inhomogenities. This includes AFM and SEM for the microscopic samples (microparticles and nanoindented holes) and white light interferometry for the macroscopic lenses.
This study results in a systematic screening of different coated and uncoated material systems with a topology that does not fit into conventional ellipsometry and thus is analyzed by Muller-Matrix imaging ellipsometry. This will help in quality control and is a contribution to the understanding of the polarizing effects of non-ideal Systems analyzed by ellipsometry.
Up until several years ago, tensile and compressive tests have been exclusively carried out as single-sample tests within a tensile, hardness or universal testing machine. The availability of centrifuge technology changed this situation in 2013 in several ways because centrifugal force is used as testing force within a rotational reference frame.
Firstly, multiple-sample strength testing became feasible for both tensile load condi-tions, e.g. determination of composite, bonding or adhesive strength, and compressive load conditions, e.g. hardness, compressibility and compactibility. Secondly, there is no need for a two-sided sample clamping and double-cardanic suspensions as samples are simply inserted using a one-sided sample support. Thirdly, shear forces can be avoided by means of guiding sleeves which steer test stamps acting as mass bodies for either tensile or compressive testing. Fourthly, up to eight samples can be tested under identical conditions within a very short period of time, typically within 15 minutes including sample loading and unloading. Hence, either a reliable statistics (of identical samples) or a ranking (of different samples) can be derived from one test run.
The bench-top test system is described in detail and demonstrated that centrifugal force acts as testing force in an appropriate way because Euler and Coriolis force do not affect the testing results. Examples for both tensile strength testing, i.e. bonding strength of adhesives-bonded joints and adhesive strength of coatings, and compres-sive strength testing, i.e. Vickers-, Brinell- and ball indentation hardness and deter-mination of spring constants, are presented, discussed and compared with conven-tional tests within tensile, hardness or universal testing machines.
At present, a maximum testing force of 6.5 kN can be realized which results at test stamp diameters of 5 mm, 7 mm, and 10 mm in tensile or compressive stress values of 80 MPa, 160 MPa, and 320 MPa. For tensile strength, this is already beyond bonding strength of cold- and warm-curing adhesives. Moreover, centrifuge technology is compliant to standards such as EN 15870, EN ISO 4624, EN ISO 6506/6507 and VDI/VDE 2616. Programmable test cycles allow both short-term stress and log-term fatigue tests. Based on a variety of examples of surface and bonding technology, applications in both fields R&D and QC are presented. Meanwhile, centrifuge technology is also accredited according to DIN EN ISO/IEC 17025.
Some critical discussion of the state of the art of uncertainty evaluationin Instrumented Indentation Testing IIT
Nowadays the Instrumented Indentation Testing (IIT), in the nano range often named as nano indention, is one of the most commonly used methods to determine the mechanical properties of materials in the micro and nano range. This method is already extensive standardized in ISO 14577 part 1-4. In the past, the application of this standard in testing praxis shows that the established values have an excellent precision.If an uncertainty is calculated, the range of values within which the true value is asserted to lie with some level of confidencewill be known. In part 1 of ISO 14577 [1] two methods for evaluation of the uncertainty in IIT are mentioned:
Method 1 for determining uncertainty considers only those uncertainties associated with the overall measurement performance of the testing machine with respect to the reference blocks.
Method 2calculates a combined uncertainty from individual contributions. These may be grouped into random and systematic uncertainties.
Both methods will be described in detail using examples from the dailyexperimental praxis. The comparabilityof both methods will be critically discussed. Finally, it will be showedhow the calculated uncertaintiescan be used for performancetests and product specifications.
Acknowledgement
This work was performed under the support of the EMPIR project 17NRM05Advancing measurement uncertainty̶ comprehensiveexamples for key international standards
References
[1] ISO 14577 part 1 (2017)
Porous materials play an important role in several fields of technology, especially for energy applications like photovoltaics, electrolysis or batteries. The activity of porous films is affected by properties like porosity, film thickness, chemical composition of the material, as well as the crystallinity of the framework. The complex morphology of such porous films constitutes a challenge even for modern analytical techniques and requires new approaches employing the combination/complementation of data of different analytical methods. In this contribution, we characterise thin mesoporous iridium-titanium mixed oxide film properties by electron probe microanalysis (EPMA) with energy-dispersive X-ray spectroscopy (EDS) at an SEM.
Mesoporous iridium oxide - titanium oxide (IrOx-TiOx) films were prepared via dip-coating of a solution containing a triblock-copolymer as structure-directing agent, an iridium precursor as well as a titanium precursor in ethanol. IrOx-TiOx films were synthesized with different amounts of iridium and calcined in air. The SEM micrographs reveal for all films the achievement of a well-ordered mesoporous structure and homogeneous films with thicknesses between 67 nm and 152 nm.
For the determination of film elemental composition and porosity, EPMA can be used as part of a combined SEM/EDS/STRATAGem analysis. Elemental compositions and mass depositions (in μg cm-2) of IrOx-TiOx films were calculated with the thin film analysis Software STRATAGem via k-values measured with SEM/EDS. Pure bulk Ir, TiO2 and Si were measured as references. The average density of the films was obtained from the mass Deposition and the film thickness as measured by cross-section SEM. The porosity was then extracted from the measured average film density divided by a theoretical bulk density. The latter is calculated from the weight fractions of IrOx and TiOx as determined with STRATAGem and the bulk mass densities of IrO2 and TiO2 (rutil) from literature.
The fitting results of the k-values from the STRATAGem software, which are in fair agreement with the measured k-values.
The application of the SEM/EDS/STRATAGem approach for accurate porosity determination on pure mesoporous TiOx films and pure porous IrOx films has been recently demonstrated.
The porosities of pure IrOx, TiOx and mixed IrOx-TiOx films in this study have been determined. The contribution will assess in detail the advantages and limitations of the combined SEM/EDS/STRATAGem analysis for the morphology and porosity of thin metal oxide films. Moreover, the comparison with other measurement techniques and the combination of datasets from multiple measurements will be discussed.
In well-annealed thin polymer films, with non-repulsive polymer/substrate interactions, an irreversibly adsorbed layer is formed. These adsorbed layers have shown enormous potential for technological applications. The growth kinetics and molecular dynamics of these buried layers in thin films are still not fully investigated due to the hard accessibility. Here, the irreversibly adsorbed layers of homopolymer thin films are revealed by solvent-leaching experiments. The growth kinetics of these layers is investigated as a function of original film thickness and annealing times. The thickness, topography and quality of the adsorbed layer is determined with Atomic Force Microscopy (AFM) and spectroscopic ellipsometry. Additionally, the molecular mobility of the adsorbed layer is investigated with Broadband Dielectric Spectroscopy (BDS). A recently developed nanostructured capacitor (NSC) is employed to measure the adsorbed layers with a free surface layer depending on annealing and solvent-leaching time. The results are quantitatively compared and discussed with respect to recently published work.