Systematic errors in the evaluation of uncorrected data from thermographic lock-in measurements
(2018)
Lock-in thermography (LT) is based on the correct evaluation of phase differences between the temperature oscillations at different surface regions of the object under test during periodic heating. Since the usual heating procedures contain a DC component, the actual heating pattern achieved is not harmonic. This causes systematic deviations when phase differences are determined by means of harmonic analysis, e.g. with FFT analysis. The resulting errors depend clearly on the ratio between DC and AC amplitude, which is demonstrated at simulated and experimentally recorded temperature transients. Further experimental LT data obtained by different oscillating energy inputs showed a variety of possible shapes of transients with different DC components.
Impact damages and delaminations in fibre-reinforced composites (FRC) might not be visible at the surface, but could have an influence on the resistance and on the long-term behaviour of the component. Therefore, and especially for safety relevant structures, non-destructive methods are required for the assessment of such damages.
Active thermography methods are suitable to characterize damages after loading using different kind of excitation techniques and various configurations of infrared (IR) camera and heating sources. Here, flash lamps, impulse excitation with infrared radiator and lock-in technique with halogen lamps or widened laser beams are suited. In addition, non-optical sources like sonotrodes (requiring direct contact to the structure) or induction generators (only suited for carbon fibre reinforced polymer (CFRP) structures) could be applied as well. For the investigation of the evolution of the damage during the impact, passive thermography can be applied in-situ. Elastic and plastic deformations alter the temperature of the structure and thus the temperature on the surface.
In this contribution, at first the general principles of quantitative defect characterisation in FRC using active thermography with flash, impulse and lock-in excitation are described. Optical and thermal properties of the FRC material and its anisotropy are considered. Results of phase differences obtained at flat bottom holes with flash and lock-in thermography are compared for qualifying both methods for quantitative defect characterization. Secondly, the damage evolution of CFRP and GFRP structures under impact load and static tensile loading is described. The spatial and temporal evolution of the surface temperature enables us to distinguish matrix cracks or fibre-matrix separation from delaminations between the layers. Afterwards, all results for loading defects, obtained by passive and active thermography, are compared with each other. Fig. 1 and 2 show the difference of passive and flash thermography obtained at impact and tensile loaded CFRP plates, respectively. As one purpose of these investigations is the development of standards within national (DIN) and European (CEN) standardisation bodies, new draft and final standards are presented and further needs are discussed at the end of the presentation.
In vielen Umgebungen, besonders bei hohen Temperaturen, korrosiven Umgebungen oder auf bewegten oder schlecht zugänglichen Flächen, kann die Temperatur nicht oder nur mit nicht akzeptablem Aufwand mit Berührungsthermometern gemessen werden. Diese Umgebungsbedingungen sind unter anderem in der chemischen Industrie, der Lebensmittel-, Metall-, Glas-, Kunststoff- und Papierherstellung sowie bei der Lacktrocknung anzutreffen. In diesen Bereichen kommen Strahlungsthermometer zum Einsatz. Der VDI-Statusreport zeigt typische Anwendungsfelder von nicht radiometrisch kalibrierten Wärmebildkameras und von radiometrisch kalibrierten Thermografiekameras. Um verlässlich mit spezifizierten Messunsicherheiten berührungslos Temperaturen zu messen, müssen die Strahlungsthermometer und Thermografiekameras nicht nur kalibriert, sondern radiometrisch und strahlungsthermometrisch umfassend charakterisiert werden. Auch die optische Materialeigenschaft, der spektrale Emissionsgrad und die Gesamtstrahlungsbilanz (Strahlung des Messobjekts und der Umgebung) sind bei der industriellen Temperaturmessung von großer Bedeutung. In den letzten Jahrzehnten ist dazu ein umfassendes technisches Regelwerk entstanden, das wir Ihnen mit diesem VDI-Statusreport vorstellen. Manche in den Richtlinien beschriebenen Kennwerte mögen abstrakt wirken. In diesem Statusreport zeigen wir an konkreten Beispielen, was diese Kenngrößen für die berührungslose Temperaturmessung bedeuten. Beispiele von Anwendungen zeigen, wo temperaturmessende Thermografiekameras und ausschließlich bildgebende Wärmebildkameras in der Praxis eingesetzt werden. Mit einer Analyse, welche Themen und Anwendungen derzeit besonders intensiv diskutiert werden, versuchen wir Trends für zukünftige Entwicklungen herauszuarbeiten.