In-situ observation of sub-critical crack growth in water bearing borate glasses
- 185 cracks were initiated in a soda-lime-silica glass by Vickers indentation and grown under controlled dry nitrogen atmosphere. Direct observation of subcritical crack growth (SCCG) upon indentation was performed using a video camera with an image acquisition rate of 3 ms. The results show that the validity of K(c) relations used to determine the indentation fracture toughness from a single imprint is questionable. It seems that correlation of crack length to stress intensity necessitate the use of statistical significant data of multiple crack events.
| Autor*innen: | P. Kiefer |
|---|---|
| Koautor*innen: | R. Balzer, H. Behrens, Stefan ReinschORCiD, Ralf MüllerORCiD, J. Deubener |
| Dokumenttyp: | Vortrag |
| Veröffentlichungsform: | Präsentation |
| Sprache: | Englisch |
| Jahr der Erstveröffentlichung: | 2017 |
| DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
| Freie Schlagwörter: | Glass; Indentation fracture toughness; Sub critical crack growth; Vickers; Water bearing glass |
| Veranstaltung: | FFAG 7: 7th International Workshop on Flow and Fracture of Advanced Glasses |
| Veranstaltungsort: | Aalborg, Denmark |
| Beginndatum der Veranstaltung: | 02.07.2017 |
| Enddatum der Veranstaltung: | 05.07.2017 |
| Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
| Datum der Freischaltung: | 22.02.2018 |
| Referierte Publikation: | Nein |
| Eingeladener Vortrag (wissenschaftliche Konferenzen): | Nein |