Effects of fatigue loading and alkali-silica reaction on the mechanical behaviour of pavement concrete
- The primary aim of this paper is to analyze the impact of mechanical pre-damage and alkali–silica reaction (ASR) on the fracture mechanical properties of pavement concrete. For this purpose, a four point bending test was applied to large format beams to produce a defined level of cyclic pre-damage. The fatigue-induced concrete degradation process was simultaneously recorded using a testing procedure specifically developed for the purpose. In addition, fatigue-induced cracks on extracted drilling cores were spatially visualized and quantified using micro X-ray 3D-computed tomography (3D-CT). The storage of the small-format test specimens, with and without cyclic pre-damage, in an ASR-conducive environment showed that pre-damage leads to an increase in ASR damage processes. Subsequent structural mechanical investigations on small format specimens with and without pre-damage show that fatigue loading and ASR significantly influence fracture mechanical parameters of the concrete.
Autor*innen: | A. Wiedmann, Frank WeiseORCiD, E. Kotan, H. S. Müller, Birgit MengORCiD |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Structural Concrete |
Jahr der Erstveröffentlichung: | 2017 |
Verlag: | Ernst & Sohn |
Jahrgang/Band: | 18 |
Ausgabe/Heft: | 4 |
Erste Seite: | 539 |
Letzte Seite: | 549 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurbau | |
Freie Schlagwörter: | Acoustic emissions analysis; Alkali-silica reaction; Concrete pavement; Fatigue loading; Fracture energy; Monitoring of damage; Tensile strength; Ultrasonic velocity |
DOI: | 10.1002/suco.201600179 |
ISSN: | 1751-7648 |
ISSN: | 1464-4177 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 24.07.2017 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 07.09.2017 |