Microstructure and diffusion coefficient of an old corrosion product layer and impact on steel rebar corrosion in carbonated concrete
- Corrosion is the major degradation pathway affecting reinforced concrete structures. In the long-term, the rust layer might become thick and slow down the diffusion of oxygen from the atmosphere to the steel. With this in mind, the mineralogy, microstructure and diffusion properties of an old and thick corrosion product layer were investigated. Despite the presence of macropores, the gas diffusion coefficient was found to be low. The impact of the layer on the oxygen diffusion was evaluated using Fick’s law. The results showed that the layer could reduce the flux of oxygen only in a specific configuration.
Autor*innen: | S. Poyet, W. Dridi, V. L'Hostis, Dietmar Meinel |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Corrosion Science |
Jahr der Erstveröffentlichung: | 2017 |
Verlag: | Elsevier B.V. |
Verlagsort: | Radarweg 29, 1043 NX Amsterdam, The Netherlands |
Jahrgang/Band: | 2017 |
Ausgabe/Heft: | 125 |
Erste Seite: | 48 |
Letzte Seite: | 58 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Micro-CT; Rust; Steel reinforced concrete; X-ray computed tomography |
DOI: | 10.1016/j.corsci.2017.06.002 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 31.08.2017 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 31.08.2017 |