Corrosion of galvanized reinforcement in carbonated concrete

  • Corrosion of galvanized steel in carbonated concrete is different from the corrosion of reinforcement made of carbon steel. This is based on the corrosion mechanism of galvanized steel in dependence of the pH-value of carbonated concrete. To describe the influence of a lower pHvalue on the corrosion activity of galvanized reinforcement, different electrochemical measurements were made. The anodic and cathodic partial reaction were investigated by galvanostatic pulse measurements and potentiodynamic measurements. Especially the galvanostatic pulse measurements can describe the influence of the lower pH-value by the anodic polarization resistance with pt = 20 sec. (polarization time). Additionally, corrosion current measurements were performed, coupled with potential measurements, between galvanized steel in carbonated and non-carbonated concrete. Normally, the potential measurements are an indicator to localize the anodic and cathodic parts of a macro system. In this case the cathodeCorrosion of galvanized steel in carbonated concrete is different from the corrosion of reinforcement made of carbon steel. This is based on the corrosion mechanism of galvanized steel in dependence of the pH-value of carbonated concrete. To describe the influence of a lower pHvalue on the corrosion activity of galvanized reinforcement, different electrochemical measurements were made. The anodic and cathodic partial reaction were investigated by galvanostatic pulse measurements and potentiodynamic measurements. Especially the galvanostatic pulse measurements can describe the influence of the lower pH-value by the anodic polarization resistance with pt = 20 sec. (polarization time). Additionally, corrosion current measurements were performed, coupled with potential measurements, between galvanized steel in carbonated and non-carbonated concrete. Normally, the potential measurements are an indicator to localize the anodic and cathodic parts of a macro system. In this case the cathode was more negative than the anode before they were coupled. After the coupling of the two specimens the mixed potential was much more positive than the single potential of the galvanized steel in carbonated concrete. It increased up to the potential range of the non-carbonated specimens. This means that in case of carbonated outer areas, the embedded galvanized steel forms the cathodic part of a macro element.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • Ebell_et_al - Corrosion of galvanized reinforcement in carbonated concrete.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Gino EbellORCiD
Koautor*innen:Andreas Burkert, Jürgen Mietz
Dokumenttyp:Vortrag
Veröffentlichungsform:Präsentation
Sprache:Englisch
Jahr der Erstveröffentlichung:2016
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurbau
Freie Schlagwörter:Concrete; Corrosion; Galvanized; Rebar
Veranstaltung:Eurocorr 2016
Veranstaltungsort:Montpellier, France
Beginndatum der Veranstaltung:11.09.2016
Enddatum der Veranstaltung:16.09.2016
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:21.09.2016
Referierte Publikation:Nein
Eingeladener Vortrag:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.