Thermomechanical fatigue of heat-resistant austenitic cast iron EN-GJSA-XNiSiCr35-5-2 (Ni-Resist D-5S)

  • TMF tests were carried out on EN-GJSA-XNiSiCr35-5-2 at constant minimum temperature (400 °C) and varying maximum temperatures (Tmax = 700 °C, 800 °C, 900 °C) with hold times of 180 s at Tmax and two phase angles (in-phase (IP), 180° out-of-phase (OP)). The results showed a comparable strength under OP- and IP-TMF loading. At Tmax = 700 °C and 900 °C, the lifetime in IP-tests was slightly longer than that of OP-tests, while it is vice versa at Tmax = 800 °C. The IP-tests at Tmax = 900 °C showed a similar lifetime as OP-tests at Tmax = 700 °C and 800 °C, which was unexpected for such a high testing temperature. All IP-tests at Tmax = 900 °C showed a continuous cyclic softening from the beginning on, which was different from all other testing conditions. Complementary metallographic investigations indicated that under this test condition, intergranular creep damage is present in the volume of the test pieces.

Volltext Dateien herunterladen

  • Int_J_Fatigue_99_2017_295.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Hans-Joachim Kühn, Birgit Rehmer, Birgit SkrotzkiORCiD
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):International journal of fatigue
Jahr der Erstveröffentlichung:2017
Verlag:Elsevier
Verlagsort:Oxford
Jahrgang/Band:99
Ausgabe/Heft:2 (Special issue: Recent developments in thermo-mechanical fatigue)
Erste Seite:295
Letzte Seite:302
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:Cast iron; Cracks; Cyclic softening; Microscopy; Thermomechanical fatigue
Veranstaltung:3rd International Workshop on Thermo-Mechanical Fatigue (TMF-Workshop 2016)
Veranstaltungsort:Berlin, Germany
Beginndatum der Veranstaltung:27.04.2016
Enddatum der Veranstaltung:29.04.2016
DOI:10.1016/j.ijfatigue.2017.01.009
ISSN:0142-1123
ISSN:1879-3452
Zugehöriger Identifikator:https://opus4.kobv.de/opus4-bam/frontdoor/index/index/docId/40867
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:06.04.2017
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:29.05.2017
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.