First results regarding the realisation of multi-material components manufactured by Laser Beam Melting of polymers and metals are published. For realising composite structures from polymer powders by additive manufacturing, at first relevant material properties regarding compatibility have to be analysed. The paper shows the main requirements for compatibility between different materials and offers first results in form of a compatibility matrix of possible combinations for composite structures.For achieving gradient properties of additively manufactured metal parts by using composite materials the composition of alloying components in the powder and adapted process strategies are varied. As an alternative to atomizing pre-alloyed materials, mixtures of different powders are investigated.
By using Additive Manufacturing technologies, like Laser Beam Melting (LBM) of polymers, parts can be realized within single days and necessary modifications can be quickly adapted. With increasing complexity, products are often made out of different polymer materials and the need for multi-material parts is an increasing industry requirement, which cannot be fulfilled by the single material parts realizable by LBM. Therefore, Simultaneous Laser Beam Melting (SLBM) as a new Additive Manufacturing technology offers the possibility to build parts consisting of different polymer materials. The realizable parts combine different material properties, like differing stiffness or chemical resistances, within a single part. Up to now, different materials are deposited next to each other on the building platform, thus the boundary surface between the different polymers is orientated perpendicular to the building direction. For this paper, the polymer powders are alternated in building direction. Thus, the boundary surface is orientated horizontally and is larger, both influencing the boundary surface and resulting part properties, which are analyzed by a high-resolution thermal imaging system and by cross sections.
By Laser Beam Melting of polymers (LBM), parts with almost any geometry can be built directly out of CAD files without the need for additional tools. Thus, prototypes or parts in small series production can be generated within short times. Up to now, no multi-material parts have been built by LBM, which is a major limitation of the technology. To realize multi-material parts, new mechanisms for depositing different polymer powders as well as a new irradiation strategy are needed, by which polymers with different melting temperatures can be warmed to their specific preheating temperatures and be molten simultaneously. This is achieved by simultaneous laser beam melting (SLBM). In the process, two different materials are deposited next to each other and preheated a few degrees below their melting temperatures by infrared emitters and laser radiation (λ = 10.60 µm), before in the last step the two preheated powders are molten simultaneously by an additional laser (λ = 1.94 µm). So far, multi-material tensile bars have been realized and analyzed regarding their boundary zone between both materials. The experiments showed that the temperature gradients in the boundary zone and along the building direction seem to be of great importance for the process stability and the resulting part properties. Therefore, a detailed analysis of the occurring temperature gradients during the process is needed to identify adequate process adjustments regarding the temperature controlling. To analyze the temperature gradients, thermocouples positioned inside the powder bed are used. By varying the temperature of the building platform, the influence of different temperature gradients on the resulting part properties is shown.
In the paper first results regarding the realisation of gradient and multi-material parts manufactured by Laser Beam Melting in powder bed of metals and polymers are published. Gradient properties of additively manufactured metal parts can be achieved by varying the composition of alloying components in the powder and adapting process strategies. As an alternative to atomizing pre-alloyed materials, mixtures of different powders are investigated. For realizing multi-material-parts from polymers, at first relevant material properties concerning compatibility have to be analysed. Therefore the paper shows the main requirements for compatibility between different materials and also first results regarding the compatibility of polymer powders and possible combinations for the manufacturing of multi-material components by laser beam melting of polymers.
Simultaneous laser beam melting (SLBM) allows the direct realization of multi-material components consisting of different polymer materials by a single Additive Manufacturing (AM) process. To achieve a high compound strength between different materials by adhesive bonding, a common boundary zone based on diffusion of the macromolecules is necessary and thus, both materials needs to be compatible regarding their specific adhesion compatibility. However, by SLBM also incompatible polymers can be processed to multi-material parts. If two incompatible polymers are processed, a positive locking between the different materials is necessary to achieve a connection between the materials. The positive locking results of a random mixture process of the different powder materials during the powder deposition process by a two chamber recoater system, which leads to the forming of undercuts of one material in the other during the melting and recrystallization. In this paper, thermoplastic elastomer (TPE) and polypropylene (PP) powders, which are incompatible, are processed to multi-material specimens. By qualifying basic material properties, their influence on the process and especially on the forming of undercuts in the boundary zone is analyzed. To also allow the analysis of the influence of both material and process parameters on the resulting part properties, tensile test specimens are built and their tensile strength is determined. Additionally, cross sections of the boundary zone are prepared and analyzed by microscope images.
By simultaneous laser beam melting (SLBM), parts consisting of different polymer powders can be additively manufactured within one building process. Besides the advantages of conventional LBM, e.g., not needing additional tools and being able to realize parts with almost any geometry, different product requirements can be achieved within a single part. Product requirements may be different chemical resistances or haptic material properties. Therefore, SLBM enlarges the application field for additive manufacturing in general. In the process, two different materials are deposited on the building platform and preheated a few degrees below the melting temperature of the lower melting polymer by infrared emitters. Afterward, a CO2 laser (λ = 10.6 μm) provides the energy for the temperature difference between the preheating temperatures of both materials. Finally, a digital light processing chip is used to achieve simultaneous and flexible energy deposition for melting both preheated polymers. By illuminating the chip with a laser, parts of the beam can be flexibly guided onto the powder bed or into a beam trap. As laser, a single mode thulium laser (λ = 1.94 μm) is used. After melting the layer, a new layer is deposited and the process starts anew. In this paper, polypropylene and polyamide 12 are used as materials. After analyzing the material and melting behavior during the process by a high-resolution thermal imaging system, the parts are qualified regarding their material compatibility at the boundary zone and porosity by cross sections.
Abstract — In this report, the dry delivery of polyamide 12 (PA 12) powder for the preparation of powder layers in laser beam melting (LBM) is investigated. Therefore, an experimental setup was built which consists of a glass nozzle assembled on a piezo-electric actuator. By applying a sinusoidal voltage signal to the actuator, the nozzle is set into vibration mode which enhances the powder delivery through the nozzle. By using this effect, powder mass flow is controlled and a valve-like start and stop function is realized. In order to identify suitable process parameters, a broad range of vibration modes were investigated using two nozzles made from glass with different orifice diameters. Therefore, the vibration frequency and the voltage signal of the actuator were varied and the resulting mass flow was detected by a balance. It was found that both the frequency and the voltage signal affect the mass flow and its stability but with different impact. Moreover, powder lines were deposited with different velocities in order to characterize the setup regarding applicability for highly selective powder deposition for LBM.
Powder based Additive Manufacturing technologies offer huge potential for building parts with almost no geometrical restrictions, but both the process controlling as well as the part properties are strongly dependent on different material characteristics of the material, like the flowability. In this work, different weight percentages of nano-scaled silica dioxide particles (Aerosil®) are admixed to pure polyethylene and polypropylene powder and the resulting flowability is determined. Besides using the Hausner ratio as standardized value, the degree of coverage is introduced as a new characteristic to quantify the powder flowability. The degrees of coverage are compared to the Hausner ratios to allow a discussion and evaluation about the different characteristic values. Additionally, tensile bars consisting of polypropylene are generated to determine the porosity by cross sections and the mechanical part properties by tensile testing. As mechanical part properties, the tensile strength and elongation at break are determined and the effects of different powder flowability on these properties are analyzed.
In this paper, first results regarding the realization of multi-material parts by Simultaneous Laser Beam Melting (SLBM) of polymers are presented. This new approach allows the layerwise generation of parts consisting of different polymer materials within one building process. Besides the typical advantages of additive manufacturing technologies, such parts can fulfill different product requirements concomitant and therefore could enlarge the overall field of application. The powder materials used for this paper are polyethylene (PE) and a polyamide based thermoplastic elastomer (TPE). After depositing the powder materials next to each other, infrared-emitters heat the lower melting polymer and a CO2 laser provides the preheating temperature of the higher melting polymer. In the last step, a thulium fibre laser melts the two preheated powders simultaneously. The realized specimens are characterized by cross sections and their tensile strengths are determined. Additionally, the new approach of the simultaneous energy irradiation is investigated using a Finite Element Analysis in order to gain a more profound process understanding. In that sense, the influence of the size of the exposure area on the reachable maximum temperatures inside that area was analyzed by the simulation and compared to experimental studies.
In this paper, first results regarding the realization of multi-material parts by Simultaneous Laser Beam Melting (SLBM) of polymers are presented. This new approach allows the layerwise generation of parts consisting of different polymer materials within one building process. Besides the typical advantages of additive manufacturing technologies, such parts can fulfill different product requirements concomitant and therefore could enlarge the overall field of application. The powder materials used for this paper are polyethylene (PE) and a polyamide based thermoplastic elastomer (TPE). After depositing the powder materials next to each other, infrared-emitters heat the lower melting polymer and a CO2 laser provides the preheating temperature of the higher melting polymer. In the last step, a thulium fibre laser melts the two preheated powders simultaneously.The realized specimens are characterized by cross sections and their tensile strengths are determined. Additionally, the new approach of the simultaneous energy irradiation is investigated using a Finite Element Analysis in order to gain a more profound process understanding. In that sense, the influence of the size of the
exposure area on the reachable maximum temperatures inside that area was analyzed by the simulation and compared to experimental studies.