Circumventing boundary effects while characterizing epoxy/copper interphases using nanoindentation
(2017)
Characterization of the size and mechanical properties of interphases is essential when designing multicomponent materials. When nanoindentation is used to investigate the size and mechanical properties of an interphase, a common challenge is that the indenter or the stress zone formed around it are often restricted by the reinforcement, making it difficult to distinguish the mechanical property variations caused by the interphase itself from those caused by the boundary effect. In this work, a testing system was developed that allows determining the indent affected zone and accounting for it in the interphase measurements of an epoxy/Cu system. Using finite element analysis, we confirmed the validity of the proposed system. Nanoindentation was used to investigate the Interphase between copper and two different epoxy systems; amine-cured and anhydride-cured. Nanoindentation results showed that a copper layer that is only 10 nm thick still exhibits a constriction effect on the indentations in its vicinity. The amine-cured epoxy did not show any sign of interphase existence using the introduced method. However,
a soft interphase with a thickness of ~1.7 μm was measured on theanhydride-cured epoxy. Furthermore, we show that the proposed system can be used to determine the interphase thickness as well as its relative mechanical properties regardless of the indentation depth.
This system can be further used for investigating other polymer/metal interphases to better understand the factors influencing them, thus helping engineer the interphase size and properties to enhance composite performance.
Epoxy/Carbon nanotube (CNT) composites are interesting materials that could be used in a wide variety of applications. In this study, CNT contents of 0.25, 0.5, 1 and 2 wt% were used for reinforcing epoxy. A nanoindentation device and a temperature regulating system were developed in order to investigate the effect of CNTs on the time-dependent properties of epoxy using relaxations and creep tests on the nano scale. The relaxation tests showed a significant shift for the relaxation spectrum towards shorter times with introducing a low CNT content of 0.25 wt%. Additionally, creep tests showed that both the holding time at a constant load and the unloading velocity have a major effect on the contact stiffness. However, there was no effect for the CNTs on the creep behavior with contents lower than 1 wt%, which was related to the presence of a percolation threshold around this value.
Characterization of the mechanical properties of interphases is essential when designing multicomponent materials such as fiber-reinforced matrices, protective coatings or multi-layered structures for integrated circuits. It can provide vital information about the durability of the finished product as a composite because failure is often initiated in the interfacial region induced by internal or external stress during fabrication or service. Nanoindentation is a powerful tool for investigating mechanical properties on the micro/nano scale. However, there are some challenges associated with conducting nanoindentation near interface regions. One main challenge is that the small thickness of the interphase region (typically 1-2µm) makes it difficult to apply several adjacent indents without overlap. Another issue is that the indentations are usually restricted by local reinforcement, and it becomes difficult to isolate the change in mechanical properties due solely to interphase formation. In this study we try to gauge the feasibility of nanoindentation for characterizing epoxy/Cu interphases. We develop a sample preparation method and optimize nanoindentation parameters in an attempt to avoid the restrictions mentioned above. Atomic force microscopy (AFM) and finite element analysis are employed as reference techniques to evaluate the effectiveness of our technique. We show the influence of preparation method and nanoindentaion parameters on measurements of interphase properties and how they relate the mentioned challenges.