- Alkali-activated materials (4)
- Acid resistance (2)
- MIC (2)
- Microbially induced corrosion (2)
- Biogene Schwefelsäurekorrosion (1)
- Biogenic acid corrosion (1)
- Künstliche Intelligenz (1)
- Mechanical flexibility (1)
- Mechanical property (1)
- Normung (1)
Organisationseinheit der BAM
- 6.3 Strukturanalytik (6) (entfernen)
Eingeladener Vortrag
- nein (2)
Rund ein Jahr haben DIN und DKE in einem gemeinsamen Projekt mit dem Bundesministerium für Wirtschaft und Energie und zusammen mit ca. 300 Fachleuten aus Wirtschaft, Wissenschaft, öffentlicher Hand und Zivilgesellschaft an der Normungsroadmap Künstliche Intelligenz gearbeitet. Eine hochrangige Steuerungsgruppe unter dem Vorsitz von Prof. Wolfgang Wahlster hat die Erarbeitung koordiniert und begleitet.
Ziel der Roadmap ist die frühzeitige Entwicklung eines Handlungsrahmens für die Normung und Standardisierung, der die internationale Wettbewerbsfähigkeit der deutschen Wirtschaft unterstützt und europäische Wertmaßstäbe auf die internationale Ebene hebt.(...)
Metakaolin-based alkali activated mortars (AAM) - with and without CuSO4·5H2O and ZnO addition (mass ratio Mn+/solid binder 0.08% to 1.7%) - were casted and exposed within an extensive long-term field campaign over the period of 20 months to a sewer basin, strongly affected by biogenic acid corrosion. (Un-)exposed AAM were tested regarding their physicochemical and microstructural properties, bioreceptivity and overall durability. Metal addition led to a retarding effect during alkali-activation reaction, as well as to an increase in open porosity of up to 3.0% and corresponding lower compressive strength of up to 10.9%. Reduced microbial colonization and diversity were observed on AAM with Cu, while Zn addition led to increased biodiversity. We propose that the observed higher durability of Cu-doped AAM is due to antibacterial effects and associated reduction of biogenic acid production, superseding overall negative effects of metal-dosage on physical material properties. Observed lower durability of Zn-doped AAM was related to combined negative physicochemical and microbial effects.
In this study, a multi-proxy approach combining 29Si, 27Al and 1H MAS-NMR, FEG-EPMA, XANES at the Cu K-edge and XRD analytics with hydrochemical tools such as ICP-OES analyses, oxygen-isotope signatures, and thermodynamic modelling was applied to K-silicate-activated metakaolin specimens - with and without CuSO4·5H2O addition - exposed to sulfuric acid at pH = 2 for 35 days. The results revealed a multistage deterioration mechanism governed by (i) acid diffusion, (ii) leaching of K-A-S-H, (iii) microstructural damage related to precipitation of expansive (K,Ca,Al)-sulfate-hydrate phases (iv) complete dissolution of the K-A-S-H framework, (v) and formation of silica gel in the outermost corroded regions. Copper ions were mainly located in layered spertiniite-chrysocolla-like phases in the as-cured materials. The results demonstrate an overall negative effect of Cu addition on chemical material durability, implying that the reported higher durability of Cu-doped AAM in biocorrosion environments can be best explained by bacteriostatic effects.
Materials with a high acid resistance are required in different important infrastructures. Examples include repair systems for sewer structures, where biogenic sulfuric acid corrosion is the major degradation mechanism. Low-calcium alkali-activated materials (AAMs) have been repeatedly observed to exhibit high acid resistance. However, the reasons for the high acid resistance of these materials were not fully under¬stood until recently, and the use of highly alkaline activator solutions to produce AAMs appears to hamper their commercial uptake. These issues have been tackled by characterising one-part AAMs and studying their alteration when exposed to sulfuric acid.
One-part AAMs were synthesized by mixing blends of solid silica and sodium aluminate with water, and subsequent curing at 60–80 °C. Acid resistance testing was performed according to DIN 19573, i.e. exposure to sulfuric acid at pH = 1 for 70 days. Characterisation of the cured and the acid-exposed materials was done by XRD, ATR-FTIR, SEM as well as 29Si, 27Al and 1H MAS NMR spectroscopy, including cross-polarisation and double-resonance methods.
Materials synthesized from industrial silicas were gel-zeolite composites, containing a substantial amount of unreacted ‘excess’ silica, while materials synthesized from rice husk ash were fully amorphous, containing ‘excess’ hydrous alumina. The sulfuric acid resistance of mortars based on these binders conformed to the requirements of DIN 19573 for sewer repair applications. The high acid resistance was caused by precipitation of silica gel at the mortar–solution interface, inhibiting further degradation. The presence of alumina gel may inhibit bacterial activity, potentially further improving performance in sewer environments.
The phase assemblage of silica/sodium aluminate-based one-part AAMs can be adjusted via choice of the silica starting material. Properly designed materials exhibit excellent acid resistance, caused by precipi¬tation of silica gel which protects subjacent regions, and they may also inhibit bacterial activity.
Alkali-activated materials have been repeatedly reported to exhibit high acid resistance, but no generally accepted hypothesis regarding the underlying mechanisms has emerged yet. To contribute to this issue, K-waterglass-activated metakaolin specimens, with and without the addition of CuSO4·5H2O in the starting mix, were exposed to either a chemically aggressive sewer environment (mortars) or sulfuric acid (pastes). The mode of copper incorporation in the materials and the formation of copper phases in the corroded layers were studied by XANES at the Cu K-edge, and 29Si, 27Al and 1H MAS NMR was employed to understand the processes during acid attack. Copper was found as a spertiniite-like phase in the as-cured materials, while in the deterioration layers of the pastes it was present as copper sulfate. In the corroded regions of the mortars, unequivocal identification of Cu phases was not possible, but the results were reconcilable with the presence of copper carbonate hydroxide. The solid-state NMR results revealed virtually complete dissolution of the K-A-S-H gel and the formation of silica gel, interpreted to be a central mechanism determining the acid resistance. No significant differences between the microstructural alterations of the pastes with and without Cu addition on (chemical) sulfuric acid attack were observed.
Mechanically flexible single crystals of molecular materials offer potential for a multitude of new directions in advanced materials design. Before the full potential of such materials can be exploited, insight into their mechanisms of action must be better understood. Such insight can be only obtained through synergistic use of advanced experimentation and simulation. We herein report the first detailed mechanistic study of elasto-plastic flexibility in a molecular solid. An atomistic origin for this mechanical behaviour is proposed through a combination of atomic force microscopy, μ-focus synchrotron X-ray diffraction, Raman spectroscopy, ab initio simulation, and computed elastic tensors. Our findings suggest that elastic and plastic bending are intimately linked and result from extensions of the same molecular deformations. The proposed mechanism bridges the gap between contested mechanisms, suggesting its applicability as a general mechanism for elastic and plastic bending in organic molecular crystals.