Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (51)
- Vortrag (48)
- Posterpräsentation (13)
- Beitrag zu einem Tagungsband (9)
- Beitrag zu einem Sammelband (1)
- Dissertation (1)
Sprache
- Englisch (123) (entfernen)
Schlagworte
- Interface (10)
- Mechanical properties (8)
- Epoxy (7)
- Thermoplaste (7)
- Verbundwerkstoffe (7)
- Acrylamide (5)
- Adhesion (5)
- Interphase (5)
- Kristallisation (5)
- Thermoresponsive polymers (5)
Organisationseinheit der BAM
- 5 Werkstofftechnik (23)
- 5.3 Polymere Verbundwerkstoffe (21)
- 6 Materialchemie (9)
- 6.0 Abteilungsleitung und andere (8)
- 5.4 Multimateriale Fertigungsprozesse (5)
- 4 Material und Umwelt (2)
- 4.4 Thermochemische Reststoffbehandlung und Wertstoffrückgewinnung (2)
- 8 Zerstörungsfreie Prüfung (2)
- 5.0 Abteilungsleitung und andere (1)
- 6.7 Materialsynthese und Design (1)
Paper des Monats
- ja (1)
Lightweighting as a cross-cutting technology contributes significantly to achieve the European Green Deal goals. Based on, but not limited to, advanced materials and production technologies, the demand for natural resources and CO2 emmissions are reduced by lightweighting during production, as well as use phase. Therefore, lightweighting is a crucial transformation technology assisting in decoupling economic growth from resource consumption. In this manner, lightweighting contributes significantly as a key technology of relevance for many industrial sectors such as energy, mobility, and infrastructure, towards resource efficiency, climate action and economic strength, as well as a resilient Europe. To strengthen international partnerships, addressing global issues of today at the edge of science with high performance lightweight material based on carbon fibers, an overview about the BAM expertise in carbon fiber reinforced materials is given.
Circumventing boundary effects while characterizing epoxy/copper interphases using nanoindentation
(2017)
Characterization of the size and mechanical properties of interphases is essential when designing multicomponent materials. When nanoindentation is used to investigate the size and mechanical properties of an interphase, a common challenge is that the indenter or the stress zone formed around it are often restricted by the reinforcement, making it difficult to distinguish the mechanical property variations caused by the interphase itself from those caused by the boundary effect. In this work, a testing system was developed that allows determining the indent affected zone and accounting for it in the interphase measurements of an epoxy/Cu system. Using finite element analysis, we confirmed the validity of the proposed system. Nanoindentation was used to investigate the Interphase between copper and two different epoxy systems; amine-cured and anhydride-cured. Nanoindentation results showed that a copper layer that is only 10 nm thick still exhibits a constriction effect on the indentations in its vicinity. The amine-cured epoxy did not show any sign of interphase existence using the introduced method. However,
a soft interphase with a thickness of ~1.7 μm was measured on theanhydride-cured epoxy. Furthermore, we show that the proposed system can be used to determine the interphase thickness as well as its relative mechanical properties regardless of the indentation depth.
This system can be further used for investigating other polymer/metal interphases to better understand the factors influencing them, thus helping engineer the interphase size and properties to enhance composite performance.
With this presentation, the push-out technique is explained. The focus of the experimental work is on the characterization of the fiber-matrix interface of short fiber reinforced composites. The reinforcing component was glass fibers and the matrix polymer was PA6.6 and PPA.
It is demonstrated for the first time that the push-out technique ca be applied on injection molded short fiber PMC and is sensitive to the mechanical interface properties. Further studies are planned on the influence of multiple processing, the temperature and humidity.
The longitudinal and transverse strength of three unidirectional thermoplastic prepreg systems: carbon fiber/polypropylene (CF/PP), polyamide 6 (CF/PA6), and polyphenylene sulfide (CF/PPS) are studied and analytical formulas are proposed for the estimation of matrix and fiber/matrix interface properties from composites properties. Since the matrices are semi-crystalline thermoplastics, the influence of cooling rate on the strength is statistically evaluated. While the 0° tensile strength is found to be independent of the cooling rate, the 90° tensile strength is strongly influenced by the matrix type and cooling rate. The matrix modulus increases as the cooling rate is decreased; the degree of crystallinity also increases. The matrix residual stress, interfacial shear strength, and mode II interlaminar fracture toughness are also found to depend on the cooling rate, with the trends different for different matrices.