Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
- Vortrag (22)
- Zeitschriftenartikel (16)
- Posterpräsentation (4)
- Beitrag zu einem Tagungsband (1)
Sprache
- Englisch (43)
Schlagworte
- Additive manufacturing (43) (entfernen)
Organisationseinheit der BAM
- 9.4 Integrität von Schweißverbindungen (43) (entfernen)
Paper des Monats
- ja (1)
Eingeladener Vortrag
- nein (22)
Design methodology of vessel produced by L PBF stainless steel using representative specimens
(2022)
This work presents the preliminary results of an ongoing project with a double objective: on the one hand, the characterisation of the mechanical properties against fatigue damage of an additively manufactured 316 stainless steel produced by laser powder bed-based (L-PBF) technology; on the other hand, the implementation of numerical simulation techniques able to predict the mechanical behaviour of the material in order to optimise and reduce the design costs of vessels used in the chemical sector. The current state of the work developed in this research framework allows showing the first batch of experimental results of crack propagation rate (FCGR) and high cycle fatigue (HCF) tests. The geometry of the vessels studied presents three clearly differentiated regions, either in terms of thickness (11-15 mm) or concerning the inclination of the walls to the direction of manufacturing (0º - 45º). The experimental campaign carried out so far allows identifying the differences in behaviour when comparing different extraction locations around the vessel. This is due to the variations in thermal cycles that the deposited material undergoes during the manufacturing process. Therefore, this causes variations in the microstructure which lead to changes in the response of the material. In this work, these differences are analysed qualitatively and quantitatively from the results of FCGR and HCF, thus allowing to locate the regions with the highest risk in terms of structural integrity against fatigue. This preliminary phase together with the numerical simulation of the additive manufacturing process are key to achieving a reliable description and modelling of the material. The latter will make it possible to address the priority aim of this project, involving the manufacture of independent samples whose properties are representative of the original material extracted from the reference vessels. It is, therefore, a comprehensive methodology for the design of additively manufactured components based on the localised fatigue mechanical properties of representative specimens.
Influence of deposition hatch length on residual stress in selective laser melted Inconel 718
(2018)
The present study aims to evaluate the bulk residual stresses in SLM parts by using neutron diffraction measurements performed at E3 line -BER II neutron reactor- of Helmholtz-Zentrum für Materialien und Energie (HZB) Berlin. Together with microstructure characterization and distortion measurements, it is possible to describe the stress state throughout the whole sample. The sample was measured in as-build condition (on a build plate) and after releasing from the build plate. The used material is the nickel based superalloy 718. This alloy is widely used in aerospace and chemical industries due to its superior corrosion and heat resistant properties.
Obtained results indicated different residual stress states for each of the transversal, longitudinal and normal component. The normal and transversal component exhibits a rather compressive behavior while the longitudinal was tensile in the center part of the sample and became compressive towards the tip. As expected, the absolute values of all stress components decreased after releasing the sample from the building plate. A surface scan utilizing a coordinate-measuring machine (CMM) allowed us to present top surface distortion before and after releasing. The top surface showed a distortion around ±80µm after releasing. Microstructure evolution in the scanning-building cross-section is largely dominated by columnar grains. In addition, many small random orientated grains are prominent in the regions of a laser overlap during SLM.
In summary, for the sample of superalloy 718 manufactured by SLM, a small distortion occurred when removing the sample from the build plate whereby the residual stress state decreases. Moreover, the observed columnar grains in the building direction could give a reason for the lowest stress values in that normal direction. However, the most important parameter controlling the residual stresses is the temperature gradient. Hence, future investigations are planned for a different scan strategy to distribute the laser impact in a more homogenous manner.
Alloy 36 is an iron-based alloy with 36% nickel. It is used in applications in which dimensional stability is critical, such as molding tools for composite materials in aerospace and automotive applications. Moreover, increasingly complex structures and the optimisation of resource efficiency also require additive manufacturing steps for the production or repair of components. Additively manufactured components have a heterogeneous microstructure and anisotropic mechanical properties. In addition, the manufactured components require subsequent machining surface finishing due to the high requirements. Nickel iron alloys are difficult to machine. Additionally, inhomogeneous microstructure may lead to unstable cutting forces and conditions. Alloy modifications are made to the alloy 36. For this purpose, titanium, zirconium and niobium are added up to 1 % by mass each. Plasma-Transferred-Arc is used for the welding tests. The hardness profile is determined on the transverse section. The initial structure as well as the modifications have an austenitic structure. The microstructure of the modifications of Alloy 36 with 1% Ti and 1% Zr is not refined, instead the grain size increases.
Alloy 36 (1.3912), also known as “Invar”, is an alloy with 36% nickel. The alloy has a remarkably low thermal expansion coefficient in certain temperature ranges. Therefore, it is used in applications in which dimensional stability is critical, such as moulding tools for composite materials in aerospace and automotive applications. Moreover, increasingly complex structures and the optimisation of resource efficiency also require additive manufacturing steps for the production or repair of components. Additively manufactured components have a heterogeneous microstructure and anisotropic mechanical properties. In part I of this investigation, the initial alloy 36 is modified with the elements Ti, Zr and Hf up to a maximum of 0.33 wt.-%. The influence of the modification elements on the microstructure as well as on the hardness of the AM components is examined. Part II focusses on the effect of the alloy modifications on machinability as well as on the surface integrity of plasma-transferred-arc-welded (PTA) and finish milled invar components. The results show that PTA welding cause numerous finely distributed precipitates with high silicon content.
Co-Cr alloys are frequently used for highly stressed components, especially in turbine and plant construction, due to their high resistance to thermal and mechanical stress, as well as to corrosive and abrasive loads. Furthermore, they are classified as difficult-to-cut materials because of their high strength and toughness as well as their low thermal conductivity. However, for Co, an increased cost and supply risk can be observed in recent years. Therefore, additive manufacturing (AM) offers significant economic advantages due to higher material efficiency regarding repair, modification, and manufacturing of such components. Concerning inhomogeneity and anisotropy of the microstructure and properties as well as manufacturing-related stresses, a lot of knowledge is still necessary for the economic use of additive welding processes in SMEs. In addition, subsequent machining, particularly contour milling, is essential to generate the required complex contours and surfaces. Hence, additive and machining manufacturing processes need to be coordinated in a complementary way, especially due to additional challenges arising in milling of heterogeneous hard-to-cut microstructures. Recently, it has been shown that modern, hybrid cutting processes, such as ultrasonic-assisted milling (US), can improve the cutting situation. In this investigation, the Co-Cr initial alloy is additionally modified with Ti and Zr up to 1 wt.-% with the aim to enhance the homogeneity of the microstructure and, thus, the machinability. Hence the investigation includes finish milling tests of the AM components and the comparison of US and conventional machining. Both the modifications and the ultrasonic assistance exhibit a significant effect on the machining situation, e.g., US causes a higher surface integrity of the finish milled surfaces compared to conventional milling.
Due to increasing requirements relating to the efficiency of highly stressed components in turbine or plant construction, the use of cost-intensive, difficult to process materials is increasingly necessary today. In this context, cobalt-chromium alloys in particular are highly resistant to thermal and mechanical stress, as well as to corrosive and abrasive loads. Moreover, increasingly complex structures and the optimisation of resource efficiency also require additive manufacturing steps for the production or repair of components in many sectors. In order to realise a homogeneous and isotropic microstructure, alloy modifications are made to the alloy CoCr26Ni9Mo5W. For this purpose, hafnium and zirconium are added at 1 % and 0,33 % by mass each, as these elements are supposed to have a positive effect on the microstructure morphology. Plasma-Transferred-Arc is used for the welding tests. Wall structures are welded by multiple single-layer, overlapping welding beads on low-alloyed steel substrate (S355). The results show that the alloying elements hafnium and zirconium have a clear influence on the microstructure. Hardness measurements were also carried out. With each modification, the hardness is increased compared to the original material. The machining analyses show a reduction in cutting forces using ultrasonic assisted milling for high cutting speed and low feed rate.
Co-Cr alloys are frequently used for highly stressed components, especially in turbine and plant construction, due to their high resistance to thermal and mechanical stress, as well as to corrosive and abrasive loads. Furthermore, they are classified as difficult-to-cut materials because of their high strength and toughness as well as their low thermal conductivity. However, for Co, an increased cost and supply risk can be observed in recent years. Therefore, additive manufacturing (AM) offers significant economic advantages due to higher material efficiency regarding repair, modification, and manufacturing of such components. Concerning inhomogeneity and anisotropy of the microstructure and properties as well as manufacturing-related stresses, a lot of knowledge is still necessary for the economic use of additive welding processes in SMEs. In addition, subsequent machining, particularly contour milling, is essential to generate the required complex contours and surfaces. Hence, additive and machining manufacturing processes need to be coordinated in a complementary way, especially due to additional challenges arising in milling of heterogeneous hard-to-cut microstructures. Recently, it has been shown that modern, hybrid cutting processes, such as ultrasonic-assisted milling (US), can improve the cutting situation. In this investigation, the Co-Cr initial alloy is additionally modified with Ti and Zr up to 1 wt% with the aim to enhance the homogeneity of the microstructure and, thus, the machinability. Hence the investigation includes finish milling tests of the AM components and the comparison of US and conventional machining. Both the modifications and the ultrasonic assistance exhibit a significant effect on the machining situation; for example US causes a higher surface integrity of the finish milled surfaces compared to conventional milling.
Ni alloys are cost intensive materials and generally classified as difficult-to-cut materials. However, machining of these materials is needed especially in case of alloy 36 (1.3912), which is commonly used in mould construction for the production of fibre-reinforced composites. With regard to repair, modification and manufacturing of such components, additive manufacturing offers significant economic advantages. Nevertheless, subsequent machining steps are needed to achieve the final component contour and defined surface conditions. Dependent on the material and machining process conditions, detrimental tensile residual stresses may be the result on the machined surface, having negative impact on the component performance and safety. Recent studies exhibited that hybrid machining processes, such as ultrasonic-assisted milling (USAM), are suitable for achieving favourable residual stress states at the surface of difficult-to-cut Ni-Cr alloys. In this investigation, wire arc additive manufactured (WAAM) specimens of alloy 36 were finish milled under different milling conditions. In addition to the machined surfaces condition and topology, the surface-near residual stresses were analysed using X-ray diffraction (XRD). Especially for low cutting speeds, significantly improved surface properties, roughness parameters and lower mechanical and microstructural degradations were found for the specimen machined with USAM compared to conventional milling. The improved surface integrity could furthermore be observed by a significant reduction of the tensile residual stresses in the surface boundary area.
Ni alloys are cost intensive materials and generally classified as difficult-to-cut materials. However, machining of these materials is needed especially in case of alloy 36 (1.3912), which is commonly used in mould construction for the production of fibre-reinforced composites. With regard to repair, modification and manufacturing of such components, additive manufacturing offers significant economic advantages. Nevertheless, subsequent machining steps are needed to achieve the final component contour and defined surface conditions. Dependent on the material and machining process conditions, detrimental tensile residual stresses may be the result on the machined surface, having negative impact on the component performance and safety. Recent studies exhibited that hybrid machining processes, such as ultrasonic-assisted milling (USAM), are suitable for achieving favourable residual stress states at the surface of difficult-to-cut Ni-Cr alloys. In this investigation, wire arc additive manufactured (WAAM) specimens of alloy 36 were finish milled under different milling conditions. In addition to the machined surfaces condition and topology, the surface-near residual stresses were analysed using X-ray diffraction (XRD). Especially for low cutting speeds, significantly improved surface properties, roughness parameters and lower mechanical and microstructural degradations were found for the specimen machined with USAM compared to conventional milling. The improved surface integrity could furthermore be observed by a significant reduction of the tensile residual stresses in the surface boundary area.
Alloy 36 (1.3912), also known as “Invar”, is an alloy with 36% nickel. It was developed in 1897 by Guillaume and stands out for its very low thermal expansion coefficient. It is classified as a difficult-to-cut material and is commonly used for the production of fiber-reinforced composites in the field of mold construction. Additive manufacturing (AM) offers many economic advantages regarding the repair, modification and manufacture of entire components. Subsequent machining of the AM components is necessary to account for complex structures, final contours or defined surfaces. This is usually done using a tool with a geometrically defined cutting edge, i.e., milling processes. Surface integrity is determined by metallurgical (e.g., microstructure of the subsurface), topological (e.g., surface defects, roughness) and mechanical (e.g., residual stresses) factors, which is crucial in terms of component safety and performance. Modern, hybrid cutting processes, such as ultrasonic-assisted milling (US), provide potentially improvement of the cutting situation of these components.
In part I of this investigation, the initial alloy 36 is modified with the elements Ti, Zr and Nb up to a maximum of 1 wt.-%. The influence of the modification elements on the microstructure as well as on the hardness of the AM components is examined. Part II focusses on the effect of the alloy modifications on machinability as well as on the surface integrity of plasma-transferred-arc-welded (PTA) and finish milled invar components.
The results show a significant positive influence of ultrasonic assistance on the resulting cutting force of both materials. The modification with 1% Ti shows a positive influence on the surface integrity, as the roughness of the conventional machining processes is lower compared to the initial alloy, which has to be confirmed in further experiments.