Claddings of different nickel based alloys were generated on a mild Steel (S235JR) and a stainless steel type 304 by Cold Metal Transfer (CMT). This welding procedure possesses a low degree of mixing between the Substrate and cladding material. Thus it improves the corrosion behaviour of the claddings. The aim of our investigations was to examine the effect of the welding parameters: energy per unit length, shielding gas and finishing surface treatment on the pitting corrosion behaviour of the claddings.
However, under Standard test conditions nickel based alloys are often resistant to pitting corrosion. Moreover these test methods are inaccurate and require a large period of time resulting from the iterative progress to determine the critical pitting temperature (CPT). A potentiostatic test method was modified using a high concentrated CaCI2-solution and a conventional three electrode measuring cell. The pitting corrosion behaviour is calculated from current noise charges. During the test the course of corrosion is detected online by the evaluation of electrochemical noise Signals while a continuous increase of temperature by a defined heating rate is realised.
Thus a critical pitting temperature can be estimated by only one attempt. Furthermore the deviation of the measured CPT is very low compared to Standard tests using gravimetrical and microscopic evaluation. That enables to figure out the influence of the welding parameters in an exact way.
Co-Cr alloys are frequently used for highly stressed components, especially in turbine and plant construction, due to their high resistance to thermal and mechanical stress, as well as to corrosive and abrasive loads. Furthermore, they are classified as difficult-to-cut materials because of their high strength and toughness as well as their low thermal conductivity. However, for Co, an increased cost and supply risk can be observed in recent years. Therefore, additive manufacturing (AM) offers significant economic advantages due to higher material efficiency regarding repair, modification, and manufacturing of such components. Concerning inhomogeneity and anisotropy of the microstructure and properties as well as manufacturing-related stresses, a lot of knowledge is still necessary for the economic use of additive welding processes in SMEs. In addition, subsequent machining, particularly contour milling, is essential to generate the required complex contours and surfaces. Hence, additive and machining manufacturing processes need to be coordinated in a complementary way, especially due to additional challenges arising in milling of heterogeneous hard-to-cut microstructures. Recently, it has been shown that modern, hybrid cutting processes, such as ultrasonic-assisted milling (US), can improve the cutting situation. In this investigation, the Co-Cr initial alloy is additionally modified with Ti and Zr up to 1 wt% with the aim to enhance the homogeneity of the microstructure and, thus, the machinability. Hence the investigation includes finish milling tests of the AM components and the comparison of US and conventional machining. Both the modifications and the ultrasonic assistance exhibit a significant effect on the machining situation; for example US causes a higher surface integrity of the finish milled surfaces compared to conventional milling.
In vielen Anwendungen werden aufgrund zunehmender Anforderungen an den Widerstand gegenüber hohen, kombinierten mechanischen, tribologischen, thermischen und korrosiven Beanspruchungen Hochleistungslegierungen eingesetzt. Den vielfach komplexen Bauteilstrukturen, herausfordernden Fertigungseigenschaften und der Erhöhung der Ressourceneffizienz lässt sich heute mit der additiven Fertigung (AM) begegnen, dem oftmals noch unzureichende Kenntnisse über die resultierende Homogenität und Anisotropie der speziellen Gefüge und den damit verbundenen Eigenschaften entgegensteht. Viele Anwendungen benötigen zudem definierte Oberflächen mit hohen Anforderungen an die Oberflächenintegrität, dem durch komplementären Einsatz von additiven und abtragenden Fertigungsschritten Rechnung getragen wird. Hochleistungslegierungen auf der Basis von Nickel oder Kobalt sind infolge der niedrigen Wärmeleitfähigkeit verbunden mit hoher Festigkeit und Zähigkeit äußerst herausfordernd mit Blick auf eine wirtschaftliche Zerspanung mit geometrisch bestimmter Schneide. Ein Vorhaben (IGF-Nr. 20.979 N/DVS-Nr. 1.3211) der BAM und TU Clausthal/ISAF befasst sich mit der Lösung dieser Problemstellung durch gezielte Beeinflussung des Gefüges mittels Modifikation der Schweißzusatzwerkstoffe und den Einsatz des ultraschallunterstützten Fräsens (US), bei gleichzeitiger Sicherstellung der geforderten Eigenschaften der untersuchten Werkstoffe. Im vorliegenden Beitrag werden für die beiden untersuchten FeNi- und CoCr-Legierungen wesentliche Zusammenhänge zwischen verschiedenen Legierungsmodifikationen, der entstehenden Gefügemorphologie und den Zerspanungseigenschaften von mittels PTA additiv gefertigter Proben dargestellt. Hierbei ließen sich Ti, Zr und Hf pulvermetallurgisch zu den jeweiligen Ausgangsschweißzusätzen hinzulegieren.
Untersuchungsmethoden beim Fräsen additiv gefertigter schwer spanbarer Kobalt-Chrom-Legierungen
(2021)
Für den Anlagenbau werden hochbelastete Komponenten aus Co-Cr-Legierungen hergestellt. Dabei ist die Zerspanung so herausfordernd, dass additive Fertigungsschritte oft wirtschaftlicher sind. Diese bedingen aber vorwiegende heterogene, anisotrope Gefüge und Eigenschaften und bei nachfolgender Fräsbearbeitung unstetige Zerspankräfte und instabile Spanvorgänge. Hierbei können hybride Zerspanprozesse helfen, hohe Belastungen für Werkzeug und Werkstückoberfläche zu minimieren. Diesbezügliche Charakterisierungen erfordern speziell adaptierte Zerspanungsanalysen.
Anhand eines Anwendungsbeispiels, bei dem eine Modifikation der Ausgangslegierung mit 1 % Hf erfolgte, wird die Wechselwirkung zwischen Gefügemorphologie und Fräsprozess dargestellt, der konventionelle mit einem hybriden ultraschallunterstützten Fräsprozess verglichen und die Charakterisierung des Werkzeugverschleißes anhand zweier verschiedener Fräser betrachtet. Analysen auftretender Prozesskräfte mittels Piezo-Mehrkomponenten-Dynamometer, der Werkzeugoszillation mittels Laser-Vibrometer und zusätzliche In-situ-Temperaturmessungen der Werkzeugschneiden mittels Highspeed-Pyrometer bilden den Kern der neuen Zerspanungsprüftechnik.
Die vorgestellten Untersuchungsmethoden bilden die Vorgänge bei der Zerspanung additiv gefertigter Werkstoffe detailliert und reproduzierbar ab. Sowohl Legierungsmodifikation als auch hybride Prozessbedingungen lassen gezielte Einflüsse zur deutlichen Verbesserung der Zerspanungssituation zu.
Nickel-Iron-Alloy Modification to Enhance Additively Welded Microstructure for Subsequent Milling
(2022)
The aerospace industry uses nickel–iron alloys, e.g., FeNi36, to create moulding tools for composite materials, since these alloys have a low coefficient of thermal expansion. Nickel–iron alloys are hard-to-cut materials. The moulding tools are large in size and involve complex structures, making them cost-intensive and difficult to manufacture. Thus, the focus is set on additive manufacturing, which can additionally enable the repair of components in order to eliminate local defects. However, the process usually results in a heterogeneous microstructure and anisotropic mechanical properties. As there is a high demand for a precise and exact fit of the precision moulds and the surface quality, the welded components must be subsequently machined. Additionally, inhomogeneous microstructure may lead to unstable cutting forces and conditions. Consequently, a modification of the microstructure morphology is achieved through specific alloy modifications in order to stabilise and improve the subsequent machining process. Therefore, titanium and zirconium are chosen as modification elements with a maximum 1% weight percent and are added to nickel–iron alloy powder. The elements are alloyed, and build-up welded by plasma-transferred-arcwelding. The resulting microstructure morphology of the welded wall structure and the machining properties are then determined. It can be shown that titanium has a significant effect on the structural morphology of the welded layers, as well as on the machining.
Ni alloys are generally classified as difficult-to-cut materials and cost intensive. Additive manufacturing (AM) offers economic advantages. However, machining of these AM components is mandatory to create the final contour or surface. The inhomogeneous and anisotropic microstructure and properties of AM components causes an unstable cutting process. Moreover, undesirable tensile residual stresses are generated due to subsequent machining. In this investigation, the initial alloy 36 is modified with Ti and Nb up to 1.6 wt.-% and build-up welded via gas metal arc welding (GMAW) and plasma-transferred-arc (PTA). Then, finish-milling tests are carried out to investigate the influence of the modification as well as the cutting parameters on the resulting cutting force and the surface integrity. In addition, the conventional milling process (CM) is compared with the ultrasonic-assisted milling process (US), which has a significant influence on the machinability as well as on the surface integrity.
Cobalt chromium alloys are often used in turbine and plant construction. This is based on their high thermal and mechanical stress resistance as well as their high wear resistance to corrosive and abrasive loads. However, cobalt is a cost-intensive material that is difficult to machine. Moreover, increasingly complex structures and the optimisation of resource efficiency also require additive manufacturing steps for the production or repair of components in many sectors. Concerning inhomogeneity and anisotropy of the microstructure and properties as well as manufacturing-related stresses, a lot of knowledge is still necessary for the economic use of additive welding processes in SMEs. As a result of the high stresses on the components
and requirements for a high surface quality, a complementary use of additive and machining manufacturing processes is necessary. Thereby, Co–Cr alloys are extremely challenging for machining with geometrically defined cutting edges because of their low thermal conductivity combined with high strength and toughness. An approach to solve this problem is to refine and homogenise the microstructure. This is achieved by modifying the alloy with elements zirconium and hafnium, which are added up to a maximum of 1 wt.-%. A reduction of the process forces and stresses on the tool and work piece surface is also achievable via hybrid milling processes. There are already studies on the combined use of additive and machining manufacturing processes based on laser technology. However, knowledge based on powder and wire-based arc processes is important, as these processes are more widespread. Furthermore, the effects on the surface zone of additively manufactured components by hybrid finish milling have not yet been a subject of research. The results show that the structural morphology could be significantly influenced with the addition of zirconium and hafnium.
Für Komponenten im Turbinen- oder Anlagenbau werden aufgrund ihrer Eigenschaften häufig Kobalt-Chrom-Legierungen verwendet. Diese weisen eine hohe Korrosionsbeständigkeit und hohen Verschleißwiederstand auf. Aufgrund der komplexen Strukturen und dem Bestreben nach Ressourceneffizienz wird zur Herstellung der Komponenten die additive Fertigung verwendet. Hierbei sind hinsichtlich der Inhomogenität und Anisotropie der Gefüge und deren Eigenschaften weitere Kenntnisse notwendig. Bei den vorliegenden Belastungen liegt ein erhöhter Anspruch an die Oberflächenintegrität vor, welcher durch komplementären Einsatz von additiven und abtragenden Fertigungsschritten sichergestellt wird. Dabei sind gerade Co-Cr-Legierungen wegen der niedrigen Wärmeleitfähigkeit verbunden mit hoher Festigkeit und Zähigkeit äußerst herausfordernd mit Blick auf eine wirtschaftliche Zerspanung mit geometrisch bestimmter Schneide. Ausgehend von dieser Problemstellung erfolgt im Zuge eines Gemeinschaftsvorhabens des ISAF in Kooperation mit der BAM eine gezielte Beeinflussung des Gefüges. Ziel des Projektes ist die Zusammenhänge zwischen verschiedenen Legierungsmodifikationen, der entstehenden Gefügemorphologie und den Zerspanungseigenschaften von Co- Cr-Legierungen für die additive Fertigung mittels PTA darzustellen. Der Fokus liegt auf dem Beheben der bestehenden Nachteile bei gleichzeitigem Aufrechthalten der besonderen Eigenschaften der Legierung. Durch das Hinzulegieren von variierenden Gehalten von Zirkonium und Hafnium wird die Gefügeveränderung eingestellt. Es hat sich gezeigt, dass Hafnium als zusätzliches Legierungselement einen deutlichen Einfluss auf die Gefügemorphologie hat. Darüber hinaus wird die Auswirkung der Legierungsmodifikation auf die Härte und die Zerspanbarkeit dargestellt.
Alloy 36 (1.3912) is an alloy with 36% nickel and 64% iron and is generally classified as a difficult-to-cut material. Increasingly complex structures and the optimization of resource efficiency are making additive manufacturing (AM) more and more attractive for the manufacture or repair of components. Subsequent machining of AM components is unavoidable for its final contour. By using modern, hybrid machining processes, e.g., ultrasonic-assisted milling (US), it is possible to improve the cutting situation regarding the resulting surface integrity as well as the cutting force. Part I deals with the influence of the alloying elements Ti, Zr, and Hf on the microstructure and the hardness of the initial alloy 36. Part II focusses on the effect of the alloy modifications and the ultrasonic assistance on machinability as well as on the surface integrity after finish-milling. The results show a highly significant influence of the ultrasonic assistance. The cutting force during the US is reduced by over 50% and the roughness of approx. 50% compared to conventional milling (CM) for all materials investigated. Moreover, the US causes a defect-free surface and induces near-surface compressive residual stresses. CM leads to a near-surface stress state of approx. 0 MPa.