The image designed by Natalia Cano Murillo and colleagues shows the cross section of a ternary composite (boehmite/polycarbonate/epoxy, 80μm x 80μm). The surface was measured by AFM kelvin probe microscopy, yielding the surface potential which is shown as 3D‐surface and contour lines. The sample was further subjected to AFM force spectroscopy with a lateral resolution of 1μm², yielding the local Young's modulus, projected in false colors on the 3D surface. The ternary system, containing boehmite nanoparticles, shows a broad distribution of modulus, desirable for optimized macroscopic mechanical properties, such as high stiffness as well as toughness.
In this work, a novel boehmite (BA)-embedded organic/inorganic nanocomposite coating based on cycloaliphatic epoxy oligosiloxane (CEOS) resin was fabricated applying UV-induced cationic polymerization. The main changes of the material behavior caused by the nanofiller were investigated with regard to its photocuring kinetics, thermal stability, and glass transition. The role of the particle surface was of particular interest, thus, unmodified nanoparticles (HP14) and particles modified with p-toluenesulfonic acid (OS1) were incorporated into a CEOS matrix in the concentration range of 1–10 wt.%. Resulting nanocomposites exhibited improved thermal properties, with the glass transition temperature (Tg) being shifted from 30 °C for unfilled CEOS to 54 °C (2 wt.% HP14) and 73 °C (2 wt.% OS1) for filled CEOS. Additionally, TGA analysis showed increased thermal stability of samples filled with nanoparticles. An attractive interaction between boehmite and CEOS matrix influenced the curing. Real-time infrared spectroscopy (RT-IR) experiments demonstrated that the epoxide conversion rate of nanocomposites was slightly increased compared to neat resin. The beneficial role of the BA can be explained by the participation of hydroxyl groups at the particle surface in photopolymerization processes and by the complementary contribution of p-toluenesulfonic acid surface modifier and water molecules introduced into the system with nanoparticles.