Wissenschaftliche Artikel der BAM
Filtern
Dokumenttyp
- Zeitschriftenartikel (192) (entfernen)
Sprache
- Englisch (186)
- Deutsch (5)
- Portugiesisch (1)
Schlagworte
- Concrete (15)
- Corrosion (14)
- Alkali-activated materials (13)
- Flame retardant (9)
- Cement (6)
- Durability (5)
- Additive manufacturing (4)
- Carbon steel (4)
- Cone calorimeter (4)
- Fatigue (4)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (192) (entfernen)
Paper des Monats
- ja (18)
Although fire safety regulations for buses have been adapted in recent years regarding, for example, fire detection and engine fire suppression systems, the changes in regulations for bus interior materials are minimal. A comparison of fire safety regulations for interior materials in other transport sectors for trains, ships or aircraft reveals a much lower level of requirements for bus materials. Although repeated bus accidents as well as fire statistics show the danger a bus fire can pose to passengers.
In particular, the combination of a fire incident and passengers with reduced mobility led to severe disasters in Germany and other European countries. To enhance the fire safety for passengers, the interior bus materials are crucial as the fire development in the bus cabin determines whether escape and rescue is possible. Against this background, bus interior materials were tested in different fire test scenarios. Measurement of a wide variety of parameters, for example, the mass loss, ignition time, smoke gas composition, heat release rate among others were carried out. Tested materials complied to the newest set of requirements. For this purpose, interior materials and their components had to be identified according to their chemical structure. Parts of the tests were funded by BASt (Federal Highway Research Institute) in the project 82.0723/2018. Experimental results show reaction-to-fire behaviour which lead to very limited times for escape and rescue in case of fire in a bus cabin. Based on the studies on fire behaviour and toxicity assessment, recommendations for improved fire safety regulations for interior materials could be made.
REALight ‐ Leichtgranulate und REA‐Gips aus feinkörnigen sulfatbelasteten Bau‐ und Abbruchabfällen
(2023)
Ziel des Projekts REALight ist die Entwicklung einer Referenzanlage zur Herstellung von Leichtgranulaten (leichte Gesteinskörnungen) aus Bau‐ und Abbruchabfällen und zur Gipsrückgewinnung. Als Rohstoffe werden bisher ungenutzte oder auf niedrigem Niveau eingesetzte Bau‐ und Abbruchabfälle und industrielle Nebenprodukte verwendet. Als Produkte werden leichte Gesteinskörnungen hergestellt. Die Sulfatabtrennung durch eine thermische Zersetzung bildet die Grundlage für die zusätzliche Gewinnung von Rauchgasentschwefelungs‐Gips (REA‐Gips). Das Projekt wird im Rahmen der Fördermaßnahme „Ressourceneffiziente Kreislaufwirtschaft – Bauen und Mineralische Stoffkreisläufe (ReMin)” gefördert. ReMin ist eine Maßnahme zur Umsetzung des BMBF‐Forschungskonzepts „Ressourceneffiziente Kreislaufwirtschaft” als Teil der BMBF Strategie „Forschung für nachhaltige Entwicklung – FONA”. Ziel der Förderung ist es, den Ausbau der Kreislaufwirtschaft voranzutreiben. Im Mittelpunkt steht dabei die Bauwirtschaft mit ihrer hohen Nachfrage nach Rohstoffen und gleichzeitig großen Mengen an anfallenden mineralischen Abfällen. Am Projekt REALight sind 12 Partner aus verschiedenen Bereichen der Baustoffherstellung und ‐anwendung, Abfallaufbereitung, Verfahrenstechnik sowie Forschung und Entwicklung beteiligt.
Nowadays geotechnical engineering firms have powerful software tools to extent their consult-ing business also into dynamic soil-structure interaction, which before has been restricted to a rather small community of specialized experts in this field, and they certainly do. This is par-ticularly true with respect to non-seismic sources, that is all kinds of human induced vibrations. Hence, there is a demand from clients as well as from contractors to have guidance on the re-quirements as well as the limits of numerical modelling of soil-structure interaction. From the literature as well as from relevant standards, recommendations for the numerical modelling of soil-structure interaction problems involving seismic actions are well known, e. g. ASCE/SEI 4-16. There are, however, some particularities when dealing with human-induced vibrations, which are absent in seismic analyses. For human-induced excitations very little specific guid-ance has been published in the past. A machine foundation on a homogeneous half space ex-cited by harmonic loads with excitation frequency between 4 Hz and 64 Hz has been ana-lysed by means of several commercially available software packages. Parametric studies have been performed to verify if recommendations for seismic soil-structure analyses are valid for non-seismic analyses as well. This paper provides details on the benchmark example and the most important conclusions from the undertaken parametric studies.
The reduction in train-induced ground vibrations by different railway lines and by mitigation measures in the propagation path was analysed in a unified approach by two-dimensional finite element calculations. In general, there was no reduction at low frequencies, and the reduction be-came stronger with increasing frequencies. A maximum reduction of 0.1 at high frequencies was established with an open trench. Reductions between 0.7 and 0.2 have been found for the other sit-uations, filled trenches, walls, plates, and blocks, as well as for railway lines on dams, in cuts and in a tunnel. Bridges can produce amplifications due to their resonance frequencies, but also strong reductions due to massive bridge piers. The influence of some parameters has been analysed, such as the bridge span, the inclination of the dam and the cut, the stiffness of the soil, and the tunnel structure. The dynamic track stiffnesses of a surface, bridge, and tunnel track have been calculated using the 3D finite-element boundary-element method for comparison with corresponding meas-urements.
Relation of craze to crack length during slow crack growth phenomena in high‐density polyethylene
(2024)
The craze‐crack mechanism occurring in high‐density polyethylene (HDPE) causing slow crack growth and environmental stress cracking is investigated in detail with respect to the relation of crack length and the related craze zone. This is essential for the understanding of the resulting features of the formed fracture surface and their interpretation in the context of the transition from crack propagation to ductile shear deformation. It turns out that an already formed craze zone does not inevitably result in formation of a propagating crack, but could also undergo ductile failure. For the examination, the full notch creep test (FNCT) was employed with a subsequent advanced fracture surface analysis that was performed using various imaging techniques: light microscopy, laser scanning microscopy, scanning electron microscopy, and X‐ray micro computed tomography scan. FNCT specimens were progressively damaged for increasing durations under standard test conditions applying Arkopal, the standard surfactant solution, and biodiesel as test media were used to analyze the stepwise growth of cracks and crazes. From considerations based on well‐established fracture mechanics approaches, a theoretical correlation between the length of the actual crack and the length of the preceding craze zone was established that could be evidenced and affirmed by FNCT fracture surface analysis. Moreover, the yield strength of a HDPE material exposed to a certain medium as detected by a classic tensile test was found to be the crucial value of true stress to induce the transition from crack propagation due to the craze‐crack mechanism to shear deformation during FNCT measurements.
Highlights
- Progress of crack formation in high‐density polyethylene is analyzed by different imaging techniques
- Determined growth rates depend on distinction between craze zone and crack
- The ratio of the present crack to the anteceding craze zone is validated theoretically
- The transition from crack propagation to ductile shear deformation is identified
- An already formed craze zone may still fail by ductile mechanisms
A strain-based automated operational modal analysis algorithm is proposed to track the long-term dynamic behavior of a horizontal wind turbine under operational conditions.
This algorithm is firstly validated by a scaled wind turbine model, and then it is applied to the dynamic strain responses recorded from a 5 MW wind turbine system. We observed variations in the fundamental frequency and 1f, 3f excitation frequencies due to the mass imbalance of the blades and aerodynamic excitation by the tower dam or tower wake. Inspection of the Campbell diagram revealed that the adverse resonance phenomenon and Sommerfeld effect causing excessive vibrations of the wind tower.
Many standardised durability testing methods have been developed for Portland cement-based concretes, but require validation to determine whether they are also applicable to alkali-activated materials. To address this question, RILEM TC 247-DTA ‘Durability Testing of Alkali-Activated Materials’ carried out round robin testing of carbonation and chloride penetration test methods, applied to five different alkali-activated concretes based on fly ash, blast furnace slag or metakaolin. The methods appeared overall to demonstrate an intrinsic precision comparable to their precision when applied to conventional concretes. The ranking of test outcomes for pairs of concretes of similar binder chemistry was satisfactory, but rankings were not always reliable when comparing alkali-activated concretes based on different precursors. Accelerated carbonation testing gave similar results for fly ash-based and blast furnace slag-based alkali-activated concretes, whereas natural carbonation testing did not. Carbonation of concrete specimens was observed to have occurred already during curing, which has implications for extrapolation of carbonation testing results to longer service life periods. Accelerated chloride penetration testing according to NT BUILD 443 ranked the tested concretes consistently, while this was not the case for the rapid chloride migration test. Both of these chloride penetration testing methods exhibited comparatively low precision when applied to blast furnace slag-based concretes which are more resistant to chloride ingress than the other materials tested.
The aim of RILEM TC 247-DTA ‘Durability Testing of Alkali-Activated Materials’ is to identify and validate methodologies for testing the durability of alkali-activated concretes. To underpin the durability testing work of this committee, five alkali-activated concrete mixes were developed based on blast furnace slag, fly ash, and flash-calcined metakaolin. The concretes were designed with different intended performance levels, aiming to assess the capability of test methods to discriminate between concretes on this basis. A total of fifteen laboratories worldwide participated in this round robin test programme, where all concretes were produced with the same mix designs, from single-source aluminosilicate precursors and locally available aggregates. This paper reports the mix designs tested, and the compressive strength results obtained, including critical insight into reasons for the observed variability in strength within and between laboratories.
The RILEM technical committee TC 247-DTA ‘Durability Testing of Alkali-Activated Materials’ conducted a round robin testing programme to determine the validity of various durability testing methods, originally developed for Portland cement based-concretes, for the assessment of the durability of alkali-activated concretes. The outcomes of the round robin tests evaluating sulfate resistance, alkali-silica reaction (ASR) and freeze–thaw resistance are presented in this contribution. Five different alkali-activated concretes, based on ground granulated blast furnace slag, fly ash, or metakaolin were investigated. The extent of sulfate damage to concretes based on slag or fly ash seems to be limited when exposed to an Na2SO4 solution. The mixture based on metakaolin showed an excessive, very early expansion, followed by a dimensionally stable period, which cannot be explained at present. In the slag-based concretes, MgSO4 caused more expansion and visual damage than Na2SO4; however, the expansion limits defined in the respective standards were not exceeded. Both the ASTM C1293 and RILEM AAR-3.1 test methods for the determination of ASR expansion appear to give essentially reliable identification of expansion caused by highly reactive aggregates. Alkali-activated materials in combination with an unreactive or potentially expansive aggregate were in no case seen to cause larger expansions; only the aggregates of known very high reactivity were seen to be problematic. The results of freeze–thaw testing (with/without deicing salts) of alkali-activated concretes suggest an important influence of the curing conditions and experimental conditions on the test outcomes, which need to be understood before the tests can be reliably applied and interpreted.
Risk Assessment and Value of Action Analysis for Icing Conditions of Wind Turbines Close to Highways
(2019)
The paper presents research results from the Marie Skłodowska-Curie Innovative Training Network INFRASTAR in the field of reliability approaches for decision-making for wind turbines and bridges. This paper addresses the application of Bayesian decision analysis for installation of heating systems in wind turbine blades in cases where an ice detection system is already installed in order to allow wind turbines to be placed close to highways. Generally, application of ice detection and heating systems for wind turbines is very relevant in cases where the wind turbines are planned to be placed close to urban areas and highways, where risks need to be considered due to icing events, which may lead to consequences including human fatality, functional disruptions, and/or economic losses. The risk of people being killed in a car passing on highways near a wind turbine due to blades parts or ice pieces being thrown away in cases of overicing is considered in this paper. The probability of being killed per kilometer and per year is considered for three cases: blade parts thrown away as a result of a partial or total failure of a blade, ice thrown away in two cases, i.e., of stopped wind turbines and of wind turbines in operation. Risks due to blade parts being thrown away cannot be avoided, since low strengths of material, maintenance or manufacturing errors, mechanical or electrical failures may result in failure of a blade or blade part. The blade (parts) thrown away from wind turbines in operation imply possible consequences/fatalities for people near the wind turbines, including in areas close to highways.
Similar consequences are relevant for ice being thrown away from wind turbine blades during icing situations. In this paper, we examine the question as to whether it is valuable to put a heating System on the blades in addition to ice detection systems. This is especially interesting in countries with limited space for placing wind turbines; in addition, it is considered if higher power production can be obtained due to less downtime if a heating system is installed.