Understanding the mechanical behaviour of fuel cladding is decisive for an extended dry interim storage period beyond the currently licensed period of 40 years in Germany and subsequent handling, transport, and disposal considering normal and accidental conditions. Since fuel cladding acts as the first barrier for spent fuel, its integrity should be demonstrated to enable safe and secure discharge and handling options after interim storage and subsequent transportation in preparation of final disposal. An established method for characterizing cladding material is the Ring Compression Test (RCT), where a small, cylindrical sample of the cladding tube is subjected to a compressive load. This test is a laboratory representation of a fuel rod load case and has shown a high susceptibility to failure under the occurrence of radial hydrides. Certain hydride morphologies and low temperature might even lead to brittle fracture at very small loads. The BAM research project BRUZL (Fracture mechanical analysis of spent fuel claddings during long-term dry interim storage) aims to study the results of quasi-static RCTs and to establish numerical models to gain an in-depth understanding of the stress state during the experiments. Using a fracture mechanical approach, cases of sudden failure during the RCT procedure are used to characterize the material behaviour and establish a failure criterion. As an integral part of the project BRUZL, quasi-static Ring Compression Tests have been performed to identify all experimental details, which might be helpful for numerical modelling. Unirradiated samples of the cladding material ZIRLO® have been subjected to hydrogen charging and a thermo-mechanical treatment for radial hydride reorientation. Sample preparation, testing procedures, and analysis results are presented. A numerical model has been established and an elastic-plastic material model was derived from as-received RCT samples by inverse finite element analyses. Cohesive zone modelling has been implemented to reproduce sudden load drops during RCT. The project is funded by the Federal Ministry for Economic Affairs and Energy (BMWi) under contract no. 1501561.
The evaluation of cladding integrity is a major issue to be demonstrated in Germany for extended interim storage periods up to 100 years and subsequent transportation considering operational and accidental conditions with respect to reactor operation, cask drying and dry interim storage. The chemical reaction between the zirconium fuel cladding and the cooling water in water-cooled reactors produces hydrogen and zirconium oxide. Hydrogen diffuses into the cladding and precipitates as zirconium hydrides when the solubility limit is reached, preferably oriented in hoop direction. At high temperatures during vacuum drying procedures, the hydrides can dissolve. Over a succeeding period of slow cooling with existing hoop stress the hydrides precipitate again, but partly reoriented along the radial direction of the cladding. This change of microstructure in combination with a decreasing temperature (0.5...2 K/year) during (extended) interim storage and additional mechanical load by handling procedures or under accident conditions could lead to a potential cladding embrittlement and consequently increased failure probability. The current research project BRUZL (Fracture mechanical analysis of spent fuel claddings under long-term dry interim storage conditions) has been launched by BAM to investigate potential sudden brittle failure of spent fuel claddings at small deformation under long-term dry interim storage conditions and is presented.
The current research project BRUZL (Fracture mechanical analysis of spent fuel claddings during long-term dry interim storage) is presented. General aim of the project is the development of methods for risk assessment and identification of boundary conditions to prevent potential sudden brittle failure of spent fuel claddings at small deformation during long-term dry interim storage and subsequent transportation. The project is funded by the Federal Ministry for Economic Affairs and Energy (BMWi) under contract no. 1501561.
The evaluation of cladding integrity is a major issue to be demonstrated in Germany for extended interim storage periods up to 100 years and subsequent transportation considering operational and accidental conditions with respect to reactor operation, cask drying and dry interim storage. The chemical reaction between the zirconium fuel cladding and the cooling water in water-cooled reactors produces hydrogen and zirconium oxide. Hydrogen diffuses into the cladding and precipitates as zirconium hydrides when the solubility limit is reached, preferably oriented in hoop direction. At high temperatures during vacuum drying procedures, the hydrides can dissolve. Over a succeeding period of slow cooling with existing hoop stress the hydrides precipitate again, but partly reoriented along the radial direction of the cladding. This change of microstructure in combination with a decreasing temperature (0.5...2 K/year) during (extended) interim storage and additional mechanical load by handling procedures or under accident conditions could lead to a potential cladding embrittlement and consequently increased failure probability. The current research project BRUZL (Fracture mechanical analysis of spent fuel claddings under long-term dry interim storage conditions) has been launched by BAM to investigate potential sudden brittle failure of spent fuel claddings at small deformation under long-term dry interim storage conditions and is presented.
Embrittlement of spent fuel claddings during long-term dry interim storage - Current approach at BAM
(2019)
In this presentation, the actual situation of long-term dry interim storage of spent nuclear fuel in Germany is reported. An extension of the interim storage period between 40 and 100 years for at least a relevant number of casks is foreseeable. To demonstrate the integrity of fuel rods and cladding tubes throughout the extended dry interim storage, a potential cladding embrittlement should be investigated. The current approach at BAM is a research project on experimental and numerical investigations of sudden failure of unirradiated pre-hydrided cladding tubes after hydride reorientation at small deformation under Ring Compression Test conditions. A fracture mechanics based failure analysis and suggested failure criteria for a potential brittle failure of spent fuel claddings after long-term dry interim storage under mechanical loads are discussed.
In this presentation, the history and actual situation of the German nuclear waste management policy of spent fuel (SF) and high-level waste (HLW) is reported. Beside the description of the restructuration of responsible authorities and organizations in Germany, the principle of dry interim storage of SF and HLW in dual purpose casks is explained. The need for extended interim storage towards disposal implicates additional challenges for the nuclear waste management strategy in Germany. (Extended)interim storage, subsequent transportation, and final disposal are closely linked. Integrated approaches concerning waste package designs and operations are supposed to be beneficial for the establishment of efficient long-term SF and HLW management strategies. Knowledge management and staff recruiting, education and training during phase out and beyond nuclear power plant operation are major issues.