Degradation von Werkstoffen
Filtern
Erscheinungsjahr
- 2021 (5) (entfernen)
Dokumenttyp
- Vortrag (4)
- Beitrag zu einem Tagungsband (1)
Referierte Publikation
- nein (5) (entfernen)
Schlagworte
- Crack closure (1)
- Crack closure effect (1)
- Damage tolerance assessment (1)
- Einflussfaktoren (1)
- Environmental conditions (1)
- Experimental procedure (1)
- Fatigue crack propagation threshold (1)
- Intrinsic fatigue crack propagation threshold (1)
- Intrinsischer Schwellenwert gegen Ermüdungsrissausbreitung (1)
- Residual lifetime (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (4)
The effect of the environmental conditions on the threshold against fatigue crack propagation
(2021)
The threshold against fatigue crack propagation (ΔKth) is a crucial parameter for the damage tolerance assessment of engineering components subjected to cyclic loading and it is composed by two distinct components, one intrinsic, dependent on the elastic material properties and the lattice type, and one extrinsic, related to the occurrence of crack closure effects. An important issue is that several factors can influence ΔKth and, in general, the fatigue crack propagation behavior. In this work, the influence of the experimental procedure, air humidity and test parameters on da/dN-ΔK data has been investigated. Results are discussed with their potential causes and consequences on the calculations of the residual lifetime.
Rissfortschrittsdaten sind notwendig für die bruchmechanische Bewertung zyklisch beanspruchter Bauteile. Deren zuverlässige experimentelle Ermittlung wird von verschiedenen Faktoren beeinflusst, was wiederum zur Unsicherheit bei der Restlebensdauerprognose führen kann. Der Vortrag befasst sich mit der Untersuchung der Einflussfaktoren auf die Ermittlung von Rissfortschrittsdaten. Eine Prozedur zur Berechnung der Restlebensdauer wird eingeführt, die auf rissschließfrei Rissfortschrittsdaten basiert.
The correct determination of fatigue crack propagation data is of great importance for the damage tolerance design of engineering components, especially with regard to the calculation of residual lifetime and the establishment of inspection intervals. The fatigue crack propagation threshold Δ𝐾th, in this respect, is a crucial input parameter for simulating crack growth, since it corresponds to the stress intensity factor range at which a non-growing crack starts to propagate. However, the experimental determination of Δ𝐾th, as well as its application, is still confronted with few issues related among others to the load ratio (R) dependency of Δ𝐾th, the testing procedure, and environmental effects. These can lead to large scatter and significant errors in the prediction of component failure. In this context, the use of the intrinsic fatigue crack propagation threshold Δ𝐾th,eff in component assessment is a promising alternative, since it does not depend on a number of factors that affect Δ𝐾th, but only on the elastic properties (𝐸-modulus) and the lattice (Burger’s vector ‖𝑏‖) of the material. The aim of the present work is therefore to investigate different experimental procedures for the determination of Δ𝐾th,eff, namely: (a) conventional load reduction (LR) procedures, (b) the 𝐾max procedure and (c) compression pre-cracking load reduction and constant amplitude (respectively CPLR and CPCA) methods. Furthermore, the determination of Δ𝐾th has been carried out varying some testing parameters, such as test frequency, Δ𝐾 at the beginning of the crack propagation test (Δ𝐾0) and stress ratio (R). The results are statistically analyzed and a discussion about the use of Δ𝐾th and Δ𝐾th,eff for the component fatigue assessment is presented.
Für die Bestimmung der Restlebensdauer zyklisch beanspruchter Bauteile kommt dem Schwellenwert für Ermüdungsrissausbreitung, Δ𝐾𝑡ℎ, und dem sich anschließenden Schwellenwertbereich der 𝑑𝑎𝑑𝑁⁄−Δ𝐾-Kurve große Bedeutung zu. Dem stehen Unsicherheiten bei der Bestimmung und Analyse gegenüber. Der Aufsatz befasst sich mit der Ermittlung des sogenannten intrinsischen Schwellenwerts, der als robuster Eingangsparameter für eine „rissschließfreie“ Analyse der Restlebensdauer von entscheidender Bedeutung ist.
Für die Bestimmung der Restlebensdauer zyklisch beanspruchter Bauteile kommt dem Schwellenwert für Ermüdungsrissausbreitung, Δ𝐾𝑡ℎ, und dem sich anschließenden Schwellenwertbereich der 𝑑𝑎𝑑𝑁⁄−Δ𝐾-Kurve große Bedeutung zu. Dem stehen Unsicherheiten bei der Bestimmung und Analyse gegenüber. Der Aufsatz befasst sich mit der Ermittlung des sogenannten intrinsischen Schwellenwerts, der als robuster Eingangsparameter für eine „rissschließfreie“ Analyse der Restlebensdauer von entscheidender Bedeutung ist.