A few layer/multilayer graphene (MLG) with a specific surface area of BET=250 m2/g is proposed as an efficient multifunctional nanofiller for rubbers. The preparation method, i.e., ultrasonically-assisted solution mixing of master batches followed by two-roll milling, strongly influences the dispersion in the elastomeric matrix and is fundamental for the final properties. When homogenously dispersed, single stacks of only approximately 10 graphene sheets, with an aspect ratio of 34, work at low loadings, enabling the replacement of large amounts of carbon black (CB), an increase in efficiency, and a reduction in filler load. The appropriate preparation yielded nanocomposites in which just 3 phr are sufficient to significantly improve the rheological, curing, gas barrier properties, electrical and thermal conductivity, as well as mechanical properties of different rubbers, as shown for chlorine-Isobutylene-Isoprene rubber (CIIR), nitrile-butadiene rubber (NBR), natural rubber (NR), and styrene-butadiene rubber (SBR). 3 phr of MLG tripled the Young’s modulus of CIIR, an effect equivalent to 20 phr of CB. The stronger interactions between MLG and NR or SBR also resulted in a reduction in the elongation at break by 20% and 50%, respectively, while the same parameter was hardly changed for CIIR/MLG and NBR/MLG. CIIR/MLG and NBR/MLG were stiffer but just as defomable than CIIR and NBR. The strong reinforcing effect of 3 phr MLG was confirmed by the increase of greater than 10 Shore A in hardness. MLG reduces gas permeability, increases thermal and electrical conductivities, and retards flammability, the latter shown by the reduction in heat release rate in the cone calorimeter. We investigated MLG also as a synergist for reducing the aluminium trihydrate loading in flame retardant hydrogenated acrylonitrile-butadiene (HNBR), polybutadiene chloroprene (BR/CR), and chlorosulfonated polyethylene rubber(CSM). The higher the nanofiller concentration is, the greater the improvement in the properties. For instance, the permeability decreased by 30% at 3 phr of MLG, 50% at 5 phr and 60% at 10 phr, respectively. Moreover, the MLG nanocomposites improve stability of mechanical properties against the effects of weathering. In key experiments an increase in UV-absorption and a pronounced radical scavenging were proved as stabilizing mechanisms. In a nutshell, MLG is an efficient multifunctional nanofiller ready to be used for innovative rubber development.
Elastomers, such as hydrogenated acrylonitrile-butadiene rubber (HNBR) are usually mechanically reinforced with high loadings of carbon black (CB) to achieve the properties demanded; high amounts of mineral flame retardants are used to fulfill fire safety requirements. These high filler loadings sometimes cause deterioration of the physical properties of the material. In this study, multilayer graphene (MLG), a nanoparticle made of only 10 graphene sheets, is applied in low loadings (3 phr) to reduce the total amount of filler or boost performance.1,2,3 In former studies nanofiller achieved increased flame retardancy at very low lowdings.4,5,6 The dispersion of the nanofiller is essential for the properties of the nanocomposites.7 The nanocomposites were prepared via master batch by an ultrasonically assisted solution mixing and subsequent conventional two-roll milling.
SEM and TEM micrographs and rheological measurements revealed that the MLG nanoparticles were well dispersed in the HNBR matrix. In the HNBR nanocomposites, 3 phr MLG replaced 15 phr CB, 3 phr ATH or 15 phr CB + 3 phr ATH and achieved large consistent improvement in curing, rheological and mechanical properties of the HNBR. The nanocomposites with partial replaced CB reduced the filler loading up to 60% without any deterioration of the properties. The HNBR/MLG nanocomposites achieved an even higher Young’s modulus, hardness and thermal conductivity. MLG achieved advanced flame retardancy by improving the protection layer. The layer is created during the burning phase and acted as an afterglow suppressor. This study proposed the combination of ATH with MLG as a promising approach to reduce the amount of filler, in addition to improving the mechanical properties and fire performance of HNBR rubbers.