The relevance of chloride measurements in practice for durability condition assessment and a description of the working principle of LIBS will be given. A comparison of chloride profiles obtained by the common wet chemical analysis and results from LIBS measurements are shown to demonstrate the accuracy of the LIBS-technique. In addition, an example on the extra information resulting from measurements performed with LIBS for improvement of condition assessment and prediction will be shown.
For the determination of the remaining life-time and the degree of damage of reinforced concrete structures such as marine construction, bridges or parking decks, a highly precise measurement of harmful species is also required for trace elements. One of the most interesting elements is chlorine, because above a certain threshold corrosion is triggered. To increase the intensity of the chlorine line, helium is usually used, which is costly. To overcome this problem, low electrical discharge reheating is used which operates in air atmosphere. A comparison between results obtained by measuring with helium and reheating by electrical discharge is presented. The performance is compared by the resulting calibration curves and the calculated limit of detection obtained by 15 reference samples based on cement with NaCl. Concentrations of reference samples range from 0.05 to 2.5 wt% chlorine.
In civil engineering, the laser-induced breakdown spectroscopy has been applied as a fast and reliable method for a quantitative evaluation of concrete cores. Due to a two-dimensional scanning, the heterogeneity of concrete can be evaluated and elements like Cl, Na, and S are related to the cement matrix only. This study deals with the temporal evaluation and imaging of laser-induced plasmas on cement-based materials, in order to investigate the impact of aggregates with diffrent grain size on the spectral response in LIBS.
Two calibration-free LIBS techniques are used for the quantitative analysis of synthetic cement samples: the CF-LIBS based on the Boltzmann plot method and the Monte Carlo (MC) LIBS based on the iterative spectrum fitting. In CF-LIBS, the inverse problem is solved, i.e. the elemental concentrations are determined by the reconstruction of plasma parameters from spectra. The MC-LIBS technique solves the direct problem by finding the highest correlation between the model-generated and experimental spectrum. The accuracy of both calibration-free LIBS methods suffers from factors such as inaccurately determined instrumental function, the deviation of experimental plasma from the mathematical model used, not taking into account the collection geometry and from the uncertainty of spectroscopic data. Therefore, the both calibration-free LIBS approaches are applied to synthetic spectra which perfectly suit the mathematical model of the method. This test yields the accuracy of both the approaches for the ideal case. In addition, the accuracy of both methods is investigated for non-isothermal plasma, because real laser-induced plasma often has high gradients in temperature. Both methods assume an isothermal plasma.
Die Laserinduzierte Plasmaspektroskopie (engl.: Laser-induced Breakdown Spectroscopy, kurz: LIBS) ist eine Kombination aus Laserablation mittels eines energiereichen Laser-Pulses, der Erzeugung eines Plasmas auf der zu untersuchenden Oberfläche und dem quantitativen Nachweis der Elementzusammensetzung durch spektroskopische Untersuchung der vom Plasma emittierten Strahlung. Ein LIBS-Gerät liefert dem sachkundigen Planer Daten für die Bewertung des Ist-Zustandes von Bauwerken unserer Infrastruktur durch die zweidimensionale Erfassung von Elementverteilungen. Typische Anwendungen sind die Erfassung von Chlor, Schwefel, Kohlenstoff, Natrium, Kalium und Lithium in Beton oder als – Qualitätssicherung – der Nachweis der mit einem Marker versehenen Tiefenhydrophobierung.
In Zusammenarbeit zwischen Industriepartnern und der BAM wurden ein Labor und ein mobiles LIBS-System für die Vor-Ort-Messungen entwickelt. Die Analyse erfolgt vollautomatisch. Die Ortsauflösung beträgt bis zu 0,1 mm x 0,1 mm. Es können Messflächen von 140 mm x 170 mm gescannt werden. Die Erstellung von 2D-Elementverteilungen im Beispiel unten benötigt weniger als 10 Minuten.
Detection of ion ingress by LIBS for Evaluation of the remaining lifetime of a concrete structure
(2018)
The majority of the built infrastructure is made of concrete, which is a multiphase system made of cement, aggregates, water and pores. Concrete is often used in combination with steel as reinforced concrete. Environmental influences, especially the ingress of harmful ions in combination with the ingress of water, trigger different damage processes which reduce the designed lifetime of a structure. The ingress of chlorides from de-icing salt or sea water leads to corrosion of the reinforcement. Also the carbonation of the concrete may trigger the corrosion of the reinforcement. The ingress of alkalis from de-icing salts may cause the expansion of the amorphous silica aggregates (alkali-silica reaction) through formation of a swelling gel of calcium silicate hydrate if water is present. The ingress of sulfates may cause spalling of the concrete surface due to ettringite formation.
For the standard procedure in civil engineering cores are taken, cut in slices, grinded and the obtained homogenized powder is solved in acid and investigated by standard procedures.
BAM has developed the LIBS technique for the 2D evaluation of the chemical composition of concrete [1-11]. The technique is established for automated laboratory use with high numbers of samples to investigate transport processes of harmful species (Cl-, CO2, SO42- and alkalis) in concrete. Information about ingress depth and the quantitative values are important to estimate the remaining lifetime of the infrastructure. LIBS is a surface technique. To get information about the ingress depth, a core has to be taken and cut in the middle. The measurements are carried out at the cross section. The main advantages of LIBS are the direct measurement on the surface of the concrete, fast analysis (sample rate 100 Hz) with a spatial resolution of up to 100 µm, the consideration of the heterogeneity of the concrete and the possibility of automated measurements which save a lot of manpower and time. As an example the investigation of ingress profiles for standard diffusion and migration tests in civil engineering takes hours in comparison to just a few minutes using LIBS. At the same time a 2D-evaluation provides information about hot spots of elemental concentration which may not be found by standard methods.
Ingress of chlorides due to a crack in a repair mortar. Left: Photo of the cross section of a concrete core and the surface investigated by LIBS (area 70 mm x 70 mm). Right: Color coded chlorine intensity on the cross section of a concrete core, dark red represents high chlorine content.
The state of the art of LIBS technique for applications in civil engineering will be presented, including typical results of 2D investigation of concrete in laboratory. The performance is also demonstrated by examples for onsite applications using a mobile LIBS system. The road map to standardization is presented as well.
Quantitative on-site analysis of harmful elements in building structures with a mobile LIBS-System
(2018)
Environmental influences and damage processes drastically reduce the durability of concrete and reinforced concrete structures. Much of this damage can be traced back to the penetration of harmful elements into the concrete. These elements cause damage processes such as the chlorine-induced corrosion, the alkali-silica reaction or the carbonization. For the maintenance the knowledge of the element concentration and the penetration depth of these harmful elements is essential. Based on this data, a maintenance concept can be developed and an estimation of the remaining service life-time can be carried out.
Typically, chemical analyzes are used to determine harmful elements in concrete, which are costly and time consuming. As an alternative method LIBS is used. On-site measurements were carried out with a mobile LIBS-System to determine harmful elements in a parking garage. A scanner is used to obtain a two-dimensional element mapping. For the quantitative analysis, a calibration of the system is carried out with 15 reference samples based on cement with NaCl with a concentration range of chlorine of 0.05 to 2.5 wt.%. To determine the penetration profile of the harmful element chlorine, concrete cores were drilled, split and analyzed directly on-site.
The durability and the lifetime of reinforced concrete structures can be drastically reduced by the influence of damage processes. One of the most common causes is chloride-induced corrosion, which is triggered by increased chloride content near the reinforcement. In a study, the chloride content should be determined directly at corrosion areas. The LIBS system used consists of a micro-chip laser (3 mJ, 100 Hz, 1.5ins) and two compact spectrometers covering the wavelength range of 177-355 nm (UV) and 750-940 nm (NIR). The analysis of the chloride content was carried out via the atomic chlorine spectral line 837.59 nm, using helium for signal amplification. Calibrations were carried out for quantitative chlorine measurements with 15 reference samples in the working range of 0.05 to 6.00 wt% chlorine. The calibration of the LIBS system was done according to DIN 32 645 and was tested for linearity. The determination of the quantitative chlorine contents was carried out on samples which were broken and thus have a high surface roughness. This requires real time correction of the focus point to compensate for the roughness of the samples. The poster shows spatially resolved element distributions and determined quantitative chloride concentrations near the corrosion Areas.
19th and 20th centuries glass paint layers consist of a colour body and a colourless lead silicate flux, in which borax or boric acid was added as further component to improve the paint ability and to reduce the firing temperature for multiple layers of paint. Model glasses were used in laboratory tests to investigate the stability of glass paints with additions of boron oxide. To determine boron in paint layers, a LIBS-system with pulsed NdYAG-laser was used.
In civil engineering, the investigation of existing infrastructure is of major importance for maintaining and ensuring stability of the structures. To ensure durability, uniform regulations and standards apply e.g. the European standard EN 206-1. In some countries, the EN-standard is supplemented by additional standards, as in Germany with DIN 1045-2. Here, specific application rules are described, e.g. for the cement type, to ensure the resistant to different exposures. Therefore, the knowledge of the materials originally used is important in assessing the condition of existing concrete structure. Unfortunately, these are often unknown and must be determined retrospectively. Therefore, we present the application of the laser-induced breakdown spectroscopy to distinguish between different types of cement. Spectral information’s are used to build a classification model. First, the accuracy of the classification is analyzed on ten pure laboratory cement samples. To investigate possible sources of error, the model was then applied to cement samples with different moisture content. The study shows that LIBS is a promising tool for distinguishing between cement types. For further industrial application, however, factors influencing the LIBS signal must be included to ensure a robust model.