A particle roughness analysis tool, based on electron microscopy (EM) images. The influence of various parameters on the calculated roughness was also investigated: the setting of the proper threshold, accelerating voltage, etc. The samples were gradually tilted to extend imaging information of more than only one projection. Furthermore, the measurement uncertainty of the profile roughness of particles associated to various orientations was estimated.
Welcome to the poster Towards Determination of Surface Roughness from a SEM Image, a contribution from BAM in Berlin, Germany. This work is part of the MamaLoCA project, which aims to develop a biosensor for the detection of mycotoxins in cereals. Biosensors come in a great variety, one of which makes use of microscopic beads produced by homogenous coating of polystyrene microspheres. The beads are functionalized by decorating them with bioreceptors – in our case antibodies – which then specifically react with the analyte – in our case mycotoxins – and emit an electrical or optical signal. The functionalization of the beads depends on the surface roughness because this determines the amount and orientation of binders. In other words, the surface roughness affects the accessibility to the binding sites and influences device sensitivity, hence its quantitative determination is an important step in evaluating the quality of the biosensor in general.
The presented solution to the problem of the estimation of surface roughness relies in the repetitive characteristics on the surface of the beads. A SEM image of the bead shows a raspberry like microparticle with a variation of grayscale values, which arise from the secondary electron yield. The principle of the measurement measures the variation of grayscale values along a circumference of a circle centred in the centre of the particle and with an arbitrary radius. The grayscale value variation along the given circumference gives the so-called z-modulation or the lateral profile. By performing Fast Fourier Transform on this profile we obtain the power spectrum as a function of the spatial frequencies through which the grayscales vary. The maximal value for spatial frequency then reveals the most common feature along one given circumference. Surface roughness then is the feature frequency in the spatial domain. This calculation is repeated for several concentric circles with different radii over the particle.
The results for the same particle but recorded at two different accelerating voltages show that the applied method has a potential to reveal the roughness. Interpretation of results from an SE InLens SEM image obtained using 3 kV shows that surface roughness is about 21 nm, which is in a good agreement with an alternative method given in a different presentation. The results from the 10 kV are underestimated due to the loss of surface sensitivity on the SE InLens detection at high voltages.
In conclusion, this method shows promise in determining quantitatively the surface roughness from a single SEM image and its validation is being sought using 3D SEM images and AFM methods.
A particle roughness analysis tool, based on electron microscopy images (SEM and TEM). The influence of various parameters on the calculated roughness was also investigated: the setting of the proper threshold, accelerating voltage, etc. The samples were gradually tilted to extend imaging information of more than only one projection. Furthermore, the measurement uncertainty of the profile roughness of particles associated to various orientations was estimated.
CS particles show unique properties by merging individual characteristics of the core and the shell materials. An alteration particularly in their surface roughness affects the final performance of the particles in the targeted application. Quantitative evaluation of the roughness of CS microparticles is, however, a challenging task employing microscopic techniques being scarce and showing large differences in terms of methodology and results.
In our previous work, we have reported a systematic study with a reliable analysis tool, which evaluates profile roughness quantitatively, for individual core-shell microparticles using electron microscopy (EM) images of both types, Scanning Electron Microscopy (SEM) and transmission mode SEM (or TSEM). The SEM images contain two-dimensional (2D) information, therefore, provide profile roughness data only from the projection in the horizontal plane (in other words, from the “belly”) of a spherical particle. The present study offers a practical procedure to give access to more information by tilting the sample holder and hence allowing images of a single particle to be recorded at different orientations under the same view angle. From the analysis of these images, extended information on surface roughness of the particle can be extracted. Thus, instead of obtaining 2D information from a single SEM image, three-dimensional (3D) information is obtained from 2D projections recorded at different particle orientations.