The hydrogen permeation current increase was noticed for carbon steel in 0.5 mol/L NaCl solution under strong anodic potentials, which is contrary to the common understanding. Hydrogen permeation under cathodic potentials has been widely studied because of possible hydrogen embrittlement failures of high strength steels in seawater, but investigations of anodic polarization on hydrogen permeation are fairly rare, as the hydrogen evolution reaction shall be retarded. To corroborate the observed phenomenon, experiments were conducted using both as-received and vacuum-annealed sheet specimens. It was verified that the observed phenomena originated from the released hydrogen in traps by metal dissolution under anodic polarization.
The feasibility of microbial hydrogen consumption to mitigate the hydrogen embrittlement (HE) under different cathodic potentials was evaluated using the Devanathan-Stachurski electrochemical test and the hydrogen permeation efficiency h. The hydrogen permeation efficiency h in the presence of strain GA-1 was lower than that in sterile medium. The cathodic potential inhibited the adherence of strain GA-1 to AISI 4135 steel surface, thereby reducing the hydrogen consumption of strain GA-1. The adherent GA-1 cells were capable of consuming ‘cathodic hydrogen’ and reducing the proportions of absorbed hydrogen, indicating that it is theoretically possible to control HE by hydrogen-consuming microbes.