In this study, the feasibility of using non-contact Infrared thermography as a potential tool to monitor the CMT welding process is explored. The presence of internal defects such as porosity, lack of filler material deposition and formation of improper weld bead produce perturbations in the surface temperature which can be identified using an Infrared thermography technique. We present recent results obtained from online monitoring of the the dissimilar joining using CMT weld brazing of Aluminum and Steel using a transmission mode measurement approach. The effect of loss of zinc coating on the weldability of the cold metal transfer joining of aluminum to galvanised steel was investigated. A correlation between measured online thermal indications with the weld anomalies is successfully attempted and the results are compared with the conventional post-weld NDT inspection methods.
Online (passive) thermographic inspection of overlap joints of aluminium and zinc coated steel sheets made by cold metal Transfer weld brazing process was explored. Different experimental Trials were conducted for demonstrating the feasibility of thermographic inspection to detect the porosities, improper weld bead and to differentiate the pre weld temperature. The whole process was monitored using infrared cameras in different wavelength region.
Image analysis algorithms were developed to reconstruct the thermal images that contain the signatures of the weld defects and to extract the pre weld temperature and ist evolution with distance from the centre of the weld torch. Post-weld radiography lends strong Support to the observations.
Crack detection in steel bars at high surface temperatures is a critical problem in any manufacturing industry. Surface breaking cracks are the major problems during the billet casting. Many NDT techniques are proven its capability in crack detection at room temperature. Here, we are demonstrating the possibility of exposure of cracks using laser line thermography at higher surface temperatures (up to 600 °C). A continuous-wave (CW) laser is used to excite the sample kept at higher surface temperatures. The temperature distribution over the sample due to the laser line scanning is captured using a temperature calibrated infrared (IR) thermal camera. The response of the sample temperature in crack detection is investigated using a validated FE model. The impact of the oxide layer in crack detection is investigated by using two types of samples; one without any oxide layer and the second is with the oxide layer. The influence of laser power in the detection of defects at high temperatures is studied. 3D numerical models were developed for the cases; when the sample is with oxide layer and without any oxide layer for a better understanding of physics. The surface temperature rise due to laser heating is higher for the scaled sample compared to the no-scale sample. The presence of the oxide layer above the parent metal will reduce the reflectivity of the surface. Lower reflectivity will lead to increased absorption of incident energy so that the surface temperature rise will be higher than the surface with no scale. Thermal contrast linearly depends on laser power, which means higher laser power will increase the defect detectability even at a higher surface temperature.