Conventional simultaneous thermal analysis, capillary-coupled TGMS, in situ and ex situ Raman and Mössbauer spectroscopy, as well as chemical analysis have been used for the investigation of the first decomposition step of the mixed valence chloroferrate (dmpipzH2)6[Fe(II)Cl4]2[Fe(III)Cl4]2[Fe(II)Cl5][Fe(III)Cl6]. Under argon at ca. 200°C, an almost complete reduction proceeds in a solid state reaction forming Fe(II). It is accompanied by the release of HCl and, to a minor degree, carbon containing species. A multi-phase product with at least two chloroferrate species, coke, and C,H,N-containing polymers is formed. Binuclear iron complexes, such as (dmpipzH)2[Fe(II)2Cl6], and small amounts of (dmpipzH)[Fe(III)Cl4] have been proposed to be the major and minor component of the product mixture, respectively.
While calcined clays in general have been credited with a great potential to mitigate CO2 emissions related to cement production and consumption, calcined brick clays are currently understudied in this regard. In the present work, two brick clays, a low-grade kaolinitic clay, and a mixed clay composed of 50% brick clay and 50% low-grade kaolinitic clay were studied regarding transformations on calcination, and strength and durability performance as well as pore structure of mortars made with the blended cements. All calcined clays exhibited pozzolanic reactivity, with the performance of the brick clays inferior to the low-grade kaolinitic clay. However, the mixed clay performed very similar to the low-grade kaolinitic clay, which points to a viable option for optimal use of brick clays in cementitious systems. The carbonation resistance of the blended cement mortars was generally worse than that of the plain Portland cement mortar, as expected, but the former exhibited a significantly improved chloride penetration resistance. The latter improvement was due to pore structure refinement in the blended cement mortars, compared to the Portland cement mortar.
We present a versatile and simple method using electrochemistry for the exclusive functionalization of the edge of a graphene monolayer with metal nanoparticles or polymeric amino groups. The attachment of metal nanoparticles allows us to exploit surface-enhanced Raman scattering to characterize the chemistry of both the pristine and the functionalized graphene edge. For the pristine patterned graphene edge, we observe the typical edge-related modes, while for the functionalized graphene edge we identify the chemical structure of the functional layer by vibrational fingerprinting. The ability to obtain single selectively functionalized graphene edges routinely on an insulating substrate opens an avenue for exploring the effect of edge chemistry on graphene properties systematically.