Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (65)
- Beitrag zu einem Tagungsband (5)
- Beitrag zu einem Sammelband (4)
- Handbuch (2)
- Forschungsbericht (2)
- Sonstiges (1)
Schlagworte
- XPS (6)
- Crystal structure (5)
- Nanoparticles (5)
- Rhenium (4)
- Raman spectroscopy (3)
- AIN (2)
- Additive manufacturing (2)
- Atomic force microscopy (2)
- BSA (2)
- Chelates (2)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (3)
- 1 Analytische Chemie; Referenzmaterialien (2)
- 6 Materialchemie (2)
- 6.1 Oberflächen- und Dünnschichtanalyse (2)
- 8.5 Röntgenbildgebung (2)
- 9 Komponentensicherheit (2)
- 9.4 Integrität von Schweißverbindungen (2)
- 1.1 Anorganische Spurenanalytik (1)
- 1.2 Biophotonik (1)
- 5 Werkstofftechnik (1)
We report the results of a Versailles Project on Advanced Materials and Standards (VAMAS) interlaboratory study on the measurement of the shell thickness and chemistry of nanoparticle coatings. Peptide-coated gold particles were supplied to laboratories in two forms: a colloidal suspension in pure water and particles dried onto a silicon wafer. Participants prepared and analyzed these samples using either X-ray photoelectron spectroscopy (XPS) or low energy ion scattering (LEIS). Careful data analysis revealed some significant sources of discrepancy, particularly for XPS. Degradation during transportation, storage, or sample preparation resulted in a variability in thickness of 53%. The calculation method chosen by XPS participants contributed a variability of 67%. However, variability of 12% was achieved for the samples deposited using a single method and by choosing photoelectron peaks that were not adversely affected by instrumental transmission effects. The study identified a need for more consistency in instrumental transmission functions and relative sensitivity factors since this contributed a variability of 33%. The results from the LEIS participants were more consistent, with variability of less than 10% in thickness, and this is mostly due to a common method of data analysis. The calculation was performed using a model developed for uniform, flat films, and some participants employed a correction factor to account for the sample geometry, which appears warranted based upon a simulation of LEIS data from one of the participants and comparison to the XPS results.
The primary crystallite size of titania powder relates to its properties in a number of applications. Transmission electron microscopy was used in this interlaboratory comparison (ILC) to measure primary crystallite size and shape distributions for a commercial aggregated titania powder. Data of four size descriptors and two shape descriptors were evaluated across nine laboratories. Data repeatability and reproducibility was evaluated by analysis of variance. One-third of the laboratory pairs had similar size descriptor data, but 83% of the pairs had similar aspect ratio data. Scale descriptor distributions were generally unimodal and were well-described by lognormal reference models. Shape descriptor distributions were multi-modal but data visualization plots demonstrated that the Weibull distribution was preferred to the normal distribution. For the equivalent circular diameter size descriptor, measurement uncertainties of the lognormal distribution scale and width parameters were 9.5% and 22%, respectively. For the aspect ratio shape descriptor, the measurement uncertainties of the Weibull distribution scale and width parameters were 7.0% and 26%, respectively. Both measurement uncertainty estimates and data visualizations should be used to analyze size and shape distributions of particles on the nanoscale.
Results are reported from a pilot study under the Consultative Committee for Amount of Substance (CCQM) to compare measurements of and resolve any relevant measurement issues in, the amount of thermal SiO2 oxide on (100) and (111) orientation Si wafer substrates in the thickness range 1.5 - 8 nm. As a result of the invitation to participate in this activity, 45 sets of measurements have been made in different laboratories using 10 analytical methods: medium-energy ion scattering spectrometry (MEIS), nuclear reaction analysis (NRA), RBS, elastic backscattering spectrometry (EBS), XPS, SIMS, ellipsometry, grazing-incidence x-ray reflectrometry (GIXRR), neutron reflectometry and transmission electron microscopy (TEM). The measurements are made on separate sets of 10 carefully prepared samples, all of which have been characterised by a combination of ellipsometry and XPS using carefully established reference conditions and reference parameters.
The results have been assessed against the National Physical Laboratory (NPL) data and all show excellent linearity. The remaining data sets correlate with the NPL data with average root-mean-square scatters of 0.15 nm, half being better than 0.1 nm and a few at or better than 0.05 nm. Each set of data allows a relative scaling constant and a zero thickness offset to be determined. Each method has an inherent zero thickness offset between 0 nm and 1 nm and it is these offsets, measured here for the first time, that have caused many problems in the past. There are three basic classes of offset: water and carbonadeous contamination equivalent to ~1 nm as seen by ellipsometry; adsorbed oxygen mainly from water at an equivalent thickness of 0.5 nm as seen by MEIS, NRA, RBS and possibly GIXRR; and no offset as seen by XPS using the Si 2p peaks. Each technique has a different uncertainty for the scaling constant and consistent results have been achieved. X-Ray photoelectron spectroscopy has large uncertainties for the scaling constant but a high precision and, critically, if used correctly, has zero offset. Thus, a combination of XPS and the other methods allows the XPS scaling constant to be determined with low uncertainty, traceable via the other methods. XPS laboratories returning results early were invited to test a new reference procedure. All showed very significant improvements. The reference attenuation lengths thus need scaling by 0.986 ± 0.009 (at an expansion factor of 2) deduced from the data for the other methods. Several other methods have small offsets and, to the extent that these can be shown to be constant or measurable, then these methods will also show low uncertainty. Recommendations are provided for parameters for XPS, MEIS, RBS and NRA to improve their accuracy.
Our group previously synthesized 99mTc-labeled fatty acids suitable for myocardial metabolism and flow imaging. In this set of experiments, 29 new analogues were synthesized according to the 4 + 1 mixed ligand approach with some specific differences. Conventional 4 + 1 99mTc-fatty acids are built in the sequence: Tc-chelate, alkyl chain, and carboxylic group. We developed compounds following a new design with the sequence: carboxylic group, alkyl chain, Tc-chelate, and lipophilic tail. Therefore, the 99mTc-chelate was transferred to a more central position of the compound, aiming toward an improved myocardial profile and an accelerated liver clearance. In this context, several functional groups incorporated in the lipophilic tail section were tested to evaluate their influence on the compound's character. In addition to biodistribution studies in vivo, the myocardial first-pass extraction of the compounds was tested in an isolated Langendorff rat heart model. A satisfactory myocardial uptake of up to 20% of the injected dose (% ID) in the perfused heart and a fast liver clearance in vivo with only 0.29% ID/g at 60 min postinjection demonstrate that the induced molecular modifications affect the kinetics of 99mTc-radiolabeled fatty acid compounds favorably. From the data set, rules for estimating the biodistribution of fatty acids tracers are deduced.
XTEM and TFXRD investigations of ohmic Ti/Al/Ti/Au/WSiN contacts on AlGaN/GaN HFET layer systems
(2002)
The microstructural features of the high-temperature-stable ohmic contact system Ti/Al/Ti/Au/WSiN on AlGaN/GaN were investigated using analytical transmission electron microscopy and thin film x-ray diffraction. For two typical rapid thermal annealing steps at 750 °C (non-ohmic behaviour) and 850 °C (ohmic behaviour) the intermetallic phases at the metal-semiconductor interface are presented. Increased annealing leads to the transformation of an Al2Au-AlAuTi phase mixture to a mixture of Al2Au-Al3Au8 phases and the formation of Ti-Al-nitride layers at the interfaces. In light of these results the electrical contact properties are discussed.
Recent progress in the development of A1GaN/GaN heterostructure field effect transistors (HFETs) Shows the great potential towards high temperature / high power electronics. Nevertheless investigations on reliability properties of GaN-based devices are still at the beginning. The frequently used Ti/A1 based ohmic and Pt based Schottky contacts suffer from strong Degradation after aging at elevated temperatures. Therefore new contact systems have to be employed. Concerning the source and drain metallization we used an amorphous WSiN barrier layer as applied for GaAs on top of the Ti/Al-based ohmic contact. This technique significantly reduces the in-diffusion of the Au-containing overlayer, furthermore the barrier layer guaranties smooth contact morphology after RTA and aging, respectively. For the Schottky metallization the Ir/Au system was used. Reliability studies performed on HFET devices containing refractory Ti/A1/Ti/Au/WSiN ohmic and Ir/Au Schottky contacts demonstrate stable conditions during 120h aging at 500°C.
XTEM and TFXRD investigations of ohmic Ti/Al/Ti/Au/WSiN contacts on AlGaN/GaN HFET layer systems
(2002)
The microstructural features of the high-temperature-stable ohmic contact system Ti/Al/Ti/Au/WSiN on AlGaN/GaN were investigated using analytical transmission electron microscopy and thin film x-ray diffraction.
For two typical rapid thermal annealing steps at 750 ◦C (non-ohmic behaviour) and 850 ◦C (ohmic behaviour) the intermetallic phases at the metal–semiconductor interface are presented. Increased annealing leads to the transformation of an Al2Au-AlAuTi phase mixture to a mixture of Al2Au-Al3Au8 phases and the formation of Ti-Al-nitride layers at the interfaces. In light of these results the electrical contact properties are discussed.