During the past 20 years, innovative developments in concrete technology have enabled the production of ultra-high performance fibre reinforced concretes (UHPFC) for the protection and preservation of concrete structures. The main characteristics of UHPFC comprise high compressive and flexural strength as well as high ductility compared to normal strength, normal weight concrete (NSC). This paper focuses on the analysis of crack formation and crack propagation in UHPFC under tensile loading under quasistatic conditions by using acoustic emission (AE) and optical deformation analysis (ODA).
AE is a non-destructive technique to monitor the development of micro structural damage processes caused by external forces. In this context, AE allows for a continuous monitoring of changes in the microstructure (cracks) over time and the corresponding localisation by appropriate algorithms. The AE measurements were performed along with ODA at the surface of the samples in order to analyse the deformation behaviour of the samples and the crack propagation.
For the tests, a UHPFC reference mixture was developed and tested with three different volume percentages of steel fibres (1.0 V.-%, 2.0 V.-%, and 3.0 V.-%). This paper shows that the application of AE is a suitable method to analyse the crack propagation in UHPFC specimens under tensile loading and to localise the crack initiation. Furthermore, insights into the failure mechanism of the fibres are offered by the analysis of the signals of the AE measurements, which allows for a better understanding of UHPFC and its general performance.
Einkomponentige alkaliaktivierte Bindemittel (AAB), d. h. AAB, bei denen der Aktivator als Feststoff im Bindemittel vorliegt, weisen Vorteile hinsichtlich der praktischen Anwendung im Bauwesen gegenüber konventionellen AAB auf. Einkomponentige AAB lassen sich als Gemische aus reaktiver Silica und Natriumaluminat herstellen, wobei die Reaktionsprodukte von der eingesetzten Silica und den Verhältnissen Na2O/Al2O3/SiO2/H2O abhängen: Während Mikrosilica und ähnliche Reststoffe zu zeolithreichen Produkten führen, erhält man aus Reisschalenasche vollständig amorphe Gele (sog. «Geopolymere »). Mörtel auf Basis solcher Bindemittel entsprechen den Anforderungen von DIN 19573:2016-03 hinsichtlich des Widerstands gegen Schwefelsäureangriff (Prüfung bei pH = 1 für 70 d) und sind damit potentiell als Reparatursysteme für Abwasserinfrastruktur geeignet. Untersuchungen mittels 29Si-MAS-NMR und 1H-29Si-Kreuzpolarisations(CP)-MAS-NMR sowie REM-Aufnahmen von erhärteten und dem Schwefelsäureangriff ausgesetzten AAB zeigen, dass der hohe Säurewiderstand v. a. auf die Fällung von Silicagel an der Grenzfläche Mörtel/Säure zurückzuführen ist, wodurch der Korrosionsfortschritt in darunterliegenden Schichten verlangsamt wird.
The production and processing of ordinary Portland cement are responsible for nearly 5% of the world C02 emissions. Due to the world’s increasing requirement for building materials, this air pollution is growing up in the next decades. Alternative cement such as geopolymers can reduce these emissions effectively, Conventional geopolymer binders, produced ffom fly ash or metakaolin as aluminosilicate source and water-glass or alkali hydroxide Solutions as activator, are often used and studied. It is known that under appropriate conditions the starting materials form a three-dimensional aluminosilicate structure and create a gel-like matrix, In our case, a silica source from wastewater treatment of chlorosilane production and solid sodium aluminate as starting materials are initiated to harden by water. This procedure is known as “just add water” or “one-part” geopolymer formulation. These composites have significant advantages for use on construction site, but their Chemical structure is not extensively analyzed. In this work, a well known one-part geopolymer is investigated by 'H and 27A1 magic-angle spinning nuclear magnetic resonance (MAS NMR) spectroscopy. Furthermore, it is shown that overlapping NMR lines can resolved with echo experiments and
The cement and concrete market in East, Central and Southern Africa is highly fragmented. The concrete industry in this area consists of multiple parties, including producers and suppliers of construction materials, formal and informal contractors, engineers and architects, unions of trades persons and workmen, governmental bodies and formal institutions of research and education. All these institutions mostly do not interact adequately, which makes building with cementitious materials susceptible to damage and failures. Completely opposed to the situation in Europe or North America, cement in Africa is often unaffordable, while manpower is cheap, which results in a questionable economisation of cement. Typically, there is not sufficient awareness of methods to sensibly reducing the cement content in concrete or replace Ordinary Portland Cement by adequate alternative materials. Research activities in this field of technology are often missing completely. Only few countries in the area, such as South Africa, are exempted from these issues.
This paper presents the SPIN project, which is a joint project of a consortium of 8 African and 3 European partners within the ACP Science and Technology Programme. The project is funded by the EC and ACP Secretariat is the project body. The main objective of the current project is to strengthen the cement and concrete industry in the East and Central African regions. The project shall generate reasonable solution strategies to implement clean, safe and sustainable cement and concrete technology on the African continent, including general and specific guidelines for sensible application. Furthermore it shall be the kick-off for future projects, research activities and the world-wide expansion of a European-African network.
The paper addresses special problems the cement and concrete market in Eastern, Central and Southern African countries has to face. Several options are presented in detail, which shall help overcoming the current situation. Customized solutions for the African market include rational methods for reducing the amount of cement used and the replacement of Ordinary Portland Cement with cheaper alternatives. The use of recycled concrete through a new and economically effective method, as well as the opportunity of using locally available resources is also discussed.
The high demand for sustainable and durable building materials requires profound knowledge on the material properties. In this respect, the phenomena occurring at nano-level are of crucial importance for the design of new building materials. Therefore, all around the world, increasing amounts of funding are being directed to research projects dealing with material properties on nano-level, which is claimed to have tremendous potential for the future. One of the most referred to and used cementitious nano-material is amorphous silica with a particle size in the nano-range, even though its application and effects on concrete have not been fully understood yet. Olivine (Mg,Fe)2Si04 is the fastest weathering siiicate mineral dissolving easily in acid. Düring dissolution in acid the metallic ions (Mg2+,Fe2+) are replaced by H+, yielding Si(OH)4 monomers and metallic ions in solution. After cleaning treatments an amorphous nano-silica is obtained. The produced olivine nano-silica (OnS) has a specific surface area between 100 and 400 m2/g, the size of the primary particles, which are agglomerated in Clusters, ranges from 10 to 25 nm and the impurity content is below 5 % IV. Literature related with the application of OnS in cement based materials is scarce; only one research work performed by Justnes and Ostnor 121 is available. Thus, the effect of adding OnS in cement based Systems has been not studied. Based on this, the present research aims on elucidating the effects of OnS in the fresh and hardened state of cement pastes and mortars.
Effects of amorphous nano-silica additions on mechanical and durability performance of SCC mixtures
(2012)
In the recent years the application of nanotechnology in building materials has increased
exponentially. One of the most referred and used nano-materials is amorphous silica with
particles size in the nano-range, even though its application and effect in concrete has not been
fully understood yet. It has been reported that nano-silica (nS) addition increases the
compressive strength and reduces the overall permeability of hardened concrete due to the
pozzolanic properties which are resulting in finer hydrated phases (C-S-H gel) and densified
microstructure (nano-filler and anti leaching effects). These effects enhance the durability of
concrete structures such as bridges, quays or off-shore oil facilities in marine environments.
In this study two different types of nano-silica were applied in self-compacting concrete (SCC),
both having similar particle size distributions (PSD) but produced in two different processes
(fumed powder silica and precipitated silica in colloidal suspension). The influence of nanosilica
on SCC was investigated with respect to the properties of concrete in the fresh state
(workability) and hardened state (mechanical properties and durability). Additionally, the
densification of microstructure of the hardened concrete was verified by SEM and EDS analyses.
The obtained results demonstrate that an efficient use of nano-silica in SCC can improve its
mechanical properties and durability. Considering the reactivity of the two nano-silica studied,
colloidal type shown more reactivity at early age, which influenced all the final SCC properties.
Todays superplasticizers for self-compacting concrete and high Performance cementitious materials are very versatile. Typically superplasticizers are composed of a polycarboxylic backbone equipped with polyethylene oxide graft chains of variable length and grafting degree. The mode of operation of these admixtures is based on the steric repulsion of the particles upon adsorption. The adsorption is strongly depending upon the charge density of a superplasticizer and the time dependent Adsorption processes control the retention of the flow performance – an important issue particularly for ready-mix and construction site concrete. However, the properties of polycarboxylic superplasticizers typically remain a black box for users. The paper suggests a simple and rapid test method, which can be conducted without sophisticated equipment, to qualitatively distinguish between two types of superplasticizers based on the adsorption mechanism. Interpreting the results in the right way provides a powerful tool to choose the right admixture for individual time dependent flow specifications.