Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (19)
- Vortrag (14)
- Beitrag zu einem Tagungsband (10)
- Posterpräsentation (4)
- Buchkapitel (1)
- Beitrag zu einem Sammelband (1)
- Forschungsdatensatz (1)
Schlagworte
- P92 (5)
- Creep-fatigue (4)
- Thermo-mechanical fatigue (4)
- Ferritic-martensitic steels (3)
- Low cycle fatigue (3)
- Pseudoelasticity (3)
- R-phase (3)
- Stress relaxation (3)
- Tempered martensite-ferritic steel (3)
- Creep (2)
Organisationseinheit der BAM
- 5 Werkstofftechnik (22)
- 5.2 Metallische Hochtemperaturwerkstoffe (20)
- 5.1 Mikrostruktur Design und Degradation (8)
- 5.5 Materialmodellierung (8)
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.3 Instrumentelle Analytik (1)
- 6 Materialchemie (1)
- 6.4 Materialinformatik (1)
- 7 Bauwerkssicherheit (1)
- 7.7 Modellierung und Simulation (1)
Eingeladener Vortrag
- nein (14)
Subjecting a thin NiTi specimen to uniaxial tension often leads to a localized martensitic transformation: macroscopic transformation bands form and propagate through the specimen, separating it into regions of fully transformed martensite and original austenite. In the present study, the alternating current potential drop (ACPD) technique is used to analyze the change in electrical resistance of ultra-fine grained NiTi wires subjected to a broad range of thermo-mechanical load cases: (i) uniaxial tensile straining at constant temperatures (pseudoelastic deformation); (ii) cooling and heating through the transformation range at constant load (actuator load case); (iii) a combination of mechanical and thermal loading. We monitor the ACPD signals in several zones along the gauge length of specimens, and we demonstrate that a localized type of transformation is a generic feature of pseudoelastic as well as of shape memory deformation. Moreover, the ACPD signals allow to differentiate between temperature-induced martensite (formed during cooling at no or relatively small loads), stress-induced martensite, and reoriented martensite (formed under load at low temperatures).
Mechanical Properties of Superheater Materials after Ageing and Corrosion in CO2 rich Flue Gases
(2010)
Mechanical properties of superheater materials after ageing and corrosion in CO2 rich flue gases
(2010)
On the stress-induced formation of R-phase in ultra-fine-grained Ni-Rich NiTi shape memory alloys
(2011)
Phase transformations in binary ultra-fine-grained (UFG) pseudoelastic NiTi wires were studied in a wide temperature range using mechanical loading/unloading experiments, resistance measurements, differential scanning calorimetry (DSC), thermal infrared imaging, and transmission electron microscopy (TEM). The formation of R-phase can be detected in the mechanical experiments. It is shown that the stress-strain response of the R-phase can be isolated from the overall stress-strain data. The R-phase always forms prior to B19¢ when good pseudoelastic properties are observed. The stress-induced B2 to R-phase transition occurs in a homogeneous manner, contrary to the localized character of the B2/R to B19' transformations. The temperature dependence of the critical stress values for the formation of the martensitic phases shows a Clausius Clapeyron type of behavior with constants close to 6 MPa/K (B19') and 18 MPa/K (R-phase). A stress-temperature map is suggested that summarizes the experimentally observed sequences of elementary transformation/deformation processes.
The transformation between the cubic B2 and monoclinic B19' phases in ultrafine-grained pseudoelastic NiTi can occur as a two-step process involving the intermediate rhombohedral R-phase. Experimental work using differential scanning calorimetry, electrical resistance measurements and transmission electron microscopy has demonstrated the formation of this intermediate phase during thermal cycling and during mechanical loading. In the present paper, complementary mechanical and thermographic results are presented which allow to further assess the character of the stress-induced R-phase formation. The transformation from B2 to R-phase is demonstrated to occur homogeneously within the gauge length rather than via advancing Lüders-type transition regions as it is the case in the localized transformation from B2 or R-phase to B19'.
A miniature specimen geometry is presented that allows to extract small samples for tensile creep tests directly from critical components of steam generators in power plants like e.g. superheater tubes. In this way, material can be tested which has been subjected to the full processing chain of the component. The specimens then exhibit all microstructural modifications that are present in the component after the shaping process and heat treatment, and representative mechanical properties are determined. Similarly, specimens can be extracted from pre-corroded test pieces or used components after service to determine the impact of complex aging/loading/oxidation conditions during service on the mechanical properties of the material. The applicability of the miniature specimen test method is demonstrated in a comparative creep study involving standard and miniature specimens of P91 tempered martensite ferritic steel. Test results indicate satisfactory accuracy/repeatability of the method. Comparison with large scale specimen data reveals an influence of specimen size on the obtained creep behavior. These size effects need to be considered for a correct interpretation of results from miniature specimen creep tests.