Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (19)
- Vortrag (14)
- Beitrag zu einem Tagungsband (10)
- Posterpräsentation (4)
- Buchkapitel (1)
- Beitrag zu einem Sammelband (1)
- Forschungsdatensatz (1)
Schlagworte
- P92 (5)
- Creep-fatigue (4)
- Thermo-mechanical fatigue (4)
- Ferritic-martensitic steels (3)
- Low cycle fatigue (3)
- Pseudoelasticity (3)
- R-phase (3)
- Stress relaxation (3)
- Tempered martensite-ferritic steel (3)
- Creep (2)
Organisationseinheit der BAM
- 5 Werkstofftechnik (22)
- 5.2 Metallische Hochtemperaturwerkstoffe (20)
- 5.1 Materialographie, Fraktographie und Alterung technischer Werkstoffe (8)
- 5.5 Materialmodellierung (8)
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.3 Instrumentelle Analytik (1)
- 6 Materialchemie (1)
- 6.4 Materialinformatik (1)
- 7 Bauwerkssicherheit (1)
- 7.7 Modellierung und Simulation (1)
Eingeladener Vortrag
- nein (14)
In our current view, reference datasets in the MSE domain represent specific material properties, e.g., structural, mechanical, … characteristics. A reference dataset must fulfill high-quality standards, not only in precision of measurement but also in a comprehensive documentation of material, processing, and testing history (metadata). This Infrastructure Use Case (IUC) aims to develop a framework for generating reference material datasets using creep data of a single crystal Ni-based superalloy as a best practice example. In a community-driven process, we aim to encourage the discussion and establish a framework for the creation and distribution of reference material datasets. In this poster presentation, we highlight our current vision and activities and intend to stimulate the discussion about the topic reference datasets and future collaborations and work.
This article refers to the research article entitled “Creep-Fatigue of P92 in Service-Like Tests with Combined Stress- and Strain-Controlled Dwell Times” [1]. It presents experimental mechanical data from complex service-like creep-fatigue experiments performed isothermally at 620 °C and a low strain amplitude of 0.2 % on tempered martensite-ferritic grade P92 steel. The data sets in text file format provide cyclic deformation (min. and max. stresses) and the total (hysteresis) data of all recorded fatigue cycles for three different creep-fatigue experiments: 1) a standard relaxation fatigue (RF) test with symmetrical dwell times of three minutes introduced at minimum and maximum strain, 2) a fully strain-controlled service-like relaxation (SLR) test combining these three-minute peak strain dwells with a 30-minute dwell in between at zero strain, and 3) a partly stress-controlled service-like creep (SLC) test combining the three-minute peak strain dwells with 30-minute dwells at constant stress. Such service-like (SL) tests with additional long-term stress- and strain-controlled dwell times are non-standard, rare, and expensive, making these data very valuable. They may be used to approximate cyclic softening in the technically relevant range, for the design of complex SL experiments, or for detailed analyses of stress-strain hystereses (e.g., for stress or strain partitioning methods, for the determination of hysteresis energies (work), inelastic strain components, etc.). In addition, the latter analyses may supply important input for advanced parametric lifetime modeling of components under creep-fatigue loading or model calibration parameters.
Creep-fatigue of P92 in service-like tests with combined stress- and strain-controlled dwell times
(2023)
Complex service-like relaxation- and creep-fatigue tests with strain- and stress-controlled dwells and fatigue cycle durations of approx. 2200 s were performed exemplarily on a grade P92 steel at 620 ◦C in this study. The results indicate deviations in the prevailing creep mechanisms of long-term relaxation and creep dwells, affecting subsequent dwells, load shifts, and the macroscopic softening behavior quite differently. In addition, fracture surfaces and longitudinal metallographic sections reveal intergranular crack growth for complex loading with stress-controlled dwells, whereas complex strain-controlled tests enhance oxidation and transgranular crack propagation. These findings substantiate the limited transferability of relaxation-fatigue to creep-fatigue conditions.
The dataset contains experimental mechanical data from complex service-like creep-fatigue experiments performed isothermally at 620 °C and a low strain amplitude of 0.2 % on tempered martensite-ferritic grade P92 steel. The data sets in text file format provide cyclic deformation (min. and max. stresses) and the total (hysteresis) data of all recorded fatigue cycles for three different creep-fatigue experiments: 1) a standard relaxation fatigue (RF) test with symmetrical dwell times of three minutes introduced at minimum and maximum strain, 2) a fully strain-controlled service-like relaxation (SLR) test combining these three-minute peak strain dwells with a 30-minute dwell in between at zero strain, and 3) a partly stress-controlled service-like creep (SLC) test combining the three-minute peak strain dwells with 30-minute dwells at constant stress.
Further information on data and data acquisition, analysis, and experimental details are given in “Experimental Data from Service-Like Creep-Fatigue Experiments on Grade P92 Steel”, submitted to Data in Brief. Additional analyses of these datasets, as well as experimental findings and discussions are presented in “Creep-Fatigue of P92 in Service-Like Tests with Combined Stress- and Strain-Controlled Dwell Times”, submitted to International Journal of Fatigue.
Performing mechanical tests at high temperatures is a nontrivial issue: Compared to room temperature testing, additional phenomena like time-dependent Deformation processes and oxidation effects raise the complexity of the material’s response, while more sophisticated test setups and additional control parameters increase the number of potential sources of error. To a large extent, these complications can be overcome by carefully following all recommendations given in the respective high temperature testing standards, but more comprehensive background information helps to identify points of specific importance in particular test campaigns. In this chapter, an overview is given on general high temperature testing issues like the appropriate choice of experimental equipment and key aspects of temperature measurement. In subsequent sections, the major static and dynamic high temperature test methods are reviewed and their Special features, as compared to testing at room temperature, are highlighted based on example data sets. Influences of specimen size and environmental effects are shortly outlined in a concluding section. In the whole chapter, a focus is set on testing of “classical” metallic high temperature materials, but many considerations are equally valid for testing of intermetallics, composites, and high temperature ceramics.
Das hochaktuelle Thema der Integration und Wiederverwendung von Wissen und Daten aus Herstellung, Bearbeitung und Charakterisierung von Materialien ('Digitalisierung von Materialien') wird in den Projekten Innovationsplattform MaterialDigital (PMD, materialdigital.de) und Materials-open-Lab (Mat-o-Lab, matolab.org) adressiert. In diesem Beitrag werden die Weiterentwicklungen in diesen Projekten hinsichtlich der Speicherung von Zugversuchsdaten gemäß einer normenkonformen (DIN EN ISO 6892-1:2019-11) ontologischen Repräsentation vorgestellt. Das umfasst den Weg von der Entwicklung einer Ontologie nach Norm, der Konvertierung von Daten aus Standardtests in das interoperable RDF-Format bis hin zur Verknüpfung von Ontologie und Daten. Letztendlich können die entsprechenden Daten in einem Triple Store abgelegt und abgefragt werden.
Subjecting a thin NiTi specimen to uniaxial tension often leads to a localized martensitic transformation: macroscopic transformation bands form and propagate through the specimen, separating it into regions of fully transformed martensite and original austenite. In the present study, the alternating current potential drop (ACPD) technique is used to analyze the change in electrical resistance of ultra-fine grained NiTi wires subjected to a broad range of thermo-mechanical load cases: (i) uniaxial tensile straining at constant temperatures (pseudoelastic deformation); (ii) cooling and heating through the transformation range at constant load (actuator load case); (iii) a combination of mechanical and thermal loading. We monitor the ACPD signals in several zones along the gauge length of specimens, and we demonstrate that a localized type of transformation is a generic feature of pseudoelastic as well as of shape memory deformation. Moreover, the ACPD signals allow to differentiate between temperature-induced martensite (formed during cooling at no or relatively small loads), stress-induced martensite, and reoriented martensite (formed under load at low temperatures).
Martensitic phase transformations were studied in ultrafine grained Ni-rich pseudoelastic NiTi wires during cyclic deformation under small imposed strain amplitudes. Small strain variation tests were complemented by a thermographic analysis of the emerging temperature distributions in the specimens. The characteristics of the observed thermal profiles result from the specific phase transitions which take place at different stress levels. Homogeneous temperature changes, corresponding to a non-localized transformation activity along the specimen length, were observed throughout the whole range of applied stresses, starting from values as low as 100 MPa. This behavior is in line with previous literature reports for the stress-induced transformation from B2 austenite to R-phase as long as the critical stress for B19' martensite formation is not reached. In the present study, similar type of transformation activity could also be demonstrated at higher strains/stresses, even after the stress induced transformation to B19' was apparently completed. These findings suggest that transformation activity involving the B2 phase is present throughout the whole pseudoelastic stressstrain cycle; i.e., it is not restricted to the initial loading portion. Finally, non-localized transformation to or from B19' was identified during small amplitude strain variations in the plateau-like coexistence ranges of the pseudoelastic cycle.
Fukuda et al. published a paper (Scripta Mater. 68 (2013) 984–987) in which they claimed to be able to determine the isothermal nature of the martensitic transformation in a Ti–Ni alloy. They analyzed the evolution of electrical resistance during isothermal holding stages and concluded that the variations were a consequence of the isothermal transition between austenite and martensite. In the following we will demonstrate that the discussed data do not allow the interpretation presented and that the isothermal nature is not proved.
Temperature-induced, stress-induced martensitic phase transitions and martensite reorientation process in Ni rich (50.9 at.%) NiTi pseudoelastic NiTi wires with ultra-fine grained (UFG) microstructure were studied by electrical resistance measurements. Measurements of the electrical resistance as a function of temperature at different constant mechanical loads accompanied by complementary experiments with variable loads at constant temperature were performed. Results show that the transformation mechanisms in UFG microstructures exhibit a higher level of complexity when compared with those characterizing the behavior of other microstructures (e.g., recrystallized or larger grains size). It was found that a threshold stress level below 150 MPa delimits the transition from a homogeneous (low stress) to localized but reversible Lüders type transformation (high stress) when the transformations are induced under constant applied stress and that reorientation processes require stresses of 100 MPa in the present UFG wires. Even though the strain evolutions do not always show two distinct yielding events during cooling or heating, electrical resistance measurements proved that a two-step transformation involving R-phase and B19' martensite was always present in the extended range of temperatures and stresses investigated here.