Sixteen laboratories have performed electrochemical noise (EN) measurements based on two systems. The first uses a series of dummy cells consisting of a 'star' arrangement of resistors in order to validate the EN measurement equipment and determine its baseline noise performance, while the second system, based on a previous round-robin in the literature, examines the corrosion of aluminium in three environments. All participants used the same measurement protocol and the data reporting and analysis were performed with automatic procedures to avoid errors. The measurement instruments used in the various laboratories include commercial general-purpose potentiostats and custom-built EN systems. The measurements on dummy cells have demonstrated that few systems are capable of achieving instrument noise levels comparable to the thermal noise of the resistors, because of its low level. However, it is of greater concern that some of the instruments exhibited significant artefacts in the measured data, mostly because of the absence of anti-aliasing filters in the equipment or because the way it is used. The measurements on the aluminium samples involve a much higher source noise level during pitting corrosion, and most (though not all) instruments were able to make reliable measurements. However, during passivation, the low level of noise could be measured by very few systems. The round-robin testing has clearly shown that improvements are necessary in the choice of EN measurement equipment and settings and in the way to validate EN data measured. The results emphasise the need to validate measurement systems by using dummy cells and the need to check systematically that the noise of the electrochemical cell to be measured is significantly higher than the instrument noise measured with dummy cells of similar impedance.
Dekorativ verchromte Kunststoffanbauteile werden seit Anfang der 1970er Jahre in der Automobilindustrie eingesetzt, um einem Fahrzeug eine optisch höhere Wertigkeit zu geben. Diese mikroporig bzw. mikrorissig galvanisch abgeschiedenen Überzüge auf Kunststoffanbauteilen sind in einer festgelegten Reihenfolge übereinander angeordnet, um die Funktionen Dekorativität und Korrosionsbeständigkeit zu erfüllen. Unter dem Chromüberzug befindet sich u.a. ein Glanznickelüberzug, welcher durch Poren bzw. Risse bei Kontakt mit Streusalzsole gezielt korrodieren soll und somit den Chromüberzug kathodisch schützt. Der Zusatz von Kalziumchlorid in die Streusalzmischungen in Regionen mit extrem niedrigen Temperaturen (z. B. Winter in Moskau) stört diesen Mechanismus. Unter diesen Bedingungen wurden flächenhafte Schäden am Chromüberzug mikroporig verchromter Kunststoffanbauteile beobachtet. Bei Volkswagen erfolgte daraufhin die Umstellung aller verchromten Bauteile im Exterieur auf mikrorissig. Die Ursache für diese Schäden soll in der vorliegenden Arbeit geklärt werden.
Claddings of different nickel based alloys were generated on a mild Steel (S235JR) and a stainless steel type 304 by Cold Metal Transfer (CMT). This welding procedure possesses a low degree of mixing between the Substrate and cladding material. Thus it improves the corrosion behaviour of the claddings. The aim of our investigations was to examine the effect of the welding parameters: energy per unit length, shielding gas and finishing surface treatment on the pitting corrosion behaviour of the claddings.
However, under Standard test conditions nickel based alloys are often resistant to pitting corrosion. Moreover these test methods are inaccurate and require a large period of time resulting from the iterative progress to determine the critical pitting temperature (CPT). A potentiostatic test method was modified using a high concentrated CaCI2-solution and a conventional three electrode measuring cell. The pitting corrosion behaviour is calculated from current noise charges. During the test the course of corrosion is detected online by the evaluation of electrochemical noise Signals while a continuous increase of temperature by a defined heating rate is realised.
Thus a critical pitting temperature can be estimated by only one attempt. Furthermore the deviation of the measured CPT is very low compared to Standard tests using gravimetrical and microscopic evaluation. That enables to figure out the influence of the welding parameters in an exact way.
Capillary active interior insulation materials are an important approach to minimize energy losses of historical buildings. A key factor for their performance is a high liquid conductivity, which enables redistribution of liquid moisture within the material. We set up an experiment to investigate the development of moisture profiles within two different interior insulation materials, calcium-silicate (CaSi) and expanded perlite (EP), under constant boundary conditions. The moisture profiles were determined by two different methods: simple destructive sample slicing with subsequent thermogravimetric drying as well as non-destructive NMR measurements with high spatial resolution. The moisture profiles obtained from both methods show good agreement, when compared at the low spatial resolution of sample slicing, which demonstrates the reliability of this method. Moreover, the measured T2-relaxation-time distributions across the sample depth were measured, which may give further insight into the saturation degree of the different pore sizes. In order to explain differences in the moisture profiles between CaSi and EP, we determined their pore-size distribution with different methods: conversion of the NMR T2 relaxationtime distribution at full saturation, mercury intrusion porosimetry and indirect determination from pressure plate measurements. CaSi shows a unimodal distribution at small pore diameters, while in EP, a bi-modal or wider distribution was found. We assume that the smaller pore diameters of CaSi lead to a higher capillary conductivity, which causes a more distributed moisture profile in comparison with that of EP.