Filtern
Erscheinungsjahr
Dokumenttyp
- Beitrag zu einem Tagungsband (25) (entfernen)
Referierte Publikation
- nein (25) (entfernen)
Schlagworte
- Durability (4)
- Cracks (3)
- Nano-silica (3)
- Acoustic emission analysis (2)
- Carbonation (2)
- Concrete (2)
- Crack formation (2)
- Repair (2)
- Shrinkage (2)
- 3D computed tomography (1)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (11)
- 7.4 Baustofftechnologie (10)
- 7.2 Ingenieurbau (5)
- 7.1 Baustoffe (2)
- 8 Zerstörungsfreie Prüfung (2)
- 8.2 Zerstörungsfreie Prüfmethoden für das Bauwesen (2)
- 2 Prozess- und Anlagensicherheit (1)
- 2.4 Prüfung und Bewertung von Explosivstoffen/Pyrotechnik (1)
- 2.5 Konformitätsbewertung Explosivstoffe/Pyrotechnik (1)
- 8.6 Faseroptische Sensorik (1)
Entwicklung eines PCC-Leichtmörtels zur Instandsetzung einer denkmalgeschützten Sichtbetonfassade
(2015)
Der Schutz und Erhalt der Originalsubstanz stehen im Mittelpunkt jeglicher denkmalpflegerischer Instandhaltungsmaßnahmen. Das äußere Erscheinungsbild spielt hierbei - im Gegensatz zur klassischen Betoninstandsetzung - eine größere Rolle. Nichtsdestotrotz dürfen die technischen Belange auch hier nicht außer Acht gelassen werden. Die Ermittlung des Ist- und Sollzustands stellt die Grundlage einer dauerhaften Instandsetzung dar. Der vorliegende Beitrag zeigt Schäden und Schadensursachen an einem denkmalgeschützten Gebäude in Leichtbetonbauweise auf. Das Bauwerk wurde hinsichtlich seines Schädigungsgrads, -umfangs und der maßgeblichen Schadensursachen untersucht. Im Rahmen dieser Untersuchungen wurden gehäuft Risse, Abplatzungen und Bewehrungskorrosion festgestellt. Die durch eine Brettschalung strukturierte Sichtbetonfassade soll im Zuge der Instandsetzungsmaßnahme möglichst originalgetreu wiederhergestellt werden.
Bei der Auswahl von geeigneten Instandsetzungsmethoden und -produkten konnte aufgrund fehlender Normen und Richtlinien für die Instandsetzung von denkmalgeschützten Leichtbetonbauten nicht auf bereits existierende Produkte und Methoden zurückgegriffen werden. Daher wurde in Anlehnung an die Richtlinie "Schutz und Instandsetzung von Betonbauteilen" (RL SIB) des DAfStB eine polymermodifizierte Betonergänzungsmasse mit leichter Gesteinskörnung entwickelt. Ausgehend von der Hauptschadensursache, der karbonatisierungsinduzierten Bewehrungskorrosion, wurden erforderliche Eigenschaften der Betonergänzungsmasse in enger Absprache mit der zuständigen Denkmalschutzbehörde und dem involvierten Fachplaner abgestimmt. Neben den grundlegenden mechanischen Eigenschaften spielen in diesem Anwendungsfall spezielle Eigenschaften wie z.B. farbliehe Anpassung der Betonergänzungsmasse, Möglichkeit der Oberflächenstrukturierung, Zeitfenster der Verarbeitbarkeit sowie die Modellierbarkeit eine wichtige Rolle. Der entwickelte PCC-Leichtmörtel berücksichtigt dabei auch den Einfluss einer geringen Schwind- und Quellneigung der Betonergänzungsmasse um Delaminierung infolge unterschiedlicher Längenänderungen zu vermeiden und somit eine dauerhafte Instandsetzung zu gewährleisten. Weiterhin wurde das Verbundverhalten des entwickelten PCCL Leichtmörtels für unterschiedliche Schichtaufbauten untersucht.
Reinforced concrete buildings are frequently damaged by cracks, spalling and corroded
reinforcement bars. The present article focuses on the damage analysis of one of the first
buildings in Berlin that was constructed using reinforced lightweight concrete, which makes it
historically important. The compressive strength, carbonation depth, location and diameter of
reinforcement bars as well as moisture and salt profiles were determined. The carbonationinduced corrosion of the reinforcement bars represented the main damage of the building.
Certified repair mortars with lightweight aggregates (LWA) do not exist on the German
market. Therefore, an appropriate repair mortar was developed in accordance with DIN EN
1504 and the German guideline for the repair and protection of concrete structures (RL-SIB).
On the one hand, historic preservation requirements, such as: colour of the mortar,
possibilities of surface patterning, maximum preservation of the original substance and
reversibility of any Intervention must be met. On the other hand, technical requirements of the
relevant Standards must be achieved. The developed mix was designed to resist the identified
causes of deterioration. Thermal strains within the repair mortar and between the repair
mortar and the Substrate influence the crack formation and thus the durability. Therefore,
special attention was paid to the bonding and shrinking behaviour of the concrete repair
System. By using polymers, both hardened mortar properties and durability were influenced
positively.
Am Ende des 19. und zu Beginn des 20. Jahrhunderts wurden auch in Berlin vermehrt Bauwerke mit einer Fassadenverblendung aus Eifeler Tuffsteinen errichtet. Die Eifeler Tuffsteine zeichnen sich aufgrund ihrer hohen Porosität einerseits durch eine gute Verarbeitbarkeit aus. Andererseits sind sie nur schwach gebunden und besitzen deshalb eine geringe Verwitterungsbeständigkeit.
Für die rechnerische Dimensionierung der Betondecken im Oberbau von Verkehrsflächen für den Neubau sowie die Erneuerung nach RDO Beton 09 ist die statische Spaltzugfestigkeit an der unteren bzw. unteren und oberen Scheibe des Betonzylinders bzw. Bohrkerns entsprechend der Vorgaben der AL Sp-Beton zu bestimmen. Aufgrund der unzureichenden Kenntnis der Präzision dieses Prüfverfahrens wurden mit einem breit aufgestellten Ringversuch die statistischen Kennwerte an Labor- und Bestandsbetonen unter Vergleich- und Wiederholbedingungen auf der Grundlage des „Merkblatts über die statistische Auswertung von Prüfergebnissen" ermittelt. Für eine möglichst gute statistische Absicherung nahmen an dem Ringversuch 13 erfahrene Prüfstellen teil. Zur Abdeckung des vielschichtigen Einsatzes des Prüfverfahrens erfolgte der Ringversuch an acht Prüflosen. Dabei berücksichtigen einerseits die Prüf lose 1 und 2 mit den im Transportbetonwerk hergestellten Betonzylindern die Erst-/Eignungsprüfung und das darauf aufbauende Prüflos 3 mit Bohrkernen aus einer im Feldversuch hergestellten Fahrbahnplatte mit gleicher Betonrezeptur die Übereinstimmungskontrolle bei Neubaumaßnahmen. Andererseits findet der Einsatz des Prüfverfahrens bei der Restsubstanzbewertung von Betonfahrbahnplatten bei den Prüflosen 4 bis 7 mit den Bohrkernen aus vier in Waschbetonbauweise ausgeführten Fahrbahnplatten Berücksichtigung. Das zusätzlich aufgenommene Prüflos 8 mit einem Labormörtel dient der Herausarbeitung des Materialeinflusses auf die Präzision der Spaltzugfestigkeitsprüfung. Zusammenfassend kann festgestellt werden, dass die Präzision der in der AL SP-Beton beschriebenen Spaltzugfestigkeitsprüfung mit einem Variationskoeffizienten von weniger als 10 % unter Wiederhol- und Vergleichbedingungen hinreichend genau ist. Der geringe Unterschied zwischen den Variationskoeffizienten unter Wiederhol- und Vergleichbedingungen lässt zusätzlich den Schluss zu, dass der Einfluss des unterschiedlichen Personals und der verschiedenartigen Prüftechniken bei den einzelnen Prüfstellen relativ gering ist. Die im Rahmen des Ringversuchs gewonnenen Erkenntnisse haben bereits partiell Eingang in die Normung gefunden.
Introduction of a monitoring system for Bingham fluids in additive manufacturing with concrete
(2022)
Freeform additive manufacturing of concrete structures is a rising technology in civil engineering with several fascinating advantages. Nonetheless, to ensure reliability and structural integrity, standards and quality control are required in the future to bring this technology into the market. As the concrete is manufactured continuously, continuous quality control of the printing process is also required, i.e. comprehensive process monitoring. At BAM, a test rig will be installed, enabling the printing of concrete structures with a maximum size of 2 m x 1 m x 1 m (l x w x h). Here, process monitoring is the focus of the test rig. In this study, we show the results of the first pump tests, including the measurement of several parameters such as temperature and pressure along the supply system, i.e. from the concrete pump to the printer head.
Remediation of Cracks Formed in Grouted Connections of Offshore Energy Structures under Static Loads
(2018)
The future energy demand necessitates the exploration of all potential energy sources both onshore and offshore. Global trend has shifted towards offshore energy, which can be obtained from either carbon intensive or renewable options, hence requiring structures such as rigs, platforms, and monopiles. Most of these structures adopt easily installable construction techniques, where lower foundation need to be connected with the super structure by mean of grouted composite joints. Generally, these composite connections have exterior sleeve, interior pile and infill grout. Being located in remote offshore conditions, connections can experience considerable adverse loading during their lifetimes. Degradations were reported inside similar connections, which were installed in last three decades. Besides, grouting in the offshore sites may often be proven difficult, which eventually leads to reduced capacity of connections in the long run. Thus, repair and rehabilitation of such connections should be planned ahead to minimize operational delays and costs in the future. This study aims at characterizing the nature of crack generation in grouted connections and thereby identifying the potential of repair using suitable repair material. Scaled grouted joints were manufactured using a novel mold, and connections were loaded under static load to visualize the main failure pattern. The failure mechanism and loading capacity are found compatible to previous results from earlier literature. Grouted connection was then repaired using cementitious injectable grout. The effectiveness of the repair system is also discussed.
Grouting is a universal repair and strengthening technique, which is constantly used for structural remediation of concrete components, trenches, mine subsidence, dam joints, restoration of masonry structures, and geological stabilizations. Having an extremely small particle size of only few microns, ultrafine cements are ideal for grouting applications due to their superior permeability and compressive strength properties of the hardened cement paste compared to that of the less-expensive, but coarser ordinary Portland cements. Supplementary cementitious materials (SCMs) are often used to replace ultrafine cement in order to modify certain properties and to reduce costs. The aim of this experimental study is to investigate the effect of three supplementary materials: microsilica (MS), fly ash (FA), and metakaolin (MK) on the workability, and mechanical properties of an ultrafine cement based grout with a constant water-binder ratio and constant superplasticizer content. Maximum percentages of replacement with ultrafine cement were 6% by volume of cement for MS and 16% for FA, and MK. In general, results suggest that the workability is improved by addition of FA, whereas is reduced, when modified with MS and MK. The compressive strength of grout after cement replacement remains comparable to that of pure cement grout. However, there is a tendency of the MS to positively affect the compressive strength opposite to FA, whereas flexural strength is positively affected by FA. Based on the results, it is evident that grouts with Hägerman cone flow more than 500 mm and compressive strength of more than 90 MPa after 28 days can be produced.
At present, Wind Turbine Generators (WTGs) operating in onshore and offshore wind farms are primary sources of renewable energy around the world. Cylindrical grouted sleeve connections are usually adopted in these WTG structures to connect the upper structure and foundation for ease of installation. These structures including grouted connections experience considerable adverse loading during their lifetimes. Settlements were reported inside similar connections used in energy structures especially oil and gas platforms, which were installed in last three decades. Thus, repair and rehabilitation of such connections in existing wind structures should also be planned ahead to keep them operating in the future. The nature of failure and crack generation in grouted connections are crucial prior to adopt a strengthening strategy. This pilot study is carried out to actualize the failure mechanism in the grouted connection, when subjected to axial loading. A novel reusable scaled cylindrical grouted connection with shear keys was designed and tested for its load bearing behaviour. The mechanical test was accompanied by classical measuring techniques (e.g. displacement transducer) as well as non-destructive measuring techniques (e.g. digital image correlation (DIC), acoustic emission analysis (AE)). The failure mechanism incorporating slippage of the shear keys and cracking of the grout was investigated. The capacity and applicability of such test mould were also discussed. The knowledge is expected to pave way towards repair of deteriorated grouted connections with similar geometry and failure pattern.
Effects of amorphous nano-silica additions on mechanical and durability performance of SCC mixtures
(2012)
In the recent years the application of nanotechnology in building materials has increased
exponentially. One of the most referred and used nano-materials is amorphous silica with
particles size in the nano-range, even though its application and effect in concrete has not been
fully understood yet. It has been reported that nano-silica (nS) addition increases the
compressive strength and reduces the overall permeability of hardened concrete due to the
pozzolanic properties which are resulting in finer hydrated phases (C-S-H gel) and densified
microstructure (nano-filler and anti leaching effects). These effects enhance the durability of
concrete structures such as bridges, quays or off-shore oil facilities in marine environments.
In this study two different types of nano-silica were applied in self-compacting concrete (SCC),
both having similar particle size distributions (PSD) but produced in two different processes
(fumed powder silica and precipitated silica in colloidal suspension). The influence of nanosilica
on SCC was investigated with respect to the properties of concrete in the fresh state
(workability) and hardened state (mechanical properties and durability). Additionally, the
densification of microstructure of the hardened concrete was verified by SEM and EDS analyses.
The obtained results demonstrate that an efficient use of nano-silica in SCC can improve its
mechanical properties and durability. Considering the reactivity of the two nano-silica studied,
colloidal type shown more reactivity at early age, which influenced all the final SCC properties.