Pyrolysis, fire behaviour and mechanical properties of a blend of poly(butylene terephthalate) (PBT) with a phosphorus polyester (PET-P-DOPO) are investigated and compared with PBT/aluminium diethylphosphinate (AlPi-Et) composites. The PBT/PET-P-DOPO is immiscible and exhibits gas-phase and condensed-phase activity, whereas AlPi-Et in PBT results mainly in flame inhibition. Only higher loadings of AlPi-Et yield significant condensed-phase activity. Using the same phosphorus content, PBT/PET-P-DOPO and PBT/AlPi-Et exhibit similar reductions in fire load (22%) and flame spread (17% assessed by fire growth rate, FIGRA), compared with PBT. In contrast to AlPi-Et, the addition of PET-P-DOPO does not decrease the tensile strength of PBT. Thus, PET-P-DOPO is an interesting alternative to low-molecular-weight flame retardants.
Summary: The decomposition of novel phosphorus-containing poly(oxyphenylene-sulfonyl-phenylene-oxy-diphenyl phenylene phosphine oxide) (PSU_I), 2,5-dihydroxy-1-biphenylene-phosphine oxide based polysulfone (PSU_II), poly(sulfonyl-diphenylphenylene phosphonate) (PSU_P) and bisphenol A-based polysulfone (PSU) is studied. The influence of the chemical structure, charring and phosphorus release is discussed based on the mass loss, kinetics and products. The pyrolysis and fire behaviour of blends with epoxy resin (EP) are studied. For EP-PSU_II, phosphorus initiates water elimination and changes the decomposition pathway of EP. The fire behaviour of EP-PSU shows some improvements, whereas the heat release rate is crucially reduced for EP-PSU_II due to simultaneous char formation and flame inhibition.
Flame retardancy for thermoplastics is a challenging task where chemists and engineers work together to find solutions to improve the burning behavior without strongly influencing other key properties of the material. In this work, the halogen-free additives aluminum diethylphosphinate (AlPi-Et) and a mixture of aluminum phosphinate (AlPi) and resorcinol-bis(di-2,6-xylyl phosphate) (AlPi-H + RXP) are employed in neat and reinforced poly(butylene terephthalate) (PBT), and the morphology, mechanical performance, rheological behavior, and flammability of these materials are compared. Both additives show submicron dimensions but differ in terms of particle and agglomerate sizes und shapes. The overall mechanical performance of the PBT flame-retarded with AlPi-Et is lower than that with AlPi-H-RXP, due to the presence of larger agglomerates. Moreover, the flow behavior of the AlPi-Et/PBT materials is dramatically changed as the larger rod-like primary particles build a percolation threshold. In terms of flammability, both additives perform similar in the UL 94 test and under forced-flaming combustion. Nevertheless, AlPi-Et performs better than AlPi-H + RXP in the LOI test. The concentration required to achieve acceptable flame retardancy ranges above 15 wt %.
A comparative evaluation of systematically tailored chemical structures of various phosphorus-containing aminic hardeners for epoxy resins was carried out. In particular, the effect of the oxidation state of the phosphorus in the hardener molecule on the curing behavior, the mechanical, thermomechanical, and hot-wet properties of a cured bifunctional bisphenol-A based thermoset is discussed. Particular attention is paid to the comparative pyrolysis of neat cured epoxy resins containing phosphine oxide, phosphinate, phosphonate, and phosphate (with a phosphorus content of about 2.6 wt %) and of the fire behavior of their corresponding carbon fiber-reinforced composites. Comparatively faster curing thermosetting system with an enhanced flame retardancy and adequate processing behavior can be formulated by taking advantage of the higher reactivity of the phosphorus-modified hardeners. For example, a combination of the high reactivity and of induced secondary crosslinking reactions leads to a comparatively high Tg when curing the epoxy using a substoichiometric amount of the phosphinate-based hardener. The overall mechanical performance of the materials cured with the phosphorus-containing hardeners is comparable to that of a 4,4-DDS-cured reference system. While the various phosphorus-containing hardeners in general provide the epoxy-based matrix with enhanced flame retardancy properties, it is the flame inhibition in the gas phase especially that determines the improvement in fire retardancy of carbon fiber-reinforced composites. In summary, the present study provides an important contribution towards developing a better understanding of the potential use of such phosphorus-containing compounds to provide the composite matrix with sufficient flame retardancy while simultaneously maintaining its overall mechanical performance on a suitable level.
The pyrolysis of an epoxy resin and the fire behavior of corresponding carbon fiber-reinforced composites, both flame-retarded with either 10-ethyl-9,10-dihydro-9-oxa-10-phosphaphenanthrene 10-oxide or 1,3,5-tris[2-(9,10-dihydro-9-oxa-10-phosphaphenanthrene 10-oxide-10-)ethyl]1, 3,5-triazine-2,4,6(1H,3H,5H)-trione, are investigated. The different fire retardancy mechanisms are discussed, and their influence on the fire properties assessed, in particular for flammability (limiting oxygen index, UL 94) and developing fires (cone calorimeter with different external heat fluxes of 35, 50, and 70 kW m-2). Adding the flame retardants containing 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide affects the fire behavior by both condensed phase and gas phase mechanisms. Interactions between the additives and the epoxy resin result in a change in the decomposition pathways and an increased char formation. The release of phosphorous products results in significant flame inhibition. The fire properties achieved are thus interesting with respect to industrial exploration.
Flame retarded poly(butylene terephthalate) (PBT) is required for electronic applications and is mostly achieved by low molar mass additives so far. Three phosphorus-containing polyesters are suggested as halogen-free and polymeric flame retardants for PBT. Flame retardancy was achieved according to cone calorimeter experiments showing that the peak heat release rate and total heat evolved were reduced because of flame inhibition and condensed-phase activity. The presented polymers containing derivatives of 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide form immiscible blend systems with PBT. Shear-rheology shows an increase in storage moduli at low frequencies. This is proposed as quantitative measure for the degree of phase interaction. The phase structure of the blends depends on the chemical structure of the phosphorus polyester and was quite different, depending also on the viscosity ratio between matrix and second phase. A lower viscosity ratio leads to two types of phases with spherical and additionally continuous droplets. Addition of the flame retardants showed no influence on the dielectric properties but on the mechanical behavior. The polymeric flame retardants significantly diminish the impact strength because of several reasons: (1) high brittleness of the phosphorus polyesters themselves, (2) thermodynamic immiscibility, and (3) weak phase adhesion. By adding a copolymer consisting of the two base polymers to the blend, an improvement of impact strength was obtained. The copolymer particularly acts as compatibilizer between the phases and therefore leads to a smaller phase size and to a stronger phase adhesion due to the formation of fibrils.