Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (23)
- Beitrag zu einem Sammelband (2)
- Buchkapitel (1)
Schlagworte
- Composites (6)
- Flame retardance (5)
- DOPO (4)
- Epoxy resin (4)
- Fire retardancy (3)
- Biomaterials (2)
- Calorimetry (2)
- DNA (2)
- Flame retardancy (2)
- Fracture toughness (2)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (3)
- 7.5 Technische Eigenschaften von Polymerwerkstoffen (3)
- 1 Analytische Chemie; Referenzmaterialien (2)
- 1.4 Prozessanalytik (2)
- 6 Materialchemie (2)
- 1.7 Organische Spuren- und Lebensmittelanalytik (1)
- 1.8 Umweltanalytik (1)
- 5 Werkstofftechnik (1)
- 5.6 Glas (1)
- 6.1 Oberflächen- und Dünnschichtanalyse (1)
The CCQM-K148.a comparison was coordinated by the BIPM on behalf of the CCQM Organic Analysis Working Group for NMIs and DIs which provide measurement services in organic analysis under the CIPM MRA. It was undertaken as a "Track A" comparison within the OAWG strategic plan. CCQM-K148.a demonstrates capabilities for assigning the mass fraction content of a solid organic compound having moderate molecular complexity, where the compound has a molar mass in the range (75 - 500) g/mol and is non-polar (pKow < −2), when present as the primary organic component in a neat organic solid and where the mass fraction content of the primary component in the material is in excess of 950 mg/g.
Participants were required to report the mass fraction of Bisphenol A present in one supplied unit of the comparison material. Participants using a mass balance method for the assignment were also required to report their assignments of the impurity components present in the material. Methods used by the seventeen participating NMIs or DIs were predominantly based on either stand-alone mass balance (summation of impurities) or qNMR approaches, or the combination of data obtained using both methods. The results obtained using thermal methods based on freezing-point depression methods were also reported by a limited number of participants. There was excellent agreement between assignments obtained using all three approaches to assign the BPA content.
The assignment of the values for the mass fraction content of BPA consistent with the KCRV was achieved by most of the comparison participants with an associated relative standard uncertainty in the assigned value in the range (0.1 - 0.5)%.
Under the auspices of the Organic Analysis Working Group (OAWG) of the Comité Consultatif pour la Quantité de Matière (CCQM) a key comparison, CCQM K55.a, was coordinated by the Bureau International des Poids et Mesures (BIPM) in 2009/2010. Eleven national measurement institutes and the BIPM participated. Participants were required to assign the mass fraction of estradiol present as the main component in the comparison sample (CCQM-K55.a) which consisted of a bulk estradiol hemihydrate material obtained from a commercial supplier that had been extensively but not exhaustively dried prior to sub-division into the units supplied for the comparison.
Estradiol was selected to be representative of the performance of a laboratory's measurement capability for the purity assignment of organic compounds of medium structural complexity [molar mass range 300500 Da] and low polarity (pKOW < -2) for which related structure impurities can be quantified by capillary gas phase chromatography (GC) or by high performance liquid chromatography (LC).
The majority of participants used a mass balance approach to determine the estradiol content. The key comparison reference value (KCRV) for estradiol in CCQM-K55.a was assigned by combination of KCRVs assigned by consensus from participant results for each orthogonal impurity class. This allowed participants to demonstrate the efficacy (or otherwise) of their implementation of the mass balance approach and to demonstrate that their assigned value for the main component agreed with the KCRV through use of internally consistent contributing methods.
The KCRV for the estradiol content of the material was 984.3 mg/g with a combined standard uncertainty of 0.42 mg/g. The individual participant results showed that a relative expanded uncertainty for the purity assignment of 0.2% is a reasonable estimate of the best achievable result by an individual laboratory for a material of this complexity available in this amount at this level of purity. The relative expanded uncertainties reported by laboratories having results consistent with the KCRV ranged from 0.2% to 0.8%.
The review of results that were biased from the KCRV showed that two major analytical challenges are posed by the material: the measurement of its water content and controlling for related substance artefact formation during the analysis process. The results displaying a positive bias relative to the KCRV (overestimation of estradiol content) were due to underestimation of the water content of the material, while those with a negative bias (underestimation of estradiol) overestimated the total related substance impurities through a failure to detect and control for artefact formation arising from in situ oxidative dimerization of estradiol in neutral solution prior to analysis. There was however good agreement between all participants in the identification and the quantification of the individual related structure impurities actually present in the sample.
The comparison also demonstrated the utility of high-field 1H NMR for both quantitative and qualitative analysis of high purity compounds. It is noted that all the participants who used qNMR as a major or contributing technique and included it as part of, combined it or confirmed it with a conventional 'mass balance' data estimate, obtained results consistent with the KCRV.
The present work shows results on elemental distribution analyses in Cu(In,Ga)Se2 thin films for solar cells performed by use of wavelength-dispersive and energy-dispersive X-ray spectrometry (EDX) in a scanning electron microscope, EDX in a transmission electron microscope, X-ray photoelectron, angle-dependent soft X-ray emission, secondary ion-mass (SIMS), time-of-flight SIMS, sputtered neutral mass, glow-discharge optical emission and glow-discharge mass, Auger electron, and Rutherford backscattering spectrometry, by use of scanning Auger electron microscopy, Raman depth profiling, and Raman mapping, as well as by use of elastic recoil detection analysis, grazing-incidence X-ray and electron backscatter diffraction, and grazing-incidence X-ray fluorescence analysis. The Cu(In,Ga)Se2 thin films used for the present comparison were produced during the same identical deposition run and exhibit thicknesses of about 2 µm. The analysis techniques were compared with respect to their spatial and depth resolutions, measuring speeds, availabilities, and detection limits.
The development of earth-abundant catalysts for selective electrochemical CO2 conversion is a central challenge. Cu-Sn bimetallic catalysts can yield selective CO2 reduction toward either CO or formate. This study presents oxide-derived Cu-Sn catalysts tunable for either product and seeks to understand the synergetic effects between Cu and Sn causing these selectivity trends. The materials undergo significant transformations under CO2 reduction conditions, and their dynamic bulk and surface structures are revealed by correlating observations from multiple methods—X-ray absorption spectroscopy for in situ study, and quasi in situ X-ray photoelectron spectroscopy for surface sensitivity. For both types of catalysts, Cu transforms to metallic Cu0 under reaction conditions. However, the Sn speciation and content differ significantly between the catalyst types: the CO-selective catalysts exhibit a surface Sn content of 13 at. % predominantly present as oxidized Sn, while the formate-selective catalysts display an Sn content of ≈70 at. % consisting of both metallic Sn0 and Sn oxide species. Density functional theory simulations suggest that Snδ+ sites weaken CO adsorption, thereby enhancing CO selectivity, while Sn0 sites hinder H adsorption and promote formate production. This study reveals the complex dependence of catalyst structure, composition, and speciation with electrochemical bias in bimetallic Cu catalysts.
Most of the experimental density data of the methane−hydrogen binary system available at the time of the development of the equation of state for natural gases and related mixtures, GERG-2008, at temperatures above 270 K were limited to hydrogen contents higher than 0.20 (amount-of-substance fraction). On the contrary, for mixtures with hydrogen contents lower than 0.20, experimental data were limited to temperatures below 270 K. This work intends to close the gap and provides accurate experimental (p, ρ, and T) data for three binary mixtures of methane and hydrogen, (0.95 CH4 + 0.05 H2), (0.90 CH4 + 0.10 H2), and (0.50 CH4 + 0.50 H2), at temperatures of 240, 250, 260, 275, 300, 325, and 350 K, thus extending the range of available experimental data to higher temperatures for mixtures with hydrogen contents lower than 0.20 and, accordingly, to lower temperatures for mixtures with hydrogen contents higher than 0.20. The density measurements were performed by using a single-sinker densimeter with magnetic suspension coupling at pressures up to 20 MPa. Experimental data were compared to the corresponding densities calculated from the GERG-2008 and the AGA8-DC92 equations of state, respectively. The experimental data are within the uncertainty of both equations of state, except at the lower temperatures of 240 and 250 K and pressures over 14 MPa for the mixtures with a hydrogen content of 0.05 and 0.10, respectively. The virial coefficients B(T, x) and C(T, x), as well as the second interaction virial coefficient B12(T) for the methane−hydrogen binary system, were also calculated from the experimental data set at temperatures from 240 to 350 K using the virial equation of state.
Summary: The decomposition of novel phosphorus-containing poly(oxyphenylene-sulfonyl-phenylene-oxy-diphenyl phenylene phosphine oxide) (PSU_I), 2,5-dihydroxy-1-biphenylene-phosphine oxide based polysulfone (PSU_II), poly(sulfonyl-diphenylphenylene phosphonate) (PSU_P) and bisphenol A-based polysulfone (PSU) is studied. The influence of the chemical structure, charring and phosphorus release is discussed based on the mass loss, kinetics and products. The pyrolysis and fire behaviour of blends with epoxy resin (EP) are studied. For EP-PSU_II, phosphorus initiates water elimination and changes the decomposition pathway of EP. The fire behaviour of EP-PSU shows some improvements, whereas the heat release rate is crucially reduced for EP-PSU_II due to simultaneous char formation and flame inhibition.
A systematic and comparative evaluation of the pyrolysis of halogen-free flame-retarded epoxy resins containing phosphine oxide, phosphinate, phosphonate, and phosphate (phosphorus contents around 2.6 wt.%) and the fire behaviour of their carbon fibre composites is presented. Decomposition pathways are proposed based on the thermal analysis (TG), TG coupled with evolved gas analysis (TG-FTIR), kinetics and analysis of the residue with FTIR and XPS. All organophosphorus-modified hardeners containing phenoxy groups lead to a reduced decomposition temperature and mass loss step for the main decomposition of the cured epoxy resin. With increasing oxidation state of the phosphorus the thermally stable residue increases, whereas the release of phosphorus-containing volatiles decreases. The flammability of the composites was investigated with LOI and UL 94 and the fire behaviour for forced-flaming conditions with cone calorimeter tests performed using different irradiations. The flame retardancy mechanisms are discussed. With increasing oxidation state of the phosphorus additional charring is observed, whereas the flame inhibition, which plays the more important role for the performance of the composites, decreases. The processing and the mechanical performance (delamination resistance, flexural properties and interlaminar bonding strength) of the fibre-reinforced composites containing phosphorus were maintained at a high level and, in some cases, even improved. The potential for optimising flame retardancy while maintaining mechanical properties is highlighted in this study.
The pyrolysis of an epoxy resin and the fire behavior of corresponding carbon fiber-reinforced composites, both flame-retarded with either 10-ethyl-9,10-dihydro-9-oxa-10-phosphaphenanthrene 10-oxide or 1,3,5-tris[2-(9,10-dihydro-9-oxa-10-phosphaphenanthrene 10-oxide-10-)ethyl]1, 3,5-triazine-2,4,6(1H,3H,5H)-trione, are investigated. The different fire retardancy mechanisms are discussed, and their influence on the fire properties assessed, in particular for flammability (limiting oxygen index, UL 94) and developing fires (cone calorimeter with different external heat fluxes of 35, 50, and 70 kW m-2). Adding the flame retardants containing 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide affects the fire behavior by both condensed phase and gas phase mechanisms. Interactions between the additives and the epoxy resin result in a change in the decomposition pathways and an increased char formation. The release of phosphorous products results in significant flame inhibition. The fire properties achieved are thus interesting with respect to industrial exploration.
Natural keratin fibres derived from Mexican tannery waste and coconut fibres from coconut processing waste were used as fillers in commercially available, biodegradable thermoplastic starch-polyester blend to obtain sustainable biocomposites. The morphology, rheological and mechanical properties as well as pyrolysis, flammability and forced flaming combustion behaviour of those biocomposites were investigated. In order to open up new application areas for these Kinds of biocomposites, ammonium polyphosphate (APP) was added as a flame retardant. Extensive flammability and cone calorimeter studies revealed a good flame retardance effect with natural fibres alone and improved effectiveness with the addition of APP. In fact, it was shown that replacing 20 of 30 wt. % of APP with keratin fibres achieved the same effectiveness. In the case of coconut fibres, a synergistic effect led to an even lower heat release rate and total heat evolved due to reinforced char residue. This was confirmed via scanning electron microscopy of the char structure. All in all, these results constitute a good approach towards sustainable and biodegradable fibre reinforced biocomposites with improved flame retardant properties.