Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (40) (entfernen)
Sprache
- Englisch (34)
- Deutsch (4)
- Mehrsprachig (1)
- Serbisch (1)
Schlagworte
- Aluminium (5)
- Welding (5)
- Grain refinement (4)
- Neural networks (4)
- Friction stir welding (3)
- GTA welding (3)
- Laser beam welding (3)
- Mechanical properties (3)
- Welding simulation (3)
- Automated manufacturing (2)
- Columnar to equiaxed transition (CET) (2)
- FEA (2)
- Fatigue tests (2)
- Festigkeit (2)
- Gas metal arc welding (2)
- Gas tungsten arc welding (GTAW) (2)
- High-strength low-alloy steel (2)
- Life Cycle Assessment (LCA) (2)
- Notch stress approach (2)
- Rissbildung (2)
- Temperature (2)
- Tensile tests (2)
- Transformable steels (2)
- Tubular X-joints (2)
- Werkstofffragen (2)
- Wire arc additive manufacturing (2)
- Adaptive control (1)
- Additive manufacturing (1)
- Al Ti5B1 (1)
- AlMg0.7SiTiB filler wire (1)
- Alloy 1050A (1)
- Alloy 5083 (1)
- Alloy 6082 (1)
- Aluminium/Aluminiumlegierungen (1)
- Analysis techniques (1)
- Arc welding (1)
- Automatisierte Fertigung (1)
- Axial force (1)
- Carbon dioxide footprint (1)
- Crack formation (1)
- Design of experiments (1)
- Digitalisierung (1)
- Digitalization (1)
- Digitization (1)
- Dissimilar welding (1)
- Duplex nucleation theory (1)
- Dynamic fracture tests (1)
- Economic wide technology replacement (1)
- Energy density distribution (1)
- Energy efficiency (1)
- Energy input (1)
- Environment (1)
- Environmental impact categories (1)
- Epitaxial nucleation (1)
- Equivalent stress concentration factors (1)
- Experimental validation (1)
- Fair salary (1)
- Fracture (1)
- Functional-analytical solution (1)
- GMA welding (1)
- GMA-laser hybrid welding (1)
- Gleeble experiments (1)
- Gleeble testing (1)
- Global optimisation (1)
- Grade S960QL steel (1)
- Grain size (1)
- Greenhouse gas mitigation (1)
- HSLA (1)
- Hardly separable problem (1)
- Heat conduction (1)
- Heat flow (1)
- Heat transfer (1)
- High power welding (1)
- High-strength steel (1)
- Hochfester Stahl (1)
- Hochleistungsschweißen (1)
- Hohlprofilknoten (1)
- Human health (1)
- Hybrid laser arc welding (1)
- Inverse heat conduction problem (1)
- Inverse modelling (1)
- Kerbspannungskonzept (1)
- Laser arc-hybrid welding (1)
- Laser beams (1)
- Laser-MSG-Hybridschweißen (1)
- Life cycle assessment (1)
- Life cycle assessment (LCA) (1)
- Life-cycle assessment (1)
- Lifetime (1)
- Local fatigue spproaches (1)
- MAG welding (1)
- MSG-Schweißen (1)
- Martensite start temperature (1)
- Material flow (1)
- Material modeling (1)
- Material questions (1)
- Measurement (1)
- Metallurgische Fragen (1)
- Microcracking (1)
- Model calibration (1)
- Model order reduction (1)
- Model prediction (1)
- Multi-regional inputeoutput data (1)
- Narrow gap welding (1)
- Normen (1)
- Numerical simulation (1)
- Numerical welding simulation (1)
- Open science (1)
- Open source (1)
- Optimisation (1)
- Optimization (1)
- Phase transformation (1)
- Precipitation hardening aluminum alloys (1)
- Prior austenite grain size (1)
- Process innovations (1)
- Proper generalized decomposition (1)
- Research data management (1)
- Residual stress (1)
- Resistance spot welding (1)
- Resource efficiency (1)
- Schweißnahtfehler (1)
- Schweißnahtgeometrie (1)
- Sensor (1)
- Simulating (1)
- Social Life Cycle Assessment (SLCA) (1)
- Standards (1)
- Stochastic search method (1)
- Strain-rate (1)
- Strength (1)
- Stress-strain behavior (1)
- Structural stress approach (1)
- Super martensitic filler material (1)
- Sustainability assessment (1)
- TRIP - transformation induced plasticity (1)
- Tandem gas metal arc welding (1)
- Tandem welding (1)
- Tear tests (1)
- Technical crack detection (1)
- Temperature field generation (1)
- Thermal analysis (1)
- Thermal energy generation (1)
- Thermo physical simulation (1)
- Tool torque (1)
- Transformation induced plasticity (TRIP) (1)
- Traverse force (1)
- Tubular joints (1)
- Ultrasonic vibration (1)
- Umweltschutz (1)
- Viscoplasticity (1)
- Volume heat source (1)
- Volumetric heat source (1)
- Weld defects (1)
- Weld seam geometry (1)
- Welding residual stresses (1)
- Welding-induced residual stress (1)
- Weldx (1)
- digital image correlation (1)
- dual phase steel (1)
- resistance spot welding (1)
- sensitivity analysis (1)
- welding residual stresses (1)
- Äquivalente Spannungskonzentrationsfaktoren (1)
- Ökobilanz (1)
Organisationseinheit der BAM
Die Mikrostruktur einer Schmelzschweißnaht hat großen Einfluss auf die Heißrissanfälligkeit des Grundwerkstoffs und die mechanischen Eigenschaften der Schweißnaht. Für eine erhöhte Festigkeit, Duktilität und Zähigkeit und eine geringe Heißrissneigung sind anstatt großer, länglicher Körner kleine, globulitische Körner notwendig. Diese Studie berichtet über die Faktoren, die eine solche Schweißnahtkornfeinung hauptsächlich beeinflussen. So wurde für das Wolfram-Intertgasschweißen (WIG-Schweißen) von drei verschiedenen Aluminiumlegierungen der Einfluss der thermischen Bedingungen, der chemischen Zusammensetzung des Schweißguts und der Anzahl und Art der Erstarrungskeime auf die Mikrostruktur klassifiziert.---------------------------------------------------------------------------------------------------------------------------------------------------------------------------
The microstructure of fusion welds has a significant influence on the susceptibility of the base material to hot cracking and on the mechanical properties of the weld. Small, globulitic grains are important for increased strength, ductility and toughness and for a low susceptibility to solidification cracking instead of large, columnar grains. This study shows the main influences on such weld metal grain refinement. Therefore, the influence of thermal conditions, the chemical composition of the weld metal and the number and type of solidification nuclei on the microstructure were classified for the TIG welding of three different aluminium alloys.
Influence of solute content and solidification parameters on grain refinement of aluminum weld metal
(2013)
Grain refinement provides an important possibility to enhance the mechanical properties (e.g., strength and ductility) and the weldability (susceptibility to solidification cracking) of aluminum weld metal. In the current study, a filler metal consisting of aluminum base metal and different amounts of commercial grain refiner Al Ti5B1 was produced. The filler metal was then deposited in the base metal and fused in a GTA welding process. Additions of titanium and boron reduced the weld metal mean grain size considerably and resulted in a transition from columnar to equiaxed grain shape (CET). In commercial pure aluminum (Alloy 1050A), the grain-refining efficiency was higher than that in the Al alloys 6082 and 5083. Different welding and solidification parameters influenced the grain size response only slightly. Furthermore, the observed grain-size reduction was analyzed by means of the undercooling parameter P and the growth restriction parameter Q, which revealed the influence of solute elements and nucleant particles on grain size.
A combined experimental and numerical approach is applied for a numerical analysis of the non-uniform martensitic transformation kinetic on welding residual stresses and distortion of a single pass weld. The (γ → α)-transformation kinetic within the weld pool region is governed by a non-uniform distribution of the elements chromium and nickel. The single-pass weld was performed by use of the low-alloyed high-strength steel S960QL with the high-alloyed high-strength filler wire CN 13/4-IG®. A thermo-mechanical FE model of the welding process was experimentally validated against temperature field, solid phase distribution, transformation behaviour, X-Ray stress measurements and transient optical distortion measurements.
The experimentally determined and calculated weld residual stresses and transient distortion are in good agreement. It can be shown that the change on the (γ → α)-transformation kinetic driven by the inhomogeneous distribution of the chemical contents causes a strong influence on the weld residual stresses within the volume of the weld pool, which could promote crack propagation within the solidified weld pool by use of high-alloyed filler materials. Furthermore, a significant influence on the development of the transient welding distortion is visible. This influence should be respected during numerically calculation of welding distortion in case of multi-pass welding using interpass temperatures and high-alloyed filler materials.
Grain refinement is an important possibility to enhance the mechanical properties such as strength, ductility and toughness of aluminium weld metal. In this study, grain refinement was achieved through the addition of commercial grain refiner Al Ti5B1 to gas tungsten arc weld metal of the aluminium alloys 1050A (Al 99.5) and 5083 (Al Mg4.5Mn0.7). The grain refiner additions led to a significant reduction of the weld metal mean grain size (Alloy 1050A, 86 %; Alloy 5083, 44 %) with a change in grain shape from columnar to equiaxed. Tensile tests showed for Alloy 5083 that the weld metal's ductility can be increased through grain refinement. No improvement in weld metal strength (i.e. yield strength and ultimate tensile strength) was observed. Furthermore, tear tests with notched specimens revealed that the resistance against initiation and propagation of cracks in the weld metal can be enhanced through grain refinement. The toughness was observed to increase clearly by grain refinement in weld metal of commercial pure Al (Alloy 1050A). In Alloy 5083 weld metal, the toughness was not improved through grain refinement, likely because of a semi-continuous network of brittle intermetallic phases that facilitate crack propagation.
Surface modification of mild steel was undertaken using two covered electrodes and two tubular electrodes. The two covered electrodes are DIN 8555: E6-UM-60 and E10-UM-60GR; however, the two tubular electrodes are E10-GF-60GR1 and E10-GF-60GR2. Chemical analysis for the weld metal and XRD of the flux covering for covered electrodes and flux core for tubular electrodes were conducted. The most important factor in determining the wear resistance is the microstructure of the deposit layers. In similar carbon equivalent electrodes E10-UM-60GR and E10-GF-60GR1, electrode E10-GF-60GR1 (tubular) shows larger carbides area fraction and better wear resistance than electrode E10-UM-60GR (covered). This could be attributed to a lower dilution associated with tubular electrode compared with covered electrode. The two tubular electrodes showed higher wear resistance than the covered electrodes which is mainly due to the larger Fe-Cr carbide precipitation area fraction.
The microstructure of a fusion weld has great influences on the susceptibility of the base material to hot cracking and on the mechanical properties of the weld. Small, globulitic grains are necessary for increased strength, ductility and toughness and for a low inclination to hot cracking instead of large, oblong grains. This study reports on the factors which exert the main influences on such grain refinement in the weld. Thus, the influences of the thermal conditions, the chemical composition of the weld metal and the number and type of solidification nuclei on the microstructure were classified for the TIG welding of three different aluminium alloys.
Fast temperature field generation for welding simulation and reduction of experimental effort
(2011)
The quality of welding processes is governed by the occurring induced distortions yielding an increase in production costs due to necessary reworking. Especially for more complex specimens, it is difficult to evaluate the optimal configuration of welding sequences in order to minimize the distortion. Even experienced welding operators can solve this task only by trial and error which is time and cost consuming. In modern engineering the application of welding simulation is already known to be able to analyse the heat effects of welding virtually. However, the welding process is governed by complex physical interactions. Thus, recent weld thermal models are based on many simplifications. The state of the art is to apply numerical methods in order to solve the transient heat conduction equation. Therefore, it is not possible to use the real process parameters as input for the mathematical model. The model parameters which allow calculating a temperature field that is in best agreement with the experiments cannot be defined directly but inversely by multiple simulations runs. In case of numerical simulation software based on finite discretization schemes this approach is very time consuming and requires expert users. The weld thermal model contains an initial weakness which has to be adapted by finding an optimal set of model parameters. This process of calibration is often done against few experiments. The range of model validity is limited. An extension can be obtained by performing a calibration against multiple experiments. The focus of the paper is to show a combined modelling technique which provides an efficient solution of the inverse heat conduction problem mentioned above. On the one hand the inverse problem is solved by application of fast weld thermal models which are closed form solutions of the heat conduction equation. In addition, a global optimization algorithm allows an automated calibration of the weld thermal model. This technique is able to provide a temperature field automatically that fits the experimental one with high accuracy within minutes on ordinary office computers. This fast paradigm permits confirming the application of welding simulation in an industrial environment as automotive industry. On the other hand, the initial model weakness is compensated by calibrating the model against multiple experiments. The unknown relationship between model and process parameters is approximated by a neural network. The validity of the model is increased successively and enables to decrease experimental effort, For a test case, it is shown that this approach yields accurate temperature fields within very short amount of time for unknown process parameters as input data to the model contributing to the requirement to construct a substitute system of the real welding process.
The development within the offshore wind sector towards more powerful turbines combined with increasing water depth for new wind parks is challenging both the designer as well as the manufacturer of bottom fixed support structures. Besides XL-monopiles, the market developed an innovative and economic jacket support structure which is based on automatically manufactured tubular joints combined with standardized pipes. Besides the improvements for a serial manufacturing process the automatically welded tubular joints show a great potential in terms of fatigue resistance e.g. due to a smooth weld geometry without sharp notches. However, these benefits are not considered yet within the fatigue design process of automatically manufactured jacket substructures according to current standards due to the lack of suitable S-N curves. Therefore, 32 axial fatigue tests on single and double-sided automatically welded tubular X-joints have been performed to determine a new hot spot stress related S-N curve. Based on these constant amplitude fatigue tests a new S-N curve equal to a FAT 126 curve was computed which implicitly includes the benefits of the automatically welding procedure.
A combined experimental numerical approach is applied to determine the transformation induced plasticity (TRIP)-parameter K for different strength low-alloy steels of grade S355J2+N and S960QL as well as the super martensitic filler CN13-4-IG containing 13 wt% chromium and 4 wt% nickel. The thermo-physical analyses were conducted using a Gleeble® 3500 facility. The thermal histories of the specimens to be tested were extracted from corresponding simulations of a real gas metal arc weldment. In contrast to common TRIP-experiments which are based on complex specimens a simple flat specimen was utilized together with an engineering evaluation method. The evaluation method was validated with literature values for the TRIP-parameter. It could be shown that the proposed approach enables a correct description of the TRIP behavior.
This paper investigates gas metal arc welding (GMAW) with respect to energy consumption and its associated environmental impacts. Different material transfer modes and power levels for single wire GMAW (SGMAW) and tandem GMAW (TGMAW) are evaluated by means of the indicator electrical deposition efficiency. Furthermore, the wall-plug efficiency of the equipment is measured in order to describe the total energy consumption from the electricity grid. The results show that the energy efficiency is highly affected by the respective process and can be significantly enhanced by a TGMAW process. The wall-plug efficiency of the equipment shows no significant dependency on the power range or the material transfer mode. Moreover, the method of life cycle assessment (LCA) is adopted in order to investigate the influences of energy efficient welding on the environmental impacts. In the comparative LCA study, the demand of electrical energy is reduced up to 24%. In consequence, the indicator values for global warming potential (100), acidification potential, eutrophication potential, and photochemical ozone creation potential are reduced up to 11%.