Among the large number of new ambient ionization schemes in the last few years, dielectric barrier discharge (DBD) has witnessed special attention. In this contribution a versatile dual mode DBD is introduced and characterized by means of optical emission spectroscopy and time-of-flight mass spectrometry. A direct comparison of the individual results from spectroscopy, spectrometry and transient current/voltage consumption gives evidence for the existence of two individual operational mechanisms. The first is driven by rapid transient changes in the potential difference between the two electrodes over time (usually denoted as the homogeneous mode), while the second is caused at high static potential differences (leading to filamentary discharges). The transient versus steady-state characteristics of the individual discharge origin suggest the driving force for the current flow to be inductive and capacitive, respectively. In most cases of dielectric barrier plasmas both discharge types coexist as competitive ion formation channels, however, detailed plasma characteristics of DBDs operated under different conditions allow for a clear distinction of the individual contributions. In this way, two characteristic product channels for the ionization of ambient water could be observed resulting in the generation of either preferentially protonated water clusters or ammonium water clusters. Careful tuning of the operation parameters of the discharge device allows an operation predominated by either of the two modes. As a consequence, facile switching into the desired operational mode results in either protonated molecules or ammoniated molecules of the analyte. Plasma characteristics for both moieties were evaluated and cross-correlated on the basis of several factors including: the production of reagent ions, the individual appearance of current/voltage profiles, UV/Vis spectroscopy, voltage and flux dependence and the individual response to test compounds. Although the filamentary mode has been already discussed in the literature to induce fragmentation processes, no experimental evidence for analyte dissociation could be found in the case of the test compounds used
In this work the determination of Cd, Cu, Cr, Fe and Sb as organic and inorganic additives in in-house plastic materials (ABS, LDPE) using electrothermal vaporization combined with inductively coupled plasma optical emission spectroscopy is described. The influence of CCl2F2 as gaseous halogenation modifier was investigated. Especially for the carbide forming elements the sensitivity was improved and the memory effects were significantly reduced. Calibration was performed by external calibration and standard addition with aqueous standard solutions added directly into the sample boats. Absolute limits of detection (3s-criterion) range between 0.1 ng (Cd) and 9 ng (Fe) which corresponds to relative values of 0.1 mg kg-1 and 1.6 mg kg-1, respectively, taking 5 mg as typical sample mass. The detection limits are sufficient to monitor the element contents of plastic materials according to European directives such as European directive on the safety of toys. The developed ETV-ICP-OES method allows a fast analysis with a high sample throughput (3 minutes per analysis), low sample consumption and good trueness and precision for the analyzed elements. Sample preparation is reduced to ashing the samples in a muffle furnace. Furthermore, measurements are possible regardless of the chemical form in the additives. For verification the results obtained with the developed method were compared with measurement results of independent methods ICP-MS/OES after digestion. In addition Cd, Cr and Pb were determined in a solid plastic reference material BAM-H010 to confirm the applicability and accuracy of the method.
Rationale
The ionization of polystyrenes in matrix-assisted laser desorption/ionization mass spectrometry (MALDI-MS) is typically achieved by the use of silver salts. Since silver salts can cause severe problems, such as cluster formation, fragmentation of polymer chains and end group cleavage, their substitution by alkali salts is highly desirable.
Methods
The influence of various cations (Ag+, Cs+ and Rb+) on the MALDI process of polystyrene (PS) mixtures and high mass polystyrenes was examined. The sample preparation was kept as straightforward as possible. Consequently, no recrystallization or other cleaning procedures were applied.
Results
The investigation of a polystyrene mixture showed that higher molecular polystyrenes could be more easily ionized using caesium, rather than rubidium or silver salts. In combination with the use of DCTB as matrix a high-mass polymer analysis could be achieved, which was demonstrated by the detection of a 1.1 MDa PS.
Conclusions
A fast, simple and robust MALDI sample preparation method for the analysis of ultra-high molecular weight polystyrenes based on the use of DCTB and caesium salts has been presented. The suitability of the presented method has been validated by using different mass spectrometers and detectors.
Hydrophilic interaction chromatography (HILIC) coupled with inductively coupled plasma mass spectrometry (ICP-MS) were optimised for the direct determination of gadolinium-based contrast agents in tap water. In comparison to our previous work, a new developed zwitterionic HILIC column (ZIC-cHILIC) was used for speciation of Gd-containing contrast agents. The limit of quantification (LOQ) for the five contrast agents Gd-BOPTA, Gd-DPTA-BMA, Gd-BT-DO3A, Gd-DOTA and Gd-DTPA are in the range of 512 ng Gd per litre. Additionally, a new internal standard, Pr-DOTA, was investigated to correct intensity drifts, minor and major changes in the sample volumes and possible matrix effects. With the speciation method described, tap water samples from the area of Berlin were analysed and for the first time, three Gd species, Gd-BT-DO3A, Gd-DOTA and Gd-BOPTA, were found in tap water samples at concentrations of about 10–20 ng Gd per litre. These are the same Gd species which have been previously detected predominantly in surface waters of the Berlin area.
The use of magnetic materials as heterogeneous catalysts has attracted increasing attention in the last years since they proved to be promising candidates for water treatment. In the present study, two types of surface-modified magnetite (Fe3O4) nanoparticles, coated with non-hazardous naturally occurring agents—either tannic acid (TA) or dissolved natural organic matter—were evaluated as magnetic heterogeneous catalysts. Chemical synthesis (co-precipitation) was chosen to yield the nanocatalysts due to its well-established simplicity and efficiency. Subsequently, the properties of the final products were fully assessed by various characterization techniques. The catalytic activity in heterogeneous oxidation of aqueous solutions containing a model pollutant, Bisphenol A (BPA), was comparatively studied. The effect of operational parameters (catalyst loading, H2O2 dosage, and UV light irradiation) on the Degradation performance of the oxidation process was investigated. The optimum experimental parameters were found to be 1.0 g/L of catalysts and 10 mM H2O2, under UV irradiation. The highest mineralization rates were observed for Fe3O4-TA catalyst. More than 80 % of BPA was removed after 30 min of reaction time under the specified experimental conditions. The obtained results showed that the two catalysts studied here are suitable candidates for the removal of pollutants in wastewaters by means of heterogeneous reaction using a green sustainable treatment method.
Green Fenton-like magnetic nanocatalysts: Synthesis, characterization and catalytic application
(2015)
Five iron oxalate core–shell magnetite nanoparticles catalysts are evaluated as magnetic heterogeneous materials. Simple and efficient procedures for the preparation of magnetic iron oxalate coated nanoparticles are presented. The catalysts are fully characterized using various investigation techniques. Additionally, the formation of photo-sensitized oxygen by spin-trapping using electron spin resonance is investigated. The catalytic activity of two model substrates (carbamazepine and bisphenol A) is also evaluated. The effect of operational parameters (catalyst and H2O2 concentration, UVA light) on the degradation performance of the oxidation process is investigated. The obtained reaction rates depend on the nature of the compound and increase with iron oxide shell thickness of the catalyst. Moreover, these materials show a significant activity during two consecutive tests. The optimum experimental parameters are found to be 1.0 g L-1 of catalysts, 10 mM H2O2, under UVA irradiation. More than 99% of both substrates are removed after 30 min of reaction time under the experimental conditions given above. The results obtained show that the catalysts are suitable candidates for the removal of pollutants in wastewaters by means of the Fenton heterogeneous reaction.
The catalytic efficiency of two magnetically responsive nanocatalysts was evaluated for the Degradation of Reactive Black 5 (RB5) and Reactive Yellow 84 (RY84) azo dyes using hydrogen peroxide as oxidant undervery mild conditions (atmospheric pressure, room temperature). In order to obtain the nanocatalysts, thesurface of magnetite (Fe3O4) nanoparticles, prepared by a co-precipitation method, was further modified with ferrous oxalate, a highly sensitive non-hazardous reducing agent. The sensitized nanomaterials were characterized by X-ray diffraction, scanning and transmission electron microscopy, energy-dispersive X-ray spectroscopy and vibrating sample magnetometry, and used in the catalytic wet hydrogen peroxideoxidation (CWHPO) of RB5 and RY84, in laboratory-scale experiments. The effect of important variables such as catalyst dosage, H2O2 concentration, and contact time was studied in the dye Degradation kinetics. The results showed that it was possible to remove up to 99.7% dye in the presence of 20 mM H2O2 after 240 min of oxidation for a catalyst concentration of 10 g L−1at 25◦C and initial pH value of 9.0.CWHPO of reactive dyes using sensitized magnetic nanocatalysts can be a suitable pre-treatment methodfor complete decolorization of effluents from textile dyeing and finishing processes, once the Optimum operating conditions are established.
Green Fenton-like magnetic nanocatalysts: Synthesis, characterization and catalytic application
(2015)
Five iron oxalate core–shell magnetite nanoparticles catalysts are evaluated as magnetic heterogeneous materials. Simple and efficient procedures for the preparation of magnetic iron oxalate coated nanoparticles are presented. The catalysts are fully characterized using various investigation techniques. Additionally, the formation of photo-sensitized oxygen by spin-trapping using electron spin resonance is investigated. The catalytic activity of two model substrates (carbamazepine and bisphenol A) is also evaluated. The effect of operational parameters (catalyst and H2O2 concentration, UVA light) on the degradation performance of the oxidation process is investigated. The obtained reaction rates depend on the nature of the compound and increase with iron oxide shell thickness of the catalyst. Moreover, these materials show a significant activity during two consecutive tests. The optimum experimental parameters are found to be 1.0 g L−1 of catalysts, 10 mM H2O2, under UVA irradiation. More than 99% of both substrates are removed after 30 min of reaction time under the experimental conditions given above. The results obtained show that the catalysts are suitable candidates for the removal of pollutants in wastewaters by means of the Fenton heterogeneous reaction.
Pathway of a damaging mechanism - Analyzing chloride attack by synchrotron based X-ray diffraction
(2015)
Typically, the changes of the phase compositions due to the chemical attack are studied in-situ only by chemical analysis or microscopy. In this study, the chloride transport and binding in the cement matrix in different cementitious materials was analyzed by synchrotron based X-ray diffraction (SyXRD) and energy dispersive X-ray spectroscopy (EDX). Sample materials consisting of cement paste were embedded in high concentrated sodium chloride solution over different time spans. Afterwards, the phase and chemical compositions were determined. The high spatial resolution and the information about the chloride distribution offer a detailed view of chloride binding in the cement matrix and allow the conclusions about the degradation mechanisms. The results are discussed related to the influence of different supplementary cementitious materials on the damaging mechanism.
Matrix-assisted laser desorption/ionization mass spectrometry (MALDI-MS) has been suggested as a promising tool for the investigation of pollen, but the usefulness of this approach for classification and identification of pollen species has to be proven by an application to samples of varying taxonomic relations.